Large-area two-dimensional(2D)materials,such as graphene,MoS_(2),WS_(2),h-BN,black phosphorus,and MXenes,are a class of advanced materials with many possible applications.Different applications need different substrat...Large-area two-dimensional(2D)materials,such as graphene,MoS_(2),WS_(2),h-BN,black phosphorus,and MXenes,are a class of advanced materials with many possible applications.Different applications need different substrates,and each substrate may need a different way of transferring the 2D material onto it.Problems such as local stress concentrations,an uneven surface tension,inconsistent adhesion,mechanical damage and contamination during the transfer can adversely affect the quality and properties of the transferred material.Therefore,how to improve the integrity,flatness and cleanness of large area 2D materials is a challenge.In order to achieve high-quality transfer,the main concern is to control the interface adhesion between the substrate,the 2D material and the transfer medium.This review focuses on this topic,and finally,in order to promote the industrial use of large area 2D materials,provides a recipe for this transfer process based on the requirements of the application,and points out the current problems and directions for future development.展开更多
Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coati...Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition(CVD)technique.Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces.Additionally,the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test.The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2%(volume fraction)and 11.1%,and 40.7%(volume fraction)and 7.5%,respectively.And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa,and 180.2 MPa and 97.2 GPa,respectively.With a proper thickness,the coating can effectively adjust the fiber/matrix interface,thus causing a dramatic increase in the mechanical properties of the composites.展开更多
基金the National Key R&D Program of China(2022YFA1505200)the National Natural Science Foundation of China(22472140,22021001)the Fundamental Research Funds for the Central Universities(20720210017 and 20720210009)。
文摘Large-area two-dimensional(2D)materials,such as graphene,MoS_(2),WS_(2),h-BN,black phosphorus,and MXenes,are a class of advanced materials with many possible applications.Different applications need different substrates,and each substrate may need a different way of transferring the 2D material onto it.Problems such as local stress concentrations,an uneven surface tension,inconsistent adhesion,mechanical damage and contamination during the transfer can adversely affect the quality and properties of the transferred material.Therefore,how to improve the integrity,flatness and cleanness of large area 2D materials is a challenge.In order to achieve high-quality transfer,the main concern is to control the interface adhesion between the substrate,the 2D material and the transfer medium.This review focuses on this topic,and finally,in order to promote the industrial use of large area 2D materials,provides a recipe for this transfer process based on the requirements of the application,and points out the current problems and directions for future development.
基金Project(NCET-07-0228)support by the New Century Excellent Talents in University
文摘Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition(CVD)technique.Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces.Additionally,the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test.The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2%(volume fraction)and 11.1%,and 40.7%(volume fraction)and 7.5%,respectively.And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa,and 180.2 MPa and 97.2 GPa,respectively.With a proper thickness,the coating can effectively adjust the fiber/matrix interface,thus causing a dramatic increase in the mechanical properties of the composites.