Abstract： An alloy steel/alumina composite was successfully fabricated by pressureless infiltration of X10CrNil8-8 steel melt on 30% （mass fraction） Ni-containing alumina based composite ceramic （Ni/Al2O3） at 1 6...Abstract： An alloy steel/alumina composite was successfully fabricated by pressureless infiltration of X10CrNil8-8 steel melt on 30% （mass fraction） Ni-containing alumina based composite ceramic （Ni/Al2O3） at 1 600 ℃. The infiltration quality and interfacial bonding behavior were investigated by SEM, EDS, XRD and tensile tests. The results show that there is an obvious interfacial reaction layer between the alloying steel and the Ni/Al2O3 composite ceramic. The interfacial reactive products are （FexAly）3O4 intermetallic phase and （AlxCry）2O3 solid solution. The interracial bonding strength is as high as about 67.5 MPa. The bonding mechanism of X10CrNi 18-8 steel with the composite ceramic is that Ni inside the ceramic bodies dissolves into the alloy melt and transforms into liquid channels, consequently inducing the steel melt infiltrating and filling in the pores and the liquid channels. Moreover, the metallurgical bonding and interfacial reactive bonding also play a key role on the stability of the bonding interface.展开更多
Pre-heat treatment is a vital step before cold ring rolling and it has significant effect on the microstructure and mechanical properties of rolled rings.The 100Cr6 steel rings were subjected to pre-heat treatment and...Pre-heat treatment is a vital step before cold ring rolling and it has significant effect on the microstructure and mechanical properties of rolled rings.The 100Cr6 steel rings were subjected to pre-heat treatment and subsequent cold rolling process.Scanning electron microscopy and tensile tests were applied to investigate microstructure characteristic and mechanical property variations of 100Cr6 steel rings undergoing different pre-heat treatings.The results indicate that the average diameter of carbide particles,the tensile strength and hardness increase,while the elongation decreases with the decrease of cooling rate.The cooling rate has minor effect on the yield strength of sample.After cold ring rolling,the ferrite matrix shows a clear direction along the rolling direction.The distribution of cementite is more homogeneous and the cementite particles are finer.Meanwhile,the hardness of the rolled ring is higher than that before rolling.展开更多
基金Project(2009ZM0296) supported by the Fundamental Research Funds for the Central Universities in China
文摘Abstract： An alloy steel/alumina composite was successfully fabricated by pressureless infiltration of X10CrNil8-8 steel melt on 30% （mass fraction） Ni-containing alumina based composite ceramic （Ni/Al2O3） at 1 600 ℃. The infiltration quality and interfacial bonding behavior were investigated by SEM, EDS, XRD and tensile tests. The results show that there is an obvious interfacial reaction layer between the alloying steel and the Ni/Al2O3 composite ceramic. The interfacial reactive products are （FexAly）3O4 intermetallic phase and （AlxCry）2O3 solid solution. The interracial bonding strength is as high as about 67.5 MPa. The bonding mechanism of X10CrNi 18-8 steel with the composite ceramic is that Ni inside the ceramic bodies dissolves into the alloy melt and transforms into liquid channels, consequently inducing the steel melt infiltrating and filling in the pores and the liquid channels. Moreover, the metallurgical bonding and interfacial reactive bonding also play a key role on the stability of the bonding interface.
基金Project(2011CB706605)supported by the National Basic Research Program of ChinaProject(2011CDA12)supported by the Innovative Research Groups of the Natural Science Foundation of Hubei Province,ChinaProjects(2012-Ia-017,2013-IV-014)supported by the Fundamental Research Funds for the Central Universities,China
文摘Pre-heat treatment is a vital step before cold ring rolling and it has significant effect on the microstructure and mechanical properties of rolled rings.The 100Cr6 steel rings were subjected to pre-heat treatment and subsequent cold rolling process.Scanning electron microscopy and tensile tests were applied to investigate microstructure characteristic and mechanical property variations of 100Cr6 steel rings undergoing different pre-heat treatings.The results indicate that the average diameter of carbide particles,the tensile strength and hardness increase,while the elongation decreases with the decrease of cooling rate.The cooling rate has minor effect on the yield strength of sample.After cold ring rolling,the ferrite matrix shows a clear direction along the rolling direction.The distribution of cementite is more homogeneous and the cementite particles are finer.Meanwhile,the hardness of the rolled ring is higher than that before rolling.