The dynamic recrystallization behavior of high strength steel during hot deformation was investigated.The hot compression test was conducted in the temperature range of 950-1150 °C under strain rates of 0.1,1 and...The dynamic recrystallization behavior of high strength steel during hot deformation was investigated.The hot compression test was conducted in the temperature range of 950-1150 °C under strain rates of 0.1,1 and 5 s-1.It is observed that dynamic recrystallization(DRX) is the main flow softening mechanism and the flow stress increases with decreasing temperature and increasing strain rate.The relationship between material constants(Q,n,α and ln A) and strain is identified by the sixth order polynomial fit.The constitutive model is developed to predict the flow stress of the material incorporating the strain softening effect and verified.Moreover,the critical characteristics of DRX are extracted from the stress-strain curves under different deformation conditions by linear regression.The dynamic recrystallization volume fraction decreases with increasing strain rate at a constant temperature or decreasing deformation temperature under a constant strain rate.The kinetics of DRX increases with increasing deformation temperature or strain rate.展开更多
The flow stress behavior of high-purity Al-Cu-Mg alloy under hot deformation conditions was studied by Gleeble-1500,with the deformation temperature range from 300 to 500 °C and the strain rate range from 0.01 to...The flow stress behavior of high-purity Al-Cu-Mg alloy under hot deformation conditions was studied by Gleeble-1500,with the deformation temperature range from 300 to 500 °C and the strain rate range from 0.01 to 10 s-1. From the true stress-true strain curve, the flow stress increases with the increasing of strain and tends to be constant after a peak value, showing dynamic recover, and the peak value of flow stress increases with the decreasing of deformation temperature and the increasing of strain rate.When the strain rate is 10 s-1 and the deformation temperature is higher than 400 °C, the flow stress shows dynamic recrystallization characteristic. TEM micrographs were used to reveal the evolution of microstructures. According to the processing map at true strain of 0.7, the feasible deformation conditions are high strain rate(>0.5 s-1) or 440-500 °C and 0.01-0.02 s-1.展开更多
Abstract： The hot deformation behaviors of AI-Zn-Mg-Sc-Zr alloy were investigated in a temperature range of 340-500℃ and a strain rate range of 0.001-10 s 1 using uniaxial compression test on Gleeble-1500 thermal si...Abstract： The hot deformation behaviors of AI-Zn-Mg-Sc-Zr alloy were investigated in a temperature range of 340-500℃ and a strain rate range of 0.001-10 s 1 using uniaxial compression test on Gleeble-1500 thermal simulation machine. The results show that the flow stress increases with increasing strain and tends to be constant after a peak value. The flow stress increases with increasing strain rate and decreases with increasing deformation temperature. The phenomenon of dynamic recovery and dynamic recrystallization can be observed by microstructural evolutions. Based on the hyperbolic Arrhenius-type equation, the true stress-true strain data from the tests were employed to establish the constitutive equation considering the effect of the true strain on material constants （α, β, Q, n and A）, which reveals the dependence of the flow stress on strain, strain rate and deformation temperature. The predicted stress-strain curves are in good agreement with experimental results, which confirms that the developed constitutive equations are suitable to research the hot deformation behaviors of Al-Zn-Mg-Sc-Zr alloy.展开更多
The relationship between viscosity/yield stress and flotation rate in different chalcopyrite and lizardite concentrations was investigated by zeta potential measurements,rheological tests,flotation experiments,and Der...The relationship between viscosity/yield stress and flotation rate in different chalcopyrite and lizardite concentrations was investigated by zeta potential measurements,rheological tests,flotation experiments,and DerjguinLandau-Verwey-Overbeek theoretical calculation.Results indicated that the concentration of minerals would affect the viscosity and yield stress of the slurry.That is,the viscosity/yield stress in the slurry rises accordingly when the concentration of minerals increases.The increase in viscosity/yield stress in slurry is also unfavorable to the enrichment of chalcopyrite but is conducive to the entrainment of lizardite in either single or binary system.Specifically,the flotation rate of chalcopyrite decreases while that of lizardite increases with the rise in viscosity/yield stress.展开更多
