The mechanism of oxygen pressure acid leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation was investigated in this study.Artificial sphalerite was fabricated with varying amounts of iron content via the ...The mechanism of oxygen pressure acid leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation was investigated in this study.Artificial sphalerite was fabricated with varying amounts of iron content via the sintering of ZnS and FeS and used for the pressure acid leaching experiment.The variations in the potential of the pressure leaching system were investigated by using a self-designed potential autoclave.The results showed that compared to the non-iron sphalerite,there was a violent redox reaction between the 25.70%Fe-artificial sphalerite and dissolved oxygen during the process of pressure leaching;and the catalytic mechanism was attributed to the redox couple Fe^3+/Fe^2+,where Fe3+oxidizes the H2S gas film and the reduced Fe2+state is subsequently oxidized by the dissolved oxygen.Furthermore,the effect of temperature,H2SO4 concentration,and oxygen partial pressure on the artificial sphalerite with different iron contents was studied.The sphalerite samples with iron content were observed to dissolve more easily in sulfuric acid compared to the non-iron samples.Moreover,the activation energy of artificial sphalerite was observed to be lower in the sample with 25.70%iron content(22.26 kJ/mol)compared to that with no iron(32.31 kJ/mol);and the apparent reaction orders were obtained with respect to H2SO4 concentration(1.10 and 1.36)and oxygen partial pressure(1.29 and 1.41),respectively.A comprehensive kinetic model was developed on the basis of the experimental data and the fitted leaching ratio plot;and the kinetic equations for the leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation were determined.展开更多
A new technology was developed to recover multiple valuable elements from the spent Al2O3-based catalyst by X-ray phase analysis and exploratory experiments. The experimental results show that in the condition of roas...A new technology was developed to recover multiple valuable elements from the spent Al2O3-based catalyst by X-ray phase analysis and exploratory experiments. The experimental results show that in the condition of roasting temperature of 750℃ and roasting time of 30 min, molar ratio of Na2O to Al2O3 of 1.2, the leaching rates of alumina, vanadium and molybdenum in the spent catalyst are 97.2%, 95.8% and 98.9%, respectively. Vanadium and molybdenum in sodium aluminate solution can be recovered by precipitators A and B, and the precipitation rates of vanadium and molybdenum are 94.8% and 92.6%. Al（OH）3 was prepared from sodium aluminate solution in the carbonation decomposition process, and the purity of Al2O3 is 99.9% after calcination, the recovery of alumina reaches 90.6% in the whole process; the Ni-Co concentrate was leached by sulfuric acid, a nickel recovery of 98.2% and cobalt recovery over 98.5% can be obtained under the experimental condition of 30% H2SO4, 80℃, reaction time 4 h, mass ratio of liquid to solid 8, stirring rate 800r/min.展开更多
Sulfuric acid leaching process was applied to extract nickel from roasting-dissolving residue of a spent catalyst, the effect of different parameters on nickel extraction was investigated by leaching experiments, and ...Sulfuric acid leaching process was applied to extract nickel from roasting-dissolving residue of a spent catalyst, the effect of different parameters on nickel extraction was investigated by leaching experiments, and the leaching kinetics of nickel was analyzed. The experimental results indicate that the effects of particle size and sulfuric acid concentration on the nickel extraction are remarkable; the effect of reaction temperature is mild; while the effect of stirring speed in the range of 400-1 200 r/min is negligible. Decreasing particle size or increasing sulfuric acid concentration and reaction temperature, the nickel extraction efficiency is improved. 93.5% of nickel in residue is extracted under suitable leaching conditions, including particle size （0.074-0.100） mm, sulfuric acid concentration 30% （mass fraction）, temperature 80 ~C, reaction time 180 min, mass ratio of liquid to solid 10 and stirring speed 800 r/min. The leaching kinetics analyses shows that the reaction rate of leaching process is controlled by diffusion through the product layer, and the calculated activation energy of 15.8 kJ/mol is characteristic for a diffusion controlled process.展开更多
