The dynamic recrystallization behavior of high strength steel during hot deformation was investigated.The hot compression test was conducted in the temperature range of 950-1150 °C under strain rates of 0.1,1 and...The dynamic recrystallization behavior of high strength steel during hot deformation was investigated.The hot compression test was conducted in the temperature range of 950-1150 °C under strain rates of 0.1,1 and 5 s-1.It is observed that dynamic recrystallization(DRX) is the main flow softening mechanism and the flow stress increases with decreasing temperature and increasing strain rate.The relationship between material constants(Q,n,α and ln A) and strain is identified by the sixth order polynomial fit.The constitutive model is developed to predict the flow stress of the material incorporating the strain softening effect and verified.Moreover,the critical characteristics of DRX are extracted from the stress-strain curves under different deformation conditions by linear regression.The dynamic recrystallization volume fraction decreases with increasing strain rate at a constant temperature or decreasing deformation temperature under a constant strain rate.The kinetics of DRX increases with increasing deformation temperature or strain rate.展开更多
The hot deformation behaviors of Cr5 steel were investigated.The hot compression tests were conducted in the temperature range of 900-1150 °C under strain rates of 0.01,0.1 and 1 s^(-1).The constitutive equation ...The hot deformation behaviors of Cr5 steel were investigated.The hot compression tests were conducted in the temperature range of 900-1150 °C under strain rates of 0.01,0.1 and 1 s^(-1).The constitutive equation and material constants(Q,n,α ln A) are obtained according to the hyperbolic sine function and Zener-Hollomon parameter.Besides,dynamic recrystallization(DRX) grain size model and critical strain model are acquired.The processing maps with the strain of 0.1,0.3 and 0.5 are obtained on the basis of dynamic materials model.It has been observed that DRX occurs at high temperature and low strain rate.According to the processing map,the safety region exists in the temperature range of 920-1150 °C with strain rate of 0.01-0.20 s^(-1).展开更多
The effect of pre-recovery on the recrystallization kinetics of a supersaturated Al–Mn alloy annealed at 530°C was investigated.The results show that the pre-recovery treatment can lead to faster recrystallizati...The effect of pre-recovery on the recrystallization kinetics of a supersaturated Al–Mn alloy annealed at 530°C was investigated.The results show that the pre-recovery treatment can lead to faster recrystallization kinetics at the initial stage but cause sluggish recrystallization at the later stage.This different recrystallization behavior is explained by the formation of precipitates-free zones and the consumption of driving force during the pre-recovery treatment.The promoted recrystallization at the early stage can be interpreted by the promotion of recrystallization nucleation through sub-grain growth to a critical size inside precipitates-free zones.A simple model is presented to describe the nucleation of recrystallization with pre-recovery treatment in the supersaturated Al–Mn alloys.展开更多
基金Project (51322405) supported by the National Natural Science Foundation of ChinaProject (CX2013B085) supported by Hunan Provincial Innovation Foundation for Postgraduate,China
文摘The dynamic recrystallization behavior of high strength steel during hot deformation was investigated.The hot compression test was conducted in the temperature range of 950-1150 °C under strain rates of 0.1,1 and 5 s-1.It is observed that dynamic recrystallization(DRX) is the main flow softening mechanism and the flow stress increases with decreasing temperature and increasing strain rate.The relationship between material constants(Q,n,α and ln A) and strain is identified by the sixth order polynomial fit.The constitutive model is developed to predict the flow stress of the material incorporating the strain softening effect and verified.Moreover,the critical characteristics of DRX are extracted from the stress-strain curves under different deformation conditions by linear regression.The dynamic recrystallization volume fraction decreases with increasing strain rate at a constant temperature or decreasing deformation temperature under a constant strain rate.The kinetics of DRX increases with increasing deformation temperature or strain rate.
基金Project(51322405)supported by the National Natural Science Foundation of China
文摘The hot deformation behaviors of Cr5 steel were investigated.The hot compression tests were conducted in the temperature range of 900-1150 °C under strain rates of 0.01,0.1 and 1 s^(-1).The constitutive equation and material constants(Q,n,α ln A) are obtained according to the hyperbolic sine function and Zener-Hollomon parameter.Besides,dynamic recrystallization(DRX) grain size model and critical strain model are acquired.The processing maps with the strain of 0.1,0.3 and 0.5 are obtained on the basis of dynamic materials model.It has been observed that DRX occurs at high temperature and low strain rate.According to the processing map,the safety region exists in the temperature range of 920-1150 °C with strain rate of 0.01-0.20 s^(-1).
基金Project(2016YFB0300901)supported by National Key R&D Program of ChinaProject(51421001)supported by the National Natural Science Foundation of ChinaProject(106112015CDJXY130003)supported by the Fundamental Research Funds for the Central Universities,China
文摘The effect of pre-recovery on the recrystallization kinetics of a supersaturated Al–Mn alloy annealed at 530°C was investigated.The results show that the pre-recovery treatment can lead to faster recrystallization kinetics at the initial stage but cause sluggish recrystallization at the later stage.This different recrystallization behavior is explained by the formation of precipitates-free zones and the consumption of driving force during the pre-recovery treatment.The promoted recrystallization at the early stage can be interpreted by the promotion of recrystallization nucleation through sub-grain growth to a critical size inside precipitates-free zones.A simple model is presented to describe the nucleation of recrystallization with pre-recovery treatment in the supersaturated Al–Mn alloys.