Isothermal compression tests at temperatures from 1 273 to l 423 K and strain rates from 0.1 to 10 s-q were carried out to investigate the flow behaviors of Q420qE steel. Stress-strain data collected from the tests we...Isothermal compression tests at temperatures from 1 273 to l 423 K and strain rates from 0.1 to 10 s-q were carried out to investigate the flow behaviors of Q420qE steel. Stress-strain data collected from the tests were employed to establish the constitutive equation, in which the influence of strain was incorporated by considering the effect of strain on material constants Q, n, a, and lnA. The results show that the flow stress curves are dependent on the strain, strain rate and deformation temperature. They display typical dynamic recrystallization behavior and consist of three stages, i.e., hardening stage, softening stage and steady stage. The flow stress decreases with increasing the deformation temperature and decreasing the strain rate. In addition, the flow stress data predicted by the proposed constitutive model agree well with the corresponding experimental results, and the correlation coefficient and the average absolute relative error between them are 0.990 3 and 3.686%, respectively.展开更多
The plastic deformation simulation of AZ31 magnesium alloy at different elevated temperatures （from 473 to 723 K） was performed on Gleeble-1500 thermal mechanical simulator at the strain rates of 0.01, 0.1, 1, 5 and...The plastic deformation simulation of AZ31 magnesium alloy at different elevated temperatures （from 473 to 723 K） was performed on Gleeble-1500 thermal mechanical simulator at the strain rates of 0.01, 0.1, 1, 5 and 10 s-t and the maximum deformation degree of 80%. The relationship between the flow stress and deformation temperature as well as strain rate was analyzed. The materials parameters and the apparent activation energy were calculated. The constitutive relationship was established with a Zener-Hollomon （Z） parameter. The results show that the flow stress increases with the increase of strain rate at a constant temperature, but it decreases with the increase of deformation temperature at a constant strain rate. The apparent activation energy is estimated to be 129-153 kJ/mol, which is close to that for self-diffusion of magnesium. The established constitutive relationship can reflect the change of flow stress during hot deformation.展开更多
基金Project (51322405) supported by the National Natural Science Foundation of ChinaProject (CX2013B085) supported by Hunan Provincial Innovation Foundation for Postgraduate,China
文摘The dynamic recrystallization behavior of high strength steel during hot deformation was investigated.The hot compression test was conducted in the temperature range of 950-1150 °C under strain rates of 0.1,1 and 5 s-1.It is observed that dynamic recrystallization(DRX) is the main flow softening mechanism and the flow stress increases with decreasing temperature and increasing strain rate.The relationship between material constants(Q,n,α and ln A) and strain is identified by the sixth order polynomial fit.The constitutive model is developed to predict the flow stress of the material incorporating the strain softening effect and verified.Moreover,the critical characteristics of DRX are extracted from the stress-strain curves under different deformation conditions by linear regression.The dynamic recrystallization volume fraction decreases with increasing strain rate at a constant temperature or decreasing deformation temperature under a constant strain rate.The kinetics of DRX increases with increasing deformation temperature or strain rate.
基金Project(51301209) supported by the National Natural Science Foundation of ChinaProject(201191107) supported by Science and Technology Plan of Xinjiang Province,China
文摘The flow stress behavior of high-purity Al-Cu-Mg alloy under hot deformation conditions was studied by Gleeble-1500,with the deformation temperature range from 300 to 500 °C and the strain rate range from 0.01 to 10 s-1. From the true stress-true strain curve, the flow stress increases with the increasing of strain and tends to be constant after a peak value, showing dynamic recover, and the peak value of flow stress increases with the decreasing of deformation temperature and the increasing of strain rate.When the strain rate is 10 s-1 and the deformation temperature is higher than 400 °C, the flow stress shows dynamic recrystallization characteristic. TEM micrographs were used to reveal the evolution of microstructures. According to the processing map at true strain of 0.7, the feasible deformation conditions are high strain rate(>0.5 s-1) or 440-500 °C and 0.01-0.02 s-1.
