Hypereutectic Al-40 wt.%Si alloys were fabricated by the combination of gas atomization and spark plasma sintering(SPS) technology. The effects of holding time(15-60 min) on phase composition, microstructure, density,...Hypereutectic Al-40 wt.%Si alloys were fabricated by the combination of gas atomization and spark plasma sintering(SPS) technology. The effects of holding time(15-60 min) on phase composition, microstructure, density,mechanical properties of Al-Si alloys were investigated by XRD, SEM, a hydrostatic balance, an automatic micro hardness tester and a universal tensile testing machine. The results showed that homogenous distribution of ultrafine primary Si and high density of alloys can be obtained at holding time of 30 min. Compared with primary Si(3.7 μm)fabricated by gas atomization, the average size increased from 5.17 to 7.72 μm with the increase of holding time during SPS process. Overall, the relative density, maximum tensile strength and Vickers hardness of 94.9%, 205 MPa and HV;196.86 were achieved at holding time of 30 min, respectively. In addition, all the diffraction peaks were corresponded to α-Al or β-Si and no other phase can be detected. Finally, the densification process of SPS was also discussed.展开更多
Giant reed is a suitable pioneer plant for metal-contaminated soil phytoremediation,however,it is imperative to dispose the metal-contaminated biomass after harvesting.The liquefaction of metal-contaminated giant reed...Giant reed is a suitable pioneer plant for metal-contaminated soil phytoremediation,however,it is imperative to dispose the metal-contaminated biomass after harvesting.The liquefaction of metal-contaminated giant reed biomass in ethylene glycol system with sulfuric acid as catalyst for the precursors of polyurethane compounds was studied.The results show that giant reed biomass from metal-contaminated soil is potentially liquefied and significantly affected by solvent/solid ratio,liquefaction temperature and liquefaction time （P〈0.05）.The liquefaction rate of biomass in acidified ethylene glycol system can reach 85.2% with optimized conditions of 60 min,170 ℃,3% sulfuric acid and solvent/biomass ratio of 5：1.The hydroxyl value of liquefied products is of 481 mg KOH/g while reactive hydroxyl groups of them are abundant,which is promised as potential precursors for polyurethane compounds.The solvent liquefaction is a potential method to dispose the metal-contaminated biomass,however,the containing-metal liquefied products should be studied deeply in order to get the suitable precursors in future.展开更多
基金Project(18JS060) supported by the Shaanxi Key Laboratory of Nano-materials and Technology,ChinaProject(2018JQ5087) supported by Natural Science Basic Research Plan of Shaanxi Province,China。
文摘Hypereutectic Al-40 wt.%Si alloys were fabricated by the combination of gas atomization and spark plasma sintering(SPS) technology. The effects of holding time(15-60 min) on phase composition, microstructure, density,mechanical properties of Al-Si alloys were investigated by XRD, SEM, a hydrostatic balance, an automatic micro hardness tester and a universal tensile testing machine. The results showed that homogenous distribution of ultrafine primary Si and high density of alloys can be obtained at holding time of 30 min. Compared with primary Si(3.7 μm)fabricated by gas atomization, the average size increased from 5.17 to 7.72 μm with the increase of holding time during SPS process. Overall, the relative density, maximum tensile strength and Vickers hardness of 94.9%, 205 MPa and HV;196.86 were achieved at holding time of 30 min, respectively. In addition, all the diffraction peaks were corresponded to α-Al or β-Si and no other phase can be detected. Finally, the densification process of SPS was also discussed.
基金Project(41271330)supported by the National Natural Science Foundation of ChinaProject(2012BAC09B04)supported by the National Key Technology Research and Development Program of the Ministry of Science and Technology of ChinaProject(2012FJ1010)supported by the Science and Technology Major Program of Hunan Province,China
文摘Giant reed is a suitable pioneer plant for metal-contaminated soil phytoremediation,however,it is imperative to dispose the metal-contaminated biomass after harvesting.The liquefaction of metal-contaminated giant reed biomass in ethylene glycol system with sulfuric acid as catalyst for the precursors of polyurethane compounds was studied.The results show that giant reed biomass from metal-contaminated soil is potentially liquefied and significantly affected by solvent/solid ratio,liquefaction temperature and liquefaction time （P〈0.05）.The liquefaction rate of biomass in acidified ethylene glycol system can reach 85.2% with optimized conditions of 60 min,170 ℃,3% sulfuric acid and solvent/biomass ratio of 5：1.The hydroxyl value of liquefied products is of 481 mg KOH/g while reactive hydroxyl groups of them are abundant,which is promised as potential precursors for polyurethane compounds.The solvent liquefaction is a potential method to dispose the metal-contaminated biomass,however,the containing-metal liquefied products should be studied deeply in order to get the suitable precursors in future.