Composite polymer electrolytes based on polyethylene oxide(PEO) were prepared by using LiClO4 as doping salt and silane-modified SiO2 as filler. SiO2 was formed in-situ in (PEO)8LiClO4 matrix by the hydrolysis and con...Composite polymer electrolytes based on polyethylene oxide(PEO) were prepared by using LiClO4 as doping salt and silane-modified SiO2 as filler. SiO2 was formed in-situ in (PEO)8LiClO4 matrix by the hydrolysis and condensation reaction of Si(OC4H9)4. The crystallinity,morphology and ionic conductivity of composite polymer electrolyte films were examined by differential scanning calorimetry,scanning electron microscopy,atom force microscopy and alternating current impedance spectroscopy,respectively. Compared with the crystallinity of the unmodified SiO2 as inert filler,that of composite polymer electrolytes is decreased. The results show that silane-modified SiO2 particles are uniformly dispersed in (PEO)8LiClO4 composite polymer electrolyte film and the addition of silane-modified SiO2 increases the ionic conductivity of the (PEO)8LiClO4 more noticeably. When the mass fraction of SiO2 is about 10%,the conductivity of (PEO)8LiClO4-modified SiO2 attains a maximum value of 4.8×10-5 S·cm-1.展开更多
A new direct recycling technology was developed to recover the valuable metals present in the stainless steelmaking dust and protect the environment. The agglomeration behavior of the dust was analyzed to ensure the r...A new direct recycling technology was developed to recover the valuable metals present in the stainless steelmaking dust and protect the environment. The agglomeration behavior of the dust was analyzed to ensure the requirements of the direct recycling. The main characteristics such as strength, leachability, structure and chemical composition of the pellets were investigated. SEM images show a significant amount of porosities affecting the strength of the pellets and the arrangement of particles in the pellets reveals that no recrystallization bonds are formed, resulting in the poor strength of the pellets. When lignosulfonate is applied as the binder for the agglomeration and the green pellets are dried at room temperature for 60 h, the strong pellets can be obtained without milling the dust. The result of leachability tests shows that the pellets agglomerated can not satisfy the regulations set by the environmental protection agency of US. And it will cause some environmental problems in the long storage of pellets.展开更多
文摘Composite polymer electrolytes based on polyethylene oxide(PEO) were prepared by using LiClO4 as doping salt and silane-modified SiO2 as filler. SiO2 was formed in-situ in (PEO)8LiClO4 matrix by the hydrolysis and condensation reaction of Si(OC4H9)4. The crystallinity,morphology and ionic conductivity of composite polymer electrolyte films were examined by differential scanning calorimetry,scanning electron microscopy,atom force microscopy and alternating current impedance spectroscopy,respectively. Compared with the crystallinity of the unmodified SiO2 as inert filler,that of composite polymer electrolytes is decreased. The results show that silane-modified SiO2 particles are uniformly dispersed in (PEO)8LiClO4 composite polymer electrolyte film and the addition of silane-modified SiO2 increases the ionic conductivity of the (PEO)8LiClO4 more noticeably. When the mass fraction of SiO2 is about 10%,the conductivity of (PEO)8LiClO4-modified SiO2 attains a maximum value of 4.8×10-5 S·cm-1.
文摘A new direct recycling technology was developed to recover the valuable metals present in the stainless steelmaking dust and protect the environment. The agglomeration behavior of the dust was analyzed to ensure the requirements of the direct recycling. The main characteristics such as strength, leachability, structure and chemical composition of the pellets were investigated. SEM images show a significant amount of porosities affecting the strength of the pellets and the arrangement of particles in the pellets reveals that no recrystallization bonds are formed, resulting in the poor strength of the pellets. When lignosulfonate is applied as the binder for the agglomeration and the green pellets are dried at room temperature for 60 h, the strong pellets can be obtained without milling the dust. The result of leachability tests shows that the pellets agglomerated can not satisfy the regulations set by the environmental protection agency of US. And it will cause some environmental problems in the long storage of pellets.
