Calcined ginger nuts admixed by fly ash and quartz sand(CGN-(F+S))has been validated to be basically compatible to earthen sites as an anchor grout.Accelerated ageing tests including water stability test,temperature a...Calcined ginger nuts admixed by fly ash and quartz sand(CGN-(F+S))has been validated to be basically compatible to earthen sites as an anchor grout.Accelerated ageing tests including water stability test,temperature and humidity cycling test,soundness test and alkali resistance test are conducted with the objective to further research the property changes of CGN-(F+S)grout.Density,surface hardness,water penetration capacity,water permeability capacity,soluble salt,scanning electron microscopy(SEM)images and energy dispersive spectrometry(EDS)spectrum of these samples have been tested after accelerated ageing tests.The results show that densities of samples decrease,surface hardness,water penetration capacity and water permeability capacity of samples increase generally.Besides,soluble salt analysis,SEM and EDS results well corroborate the changes.Based on the results it can be concluded that property changes are most serious after temperature and humidity cycling test,followed by water stability,soundness and alkali resistance test in sequence.But in general,CGN-(F+S)still has good durability.展开更多
Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive ...Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive mined-out gobs, enormous ore body under roadway and low recovery ratio of Yongshaba Mine, Kaiyang Phosphor Mine Group, Guizhou Province, China. An appropriate backfill system and craflwork were designed, using shattering milling method to crush gypsum, double-axles mixing and strong activation mixing way to mix slurry, cemented slurry and mullock backfill alternately process. The results show that gypsum is fit for backfilling afterwards by adding fly ash, though it is not an ideal aggregate for fine granule and coagulate retardation. The suggested dosage （the mass ratio of cement to fly ash to gypsum） is 1：1：6-1：1：8 with mass fraction of solid materials 60%-63%. Slurry is transported in suspend state with non-plastic strength, and then in concretion state after backfilling. The application to mine shows the technology is feasible, and gypsum utilization ratio is up to 100%. Transportation and backfill effect is very good for paste-like slurry and drenching cemented slurry into mullock, and the compressive strength and recovery ratio are 2.0 MPa and 82.6%, respectively, with the maximum subsidence of surface only 1.307 mm. Furthermore, the investment of system is about 7 × 10^6 yuan （RMB）, only 1/10 of that of traditional paste backfill system.展开更多
Solid wastes derived from metallurgical industries pose a significant threat to environment. The utilization and disposal of these solid wastes are the major concern in the world. Semi-coke generated in coal-based dir...Solid wastes derived from metallurgical industries pose a significant threat to environment. The utilization and disposal of these solid wastes are the major concern in the world. Semi-coke generated in coal-based direct reduction process of iron ore is a by-product and its suitable utilization is not available so far. In order to handle it properly, the characteristics of this by-product were comprehensively investigated. A series of analysis methods were used to demonstrate its mineral compositions, petrography and physico-chemical properties. The results reveal that the semi-coke has poor washability. The fixed carbon content of semi-coke reaches 76.11% and the gross calorific value is 28.10 MJ/kg, both of which are similar to those of traditional sinter coke breeze. Also, semi-coke ash possesses lower content of SiO2, Al2O3, S and higher content of CaO and MgO, which could improve the strength of sinter ore when partially substituting for coke breeze in sintering. Semi-coke features well-development porous structure and higher reaction activity, which predicts that the sintering speed could be elevated to some extent when employing it as a partial replacement of coke breeze, so the studies further suggest that the potential adverse effect of the high reactivity on sintering process could be weakened by adequately coarsening the semi-coke's particle size.展开更多
The electronic structure and optical properties of the tetragonal phase quaternary arsenide oxides YZnAsO and LaZnAsO were studied using density-functional theory(DFT) within generalized gradient approximation(GGA).Th...The electronic structure and optical properties of the tetragonal phase quaternary arsenide oxides YZnAsO and LaZnAsO were studied using density-functional theory(DFT) within generalized gradient approximation(GGA).The band structure along the higher symmetry axes in the Brillouin zone,the density of states(DOS) and the partial density of states(PDOS) were presented.The calculated energy band structures show that both YZnAsO and LaZnAsO are indirect gap semiconductors with band gap of 1.173 1 eV and 1.166 5 eV,respectively.The DOS and PDOS show the hybridization of Y-O/La-O atom orbits and Zn-As atom orbits.The dielectric function,reflectivity,absorption coefficient,refractive index,electron energy-loss function and optical conductivity were presented in an energy range from 0 to 25 eV for discussing the optical properties of YZnAsO and LaZnAsO.展开更多
基金Project(51578272)supported by the National Natural Science Foundation of China
文摘Calcined ginger nuts admixed by fly ash and quartz sand(CGN-(F+S))has been validated to be basically compatible to earthen sites as an anchor grout.Accelerated ageing tests including water stability test,temperature and humidity cycling test,soundness test and alkali resistance test are conducted with the objective to further research the property changes of CGN-(F+S)grout.Density,surface hardness,water penetration capacity,water permeability capacity,soluble salt,scanning electron microscopy(SEM)images and energy dispersive spectrometry(EDS)spectrum of these samples have been tested after accelerated ageing tests.The results show that densities of samples decrease,surface hardness,water penetration capacity and water permeability capacity of samples increase generally.Besides,soluble salt analysis,SEM and EDS results well corroborate the changes.Based on the results it can be concluded that property changes are most serious after temperature and humidity cycling test,followed by water stability,soundness and alkali resistance test in sequence.But in general,CGN-(F+S)still has good durability.
