The action between imidazolinyl-quaternary-ammonium-salt(IQAS) molecule and Fe atom was studied, and the influence of the alkyl group connected with N atom of imidazoline ring on corrosion inhibition efficiency was ex...The action between imidazolinyl-quaternary-ammonium-salt(IQAS) molecule and Fe atom was studied, and the influence of the alkyl group connected with N atom of imidazoline ring on corrosion inhibition efficiency was explored. Quantum chemical methods, HF/6-31 G and HF/Lan L2 dz, were applied successively to calculate the parameters such as front molecular orbit energy of IQASⅠ-Ⅳ and chemical adsorption for IQASⅠ-Ⅳ and Fe atom. The corrosion inhibition efficiency was measured with the weight loss method of carbon steel samples in acidic solution and oil field sewage. Based on the theoretical analyses and experimental results, it is concluded that N-Fe coordination bond is formed between IQAS molecule and Fe atom, corrosion inhibition efficiency is decreased in the following order(from large to small): IQAS Ⅳ, IQAS Ⅲ, IQAS Ⅱ, IQASⅠ.展开更多
The technology of black coloring for stainless steel by electrochemical method was studied. The optimum bath compositions and operating conditions were obtained as follows: 4050g/L K2Cr2O7 , 1520g/L MnSO4, 1520g/L （...The technology of black coloring for stainless steel by electrochemical method was studied. The optimum bath compositions and operating conditions were obtained as follows: 4050g/L K2Cr2O7 , 1520g/L MnSO4, 1520g/L （NH4）2SO4, 2040g/L H3BO3, 2030 g/L additive A, 2 g/L （NH4）6Mo7O 24 ; time 920 min; temperature 1530℃; potential 3V and current density 12mA/cm 2 . The effects of the compositions of the bath on the quality of black colored film were discussed. The influences of passivation process on the black coloring velocity and performances of black colored film layer were investigated. The results show that the passivation process can improve the corrosion resistance and the stability to bear color-change; （NH4）2SO4 can control the black coloring velocity and prolong black coloring bath life remarkably; and additive A can improve the evenness and compactness of black colored film layer. The results of scanning electron microscopy and energy dispersive spectra show that the microstructure is of cylindrical lump, the filling process can decrease the crackles, and the main elements of black colored film are Fe, Cr, Mn and Ni.展开更多
基金Project (05A002) supported by Scientific Research Fundation of Hunan Provincial Education Depart ment project(04JJY40010) supported by the Natural Science Foundation of Hunan Province
文摘The action between imidazolinyl-quaternary-ammonium-salt(IQAS) molecule and Fe atom was studied, and the influence of the alkyl group connected with N atom of imidazoline ring on corrosion inhibition efficiency was explored. Quantum chemical methods, HF/6-31 G and HF/Lan L2 dz, were applied successively to calculate the parameters such as front molecular orbit energy of IQASⅠ-Ⅳ and chemical adsorption for IQASⅠ-Ⅳ and Fe atom. The corrosion inhibition efficiency was measured with the weight loss method of carbon steel samples in acidic solution and oil field sewage. Based on the theoretical analyses and experimental results, it is concluded that N-Fe coordination bond is formed between IQAS molecule and Fe atom, corrosion inhibition efficiency is decreased in the following order(from large to small): IQAS Ⅳ, IQAS Ⅲ, IQAS Ⅱ, IQASⅠ.
基金Project(04JJ40036) supported by the Natural Science Foundation of Hunan Province
文摘The technology of black coloring for stainless steel by electrochemical method was studied. The optimum bath compositions and operating conditions were obtained as follows: 4050g/L K2Cr2O7 , 1520g/L MnSO4, 1520g/L （NH4）2SO4, 2040g/L H3BO3, 2030 g/L additive A, 2 g/L （NH4）6Mo7O 24 ; time 920 min; temperature 1530℃; potential 3V and current density 12mA/cm 2 . The effects of the compositions of the bath on the quality of black colored film were discussed. The influences of passivation process on the black coloring velocity and performances of black colored film layer were investigated. The results show that the passivation process can improve the corrosion resistance and the stability to bear color-change; （NH4）2SO4 can control the black coloring velocity and prolong black coloring bath life remarkably; and additive A can improve the evenness and compactness of black colored film layer. The results of scanning electron microscopy and energy dispersive spectra show that the microstructure is of cylindrical lump, the filling process can decrease the crackles, and the main elements of black colored film are Fe, Cr, Mn and Ni.