基金Project(2012CB619503)supported by National Basic Research Program of China
文摘Abstract： The hot deformation behaviors of AI-Zn-Mg-Sc-Zr alloy were investigated in a temperature range of 340-500℃ and a strain rate range of 0.001-10 s 1 using uniaxial compression test on Gleeble-1500 thermal simulation machine. The results show that the flow stress increases with increasing strain and tends to be constant after a peak value. The flow stress increases with increasing strain rate and decreases with increasing deformation temperature. The phenomenon of dynamic recovery and dynamic recrystallization can be observed by microstructural evolutions. Based on the hyperbolic Arrhenius-type equation, the true stress-true strain data from the tests were employed to establish the constitutive equation considering the effect of the true strain on material constants （α, β, Q, n and A）, which reveals the dependence of the flow stress on strain, strain rate and deformation temperature. The predicted stress-strain curves are in good agreement with experimental results, which confirms that the developed constitutive equations are suitable to research the hot deformation behaviors of Al-Zn-Mg-Sc-Zr alloy.
基金Project(2018TP1002)supported by the Key Laboratory of Hunan Province for Clean and Efficient Utilization of Strategic Calcium-containing Mineral Resources,ChinaProject(2019zzts994)supported by the Central South University Graduate Research and Innovation Project,China。
文摘The relationship between viscosity/yield stress and flotation rate in different chalcopyrite and lizardite concentrations was investigated by zeta potential measurements,rheological tests,flotation experiments,and DerjguinLandau-Verwey-Overbeek theoretical calculation.Results indicated that the concentration of minerals would affect the viscosity and yield stress of the slurry.That is,the viscosity/yield stress in the slurry rises accordingly when the concentration of minerals increases.The increase in viscosity/yield stress in slurry is also unfavorable to the enrichment of chalcopyrite but is conducive to the entrainment of lizardite in either single or binary system.Specifically,the flotation rate of chalcopyrite decreases while that of lizardite increases with the rise in viscosity/yield stress.
基金Project(200804220021) supported by the Specialized Research Fund for Doctoral Program of Higher Education of China Project (Y2007F06) supported by the Natural Science Foundation of Shandong Province,China
文摘Isothermal compression tests at temperatures from 1 273 to l 423 K and strain rates from 0.1 to 10 s-q were carried out to investigate the flow behaviors of Q420qE steel. Stress-strain data collected from the tests were employed to establish the constitutive equation, in which the influence of strain was incorporated by considering the effect of strain on material constants Q, n, a, and lnA. The results show that the flow stress curves are dependent on the strain, strain rate and deformation temperature. They display typical dynamic recrystallization behavior and consist of three stages, i.e., hardening stage, softening stage and steady stage. The flow stress decreases with increasing the deformation temperature and decreasing the strain rate. In addition, the flow stress data predicted by the proposed constitutive model agree well with the corresponding experimental results, and the correlation coefficient and the average absolute relative error between them are 0.990 3 and 3.686%, respectively.
基金Project supported by China-Canada-USA Collaborative Research and Development Project (Magnesium Front End Research and Development (MFERD))
文摘The plastic deformation simulation of AZ31 magnesium alloy at different elevated temperatures （from 473 to 723 K） was performed on Gleeble-1500 thermal mechanical simulator at the strain rates of 0.01, 0.1, 1, 5 and 10 s-t and the maximum deformation degree of 80%. The relationship between the flow stress and deformation temperature as well as strain rate was analyzed. The materials parameters and the apparent activation energy were calculated. The constitutive relationship was established with a Zener-Hollomon （Z） parameter. The results show that the flow stress increases with the increase of strain rate at a constant temperature, but it decreases with the increase of deformation temperature at a constant strain rate. The apparent activation energy is estimated to be 129-153 kJ/mol, which is close to that for self-diffusion of magnesium. The established constitutive relationship can reflect the change of flow stress during hot deformation.