基金Project(2006BAB02A03)supported by the National Key Technology Research and Development ProgramProject(08MX16)supported by Mittal Scientific and Technological Innovation Projects of Central South University during 2008
文摘Physical-chemical properties of phosphorous gypsum, proportion and cemented mechanism of slurry with gypsum as aggregate were studied to remove the harms of gypsum pile, combining with difficult problems of excessive mined-out gobs, enormous ore body under roadway and low recovery ratio of Yongshaba Mine, Kaiyang Phosphor Mine Group, Guizhou Province, China. An appropriate backfill system and craflwork were designed, using shattering milling method to crush gypsum, double-axles mixing and strong activation mixing way to mix slurry, cemented slurry and mullock backfill alternately process. The results show that gypsum is fit for backfilling afterwards by adding fly ash, though it is not an ideal aggregate for fine granule and coagulate retardation. The suggested dosage （the mass ratio of cement to fly ash to gypsum） is 1：1：6-1：1：8 with mass fraction of solid materials 60%-63%. Slurry is transported in suspend state with non-plastic strength, and then in concretion state after backfilling. The application to mine shows the technology is feasible, and gypsum utilization ratio is up to 100%. Transportation and backfill effect is very good for paste-like slurry and drenching cemented slurry into mullock, and the compressive strength and recovery ratio are 2.0 MPa and 82.6%, respectively, with the maximum subsidence of surface only 1.307 mm. Furthermore, the investment of system is about 7 × 10^6 yuan （RMB）, only 1/10 of that of traditional paste backfill system.
基金Project(2011GH561685)supported by the China Torch Program
文摘Solid wastes derived from metallurgical industries pose a significant threat to environment. The utilization and disposal of these solid wastes are the major concern in the world. Semi-coke generated in coal-based direct reduction process of iron ore is a by-product and its suitable utilization is not available so far. In order to handle it properly, the characteristics of this by-product were comprehensively investigated. A series of analysis methods were used to demonstrate its mineral compositions, petrography and physico-chemical properties. The results reveal that the semi-coke has poor washability. The fixed carbon content of semi-coke reaches 76.11% and the gross calorific value is 28.10 MJ/kg, both of which are similar to those of traditional sinter coke breeze. Also, semi-coke ash possesses lower content of SiO2, Al2O3, S and higher content of CaO and MgO, which could improve the strength of sinter ore when partially substituting for coke breeze in sintering. Semi-coke features well-development porous structure and higher reaction activity, which predicts that the sintering speed could be elevated to some extent when employing it as a partial replacement of coke breeze, so the studies further suggest that the potential adverse effect of the high reactivity on sintering process could be weakened by adequately coarsening the semi-coke's particle size.
基金Project(50474051) supported by the National Natural Science Foundation of China
文摘The electronic structure and optical properties of the tetragonal phase quaternary arsenide oxides YZnAsO and LaZnAsO were studied using density-functional theory(DFT) within generalized gradient approximation(GGA).The band structure along the higher symmetry axes in the Brillouin zone,the density of states(DOS) and the partial density of states(PDOS) were presented.The calculated energy band structures show that both YZnAsO and LaZnAsO are indirect gap semiconductors with band gap of 1.173 1 eV and 1.166 5 eV,respectively.The DOS and PDOS show the hybridization of Y-O/La-O atom orbits and Zn-As atom orbits.The dielectric function,reflectivity,absorption coefficient,refractive index,electron energy-loss function and optical conductivity were presented in an energy range from 0 to 25 eV for discussing the optical properties of YZnAsO and LaZnAsO.