In order to utilize low-grade manganese ore resources effectively, a hydrometallurgical process was developed for manganese extraction in dilute sulfuric acid medium, and the kinetics of leaching manga- nese was also ...In order to utilize low-grade manganese ore resources effectively, a hydrometallurgical process was developed for manganese extraction in dilute sulfuric acid medium, and the kinetics of leaching manga- nese was also investigated. At room temperature, manganese from low-grade manganese carbonate ores was extracted by sulfuric acid leaching without reductants. During the extracting process, single-factor analysis method was used to evaluate the effects of grinding fineness, sulfuric acid concentration, liquid-to-solid ratio, agitation rate and leaching time on the leaching efficiencies of Mn and Fe. The optimal leaching conditions are determined as coarse particles of below 2 mm size （without ball-milling）, sulfuric acid concentration of 0.86 mol/L, liquid-to-solid ratio of 5：1, agitation rate of 150 r/rain and leaching for 180 min at room temperature. Under the optimal conditions, the leaching efficiencies of Mn and Fe are 96.21g and 13.35%, respectively. In addition, through the experiments at different temper- atures, it is found that the leaching process follows the shrinking core model under the conditions of changing acid concentration and intermittent reaction device. Moreover, the apparent activations of effective diffusion and chemical reaction in the kinetic model are calculated to be 18.83 and 27.15 kJ/mol, respectively.展开更多
The leaching kinetics in cyanide media of the silver contained in the Dos Carlos waste tailings at the City of Pachuca de Soto, Hidalgo State, Mexico were carried out. The used material contained the following chemica...The leaching kinetics in cyanide media of the silver contained in the Dos Carlos waste tailings at the City of Pachuca de Soto, Hidalgo State, Mexico were carried out. The used material contained the following chemical composition: 56 10-6of Ag, 0.6 10 6of Au and 70.43%(by weight) of SiO2; 7.032%(by weight) of Al2O3; 2.69%(by weight) of Fe; 0.46%(by weight) of Mn; 3.98%(by weight) of K2O; 3.34%(by weight) of CaO; 2.50%(by weight) of Na2O; 0.04%(by weight) of Zn; 0.026%(by weight) of Pb. The mineralogical phases present were the following: Silica, albite, argentite, berlinite, orthoclase, potassium jarosite, and natrojarosite. In the leaching kinetics in cyanide media, and under the studied conditions,the effect of the CN concentration on the reaction rate has no effect on the whole process of alkaline cyanidation, of which the reaction order is n 0. Temperature has an effect on the cyanidation rate of the reaction, with an activation energy of 47.9 KJ/mol. At the same time, when the particle size decreases there is an increase in the reaction rate, which is inversely proportional to the particle diameter; when increasing the NaOH concentration there is an increase in the reaction rate Kexp, with a reaction order(n) of 0.215 under the studied ranges.展开更多
基金the Key Laboratory of Resources of Nonferrous Metals Ministry of Education (Central South University) for the laboratories and financial support
文摘In order to utilize low-grade manganese ore resources effectively, a hydrometallurgical process was developed for manganese extraction in dilute sulfuric acid medium, and the kinetics of leaching manga- nese was also investigated. At room temperature, manganese from low-grade manganese carbonate ores was extracted by sulfuric acid leaching without reductants. During the extracting process, single-factor analysis method was used to evaluate the effects of grinding fineness, sulfuric acid concentration, liquid-to-solid ratio, agitation rate and leaching time on the leaching efficiencies of Mn and Fe. The optimal leaching conditions are determined as coarse particles of below 2 mm size （without ball-milling）, sulfuric acid concentration of 0.86 mol/L, liquid-to-solid ratio of 5：1, agitation rate of 150 r/rain and leaching for 180 min at room temperature. Under the optimal conditions, the leaching efficiencies of Mn and Fe are 96.21g and 13.35%, respectively. In addition, through the experiments at different temper- atures, it is found that the leaching process follows the shrinking core model under the conditions of changing acid concentration and intermittent reaction device. Moreover, the apparent activations of effective diffusion and chemical reaction in the kinetic model are calculated to be 18.83 and 27.15 kJ/mol, respectively.
基金the Autonomous University of Hidalgo State, Mexico for the financial support
文摘The leaching kinetics in cyanide media of the silver contained in the Dos Carlos waste tailings at the City of Pachuca de Soto, Hidalgo State, Mexico were carried out. The used material contained the following chemical composition: 56 10-6of Ag, 0.6 10 6of Au and 70.43%(by weight) of SiO2; 7.032%(by weight) of Al2O3; 2.69%(by weight) of Fe; 0.46%(by weight) of Mn; 3.98%(by weight) of K2O; 3.34%(by weight) of CaO; 2.50%(by weight) of Na2O; 0.04%(by weight) of Zn; 0.026%(by weight) of Pb. The mineralogical phases present were the following: Silica, albite, argentite, berlinite, orthoclase, potassium jarosite, and natrojarosite. In the leaching kinetics in cyanide media, and under the studied conditions,the effect of the CN concentration on the reaction rate has no effect on the whole process of alkaline cyanidation, of which the reaction order is n 0. Temperature has an effect on the cyanidation rate of the reaction, with an activation energy of 47.9 KJ/mol. At the same time, when the particle size decreases there is an increase in the reaction rate, which is inversely proportional to the particle diameter; when increasing the NaOH concentration there is an increase in the reaction rate Kexp, with a reaction order(n) of 0.215 under the studied ranges.