Compound [Co 3(BTC)(HBTC)(H 2BTC)(C 2H 4O 2) 3]·3(DMF)·6(H 3O) was synthesized under mild conditions and its crystal structure was determined by using single crystal X-ray diffraction. The crystal structure ...Compound [Co 3(BTC)(HBTC)(H 2BTC)(C 2H 4O 2) 3]·3(DMF)·6(H 3O) was synthesized under mild conditions and its crystal structure was determined by using single crystal X-ray diffraction. The crystal structure was solved by direct method and refined by full-matrix least-square method. The crystal is monoclinic and belongs to space group Cc with a=2.645 3(5) nm, b= 1.670 4(3) nm, c=1\^821 6(4) nm, β=128.16(3) °, V=6.329(2) nm 3, Z=2 , D c=20.200 Mg/m 3, M r= 1 314.744, μ=10.274 mm -1, F(000) =38 226, GOF=0.99, R=0.094 1, ωR=0.257 3.展开更多
将有机-无机杂化功能材料与有序大孔材料独特的有序开孔结构相结合,在制备的三维有序大孔二氧化硅(3DOM Si O2)孔壁上可控接枝带有功能基团的聚合物链段,制备3DOM杂化材料。采用表面引发原子转移自由基(SI-ATRP)接枝技术在3DOM Si O2孔...将有机-无机杂化功能材料与有序大孔材料独特的有序开孔结构相结合,在制备的三维有序大孔二氧化硅(3DOM Si O2)孔壁上可控接枝带有功能基团的聚合物链段,制备3DOM杂化材料。采用表面引发原子转移自由基(SI-ATRP)接枝技术在3DOM Si O2孔壁上可控接枝聚甲基丙烯酸缩水甘油酯(PGMA)链段,讨论了接枝条件对接枝量及接枝链段分子量的影响,并利用FTIR、SEM、TGA、GPC等对接枝过程进行了表征。PGMA接枝链段上环氧基团可进一步与亲核试剂(二乙醇胺,浓硫酸和二乙烯三胺)发生开环反应,得到一系列带有不同官能团的具有较高接枝密度的功能杂化多孔材料,同时,利用该种材料对水中的水杨酸进行了吸附实验,吸附结果表明经二乙烯三胺开环后得到的功能化多孔材料对水杨酸具有很高的吸附量。展开更多
文摘Compound [Co 3(BTC)(HBTC)(H 2BTC)(C 2H 4O 2) 3]·3(DMF)·6(H 3O) was synthesized under mild conditions and its crystal structure was determined by using single crystal X-ray diffraction. The crystal structure was solved by direct method and refined by full-matrix least-square method. The crystal is monoclinic and belongs to space group Cc with a=2.645 3(5) nm, b= 1.670 4(3) nm, c=1\^821 6(4) nm, β=128.16(3) °, V=6.329(2) nm 3, Z=2 , D c=20.200 Mg/m 3, M r= 1 314.744, μ=10.274 mm -1, F(000) =38 226, GOF=0.99, R=0.094 1, ωR=0.257 3.
文摘将有机-无机杂化功能材料与有序大孔材料独特的有序开孔结构相结合,在制备的三维有序大孔二氧化硅(3DOM Si O2)孔壁上可控接枝带有功能基团的聚合物链段,制备3DOM杂化材料。采用表面引发原子转移自由基(SI-ATRP)接枝技术在3DOM Si O2孔壁上可控接枝聚甲基丙烯酸缩水甘油酯(PGMA)链段,讨论了接枝条件对接枝量及接枝链段分子量的影响,并利用FTIR、SEM、TGA、GPC等对接枝过程进行了表征。PGMA接枝链段上环氧基团可进一步与亲核试剂(二乙醇胺,浓硫酸和二乙烯三胺)发生开环反应,得到一系列带有不同官能团的具有较高接枝密度的功能杂化多孔材料,同时,利用该种材料对水中的水杨酸进行了吸附实验,吸附结果表明经二乙烯三胺开环后得到的功能化多孔材料对水杨酸具有很高的吸附量。