As a typical steel,the fatigue of marine high-strength steels has been emphasized by scholars.In this paper,the fatigue performance and crack growth mechanism of a high-strength steel for ships are investigated by exp...As a typical steel,the fatigue of marine high-strength steels has been emphasized by scholars.In this paper,the fatigue performance and crack growth mechanism of a high-strength steel for ships are investigated by experimental methods.First,the fatigue threshold test and fatigue crack growth rate test of this high-strength steel under different stress ratios were carried out.The influence of stress ratio on the fatigue properties of this steel was analyzed.Secondly,scanning electron microscope was used to analyze the crack growth specimen section of this steel.The crack growth and failure mechanism of this steel were revealed.Finally,based on the above research results,the stress ratio effect of high-strength steel was investigated from the perspectives of crack closure and driving force.Considering the fatigue behavior in the near-threshold stage and the destabilization stage,a fatigue crack growth behavior prediction model of highstrength steel was established.The accuracy of the model was verified by test data.Moreover,the applicability of the modified model to various materials and its excellent predictive ability were verified through comparison with literature data and existing models.展开更多
文摘As a typical steel,the fatigue of marine high-strength steels has been emphasized by scholars.In this paper,the fatigue performance and crack growth mechanism of a high-strength steel for ships are investigated by experimental methods.First,the fatigue threshold test and fatigue crack growth rate test of this high-strength steel under different stress ratios were carried out.The influence of stress ratio on the fatigue properties of this steel was analyzed.Secondly,scanning electron microscope was used to analyze the crack growth specimen section of this steel.The crack growth and failure mechanism of this steel were revealed.Finally,based on the above research results,the stress ratio effect of high-strength steel was investigated from the perspectives of crack closure and driving force.Considering the fatigue behavior in the near-threshold stage and the destabilization stage,a fatigue crack growth behavior prediction model of highstrength steel was established.The accuracy of the model was verified by test data.Moreover,the applicability of the modified model to various materials and its excellent predictive ability were verified through comparison with literature data and existing models.
基金supported by the Science and Technology Research Program of Chongqing Education Commission(Grant No.KJZD-M202100801)the Fifth Batch of Excellent Talent Support Program of Chongqing Colleges and University(Grant No.68021900601)+4 种基金the Natural Science Foundation of CQ CSTC(Grant No.cstc.2018jcyjA2073)the Program for the Chongqing Statistics Postgraduate Supervisor Team(Grant No.yds183002)the Chongqing Social Science Plan Project(Grant No.2019WT59)the Open Project from Chongqing Key Laboratory of Social Economy and Applied Statistics(Grant No.KFJJ2018066)the Mathematic and Statistics Team from Chongqing Technology and Business University(Grant No.ZDPTTD201906).