基金Projects(51804136,51764016)supported by the National Natural Science Foundation of ChinaProject(U1402271)supported by the Joint Funds of the National Natural Science Foundation of China+2 种基金Project(20181BAB216017)supported by the Jiangxi Provincial Natural Science Foundation,ChinaProject(GK-201803)supported by the Research Fund Program of State Key Laboratory of Rare Metals Separation and Comprehensive Utilization,ChinaProjects(yy2016001,yy2016012)supported by the Research Fund Program of the State Key Laboratory of Pressure Hydrometallurgical Technology of Associated Nonferrous Metal Resources,China。
文摘The mechanism of oxygen pressure acid leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation was investigated in this study.Artificial sphalerite was fabricated with varying amounts of iron content via the sintering of ZnS and FeS and used for the pressure acid leaching experiment.The variations in the potential of the pressure leaching system were investigated by using a self-designed potential autoclave.The results showed that compared to the non-iron sphalerite,there was a violent redox reaction between the 25.70%Fe-artificial sphalerite and dissolved oxygen during the process of pressure leaching;and the catalytic mechanism was attributed to the redox couple Fe^3+/Fe^2+,where Fe3+oxidizes the H2S gas film and the reduced Fe2+state is subsequently oxidized by the dissolved oxygen.Furthermore,the effect of temperature,H2SO4 concentration,and oxygen partial pressure on the artificial sphalerite with different iron contents was studied.The sphalerite samples with iron content were observed to dissolve more easily in sulfuric acid compared to the non-iron samples.Moreover,the activation energy of artificial sphalerite was observed to be lower in the sample with 25.70%iron content(22.26 kJ/mol)compared to that with no iron(32.31 kJ/mol);and the apparent reaction orders were obtained with respect to H2SO4 concentration(1.10 and 1.36)and oxygen partial pressure(1.29 and 1.41),respectively.A comprehensive kinetic model was developed on the basis of the experimental data and the fitted leaching ratio plot;and the kinetic equations for the leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation were determined.
基金Project(2003 UDBEA00C020) supported by the Collaborative Project of School and Province of Yunnan Province
文摘A new technology was developed to recover multiple valuable elements from the spent Al2O3-based catalyst by X-ray phase analysis and exploratory experiments. The experimental results show that in the condition of roasting temperature of 750℃ and roasting time of 30 min, molar ratio of Na2O to Al2O3 of 1.2, the leaching rates of alumina, vanadium and molybdenum in the spent catalyst are 97.2%, 95.8% and 98.9%, respectively. Vanadium and molybdenum in sodium aluminate solution can be recovered by precipitators A and B, and the precipitation rates of vanadium and molybdenum are 94.8% and 92.6%. Al（OH）3 was prepared from sodium aluminate solution in the carbonation decomposition process, and the purity of Al2O3 is 99.9% after calcination, the recovery of alumina reaches 90.6% in the whole process; the Ni-Co concentrate was leached by sulfuric acid, a nickel recovery of 98.2% and cobalt recovery over 98.5% can be obtained under the experimental condition of 30% H2SO4, 80℃, reaction time 4 h, mass ratio of liquid to solid 8, stirring rate 800r/min.
基金Project (50574101) supported by the National Natural Science Foundation of ChinaProject (2003UDBEA00C020) supported by the Collaborative Project of School and Province of Yunnan Province,China
文摘Sulfuric acid leaching process was applied to extract nickel from roasting-dissolving residue of a spent catalyst, the effect of different parameters on nickel extraction was investigated by leaching experiments, and the leaching kinetics of nickel was analyzed. The experimental results indicate that the effects of particle size and sulfuric acid concentration on the nickel extraction are remarkable; the effect of reaction temperature is mild; while the effect of stirring speed in the range of 400-1 200 r/min is negligible. Decreasing particle size or increasing sulfuric acid concentration and reaction temperature, the nickel extraction efficiency is improved. 93.5% of nickel in residue is extracted under suitable leaching conditions, including particle size （0.074-0.100） mm, sulfuric acid concentration 30% （mass fraction）, temperature 80 ~C, reaction time 180 min, mass ratio of liquid to solid 10 and stirring speed 800 r/min. The leaching kinetics analyses shows that the reaction rate of leaching process is controlled by diffusion through the product layer, and the calculated activation energy of 15.8 kJ/mol is characteristic for a diffusion controlled process.