The effects of low temperature thermo-mechanical treatment （LTTMT） on microstructures and mechanical properties of Ti-6Al-4V （TC4） alloy were studied by optical microscopy （OM）, tensile test, scanning electron m...The effects of low temperature thermo-mechanical treatment （LTTMT） on microstructures and mechanical properties of Ti-6Al-4V （TC4） alloy were studied by optical microscopy （OM）, tensile test, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results confirm that the strength of TC4 alloy can be improved obviously by LTTMT processing, which combines strain strengthening with aging strengthening. The effect of LTTMT on the alloy depends on the microstructure of the refined and dispersed a＋fl phase on the basis of high dislocation density by pre-deformation below recrystallization temperature. The tensile strength decreases with the increase of pre-deformation reduction. The optimal processing parameters of LTTMT for TC4 alloy are as follows： solution treatment at 900 ℃ for 15 min, pre-deformation in the range of 600-700 ℃ with a reduction of 35%, finally aging at 540 ℃ for 4 h followed by air-cooling.展开更多
The influences of BaCu（B2O5） （BCB） addition on sintering, microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry, scanning electron microscopy and mi...The influences of BaCu（B2O5） （BCB） addition on sintering, microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry, scanning electron microscopy and microwave dielectric measurements. The experimental results show that a small amount of BaCu（B2O5） addition can effectively reduce the sintering temperature to 900℃, and induce only a limited degradation of the microwave dielectric properties. Typically, the best microwave dielectric properties of er24.5, Q×f =24 622 GHz, rf=4.2×10-6℃ -1 are obtained for 1.0% BCB-doped Li2MgTi3O8 ceramics sintered at 900℃ for 3 h. The BCB-doped Li2MgTi3O8 ceramics can be compatible with Ag electrode, which may be a strong candidate for low temperature co-fired ceramics applications.展开更多
文摘W962834 大麦发芽力估测方法的评价[告,英]/Parker,D.K.…∥HGCA Project Report.-London,UK:Home Grown Cereals Authority,1994,(100).-83p[WBTA,1996,13(1),674]W962835 利用热解重力法研究 ambiol 对大麦种子膨胀的影响[刊,英]/Voronina,S.S.…∥BiologyBulletin of the Russian Academy of Sciences.-1994,21(3).-363～365[WBTA,1996,13(1),675]W962836
基金Project(2008WK2005) supported by the Science and Technology Plan of Hunan Province, China
文摘The effects of low temperature thermo-mechanical treatment （LTTMT） on microstructures and mechanical properties of Ti-6Al-4V （TC4） alloy were studied by optical microscopy （OM）, tensile test, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results confirm that the strength of TC4 alloy can be improved obviously by LTTMT processing, which combines strain strengthening with aging strengthening. The effect of LTTMT on the alloy depends on the microstructure of the refined and dispersed a＋fl phase on the basis of high dislocation density by pre-deformation below recrystallization temperature. The tensile strength decreases with the increase of pre-deformation reduction. The optimal processing parameters of LTTMT for TC4 alloy are as follows： solution treatment at 900 ℃ for 15 min, pre-deformation in the range of 600-700 ℃ with a reduction of 35%, finally aging at 540 ℃ for 4 h followed by air-cooling.
基金Project(2010GXNSFA013029) supported by the Natural Science Foundation of Guangxi Province,ChinaProject(101059529) supported by National Undergraduate Innovation Program of the Ministry of Education of China
文摘The influences of BaCu（B2O5） （BCB） addition on sintering, microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry, scanning electron microscopy and microwave dielectric measurements. The experimental results show that a small amount of BaCu（B2O5） addition can effectively reduce the sintering temperature to 900℃, and induce only a limited degradation of the microwave dielectric properties. Typically, the best microwave dielectric properties of er24.5, Q×f =24 622 GHz, rf=4.2×10-6℃ -1 are obtained for 1.0% BCB-doped Li2MgTi3O8 ceramics sintered at 900℃ for 3 h. The BCB-doped Li2MgTi3O8 ceramics can be compatible with Ag electrode, which may be a strong candidate for low temperature co-fired ceramics applications.