The pronounced anisotropy in mechanical properties presents a major obstacle to the extensive application of aluminum-lithium(Al-Li)alloys,primarily attributed to heterogeneous precipitate distribution,grain structure...The pronounced anisotropy in mechanical properties presents a major obstacle to the extensive application of aluminum-lithium(Al-Li)alloys,primarily attributed to heterogeneous precipitate distribution,grain structure variations,and crystallographic texture.This study investigates the impact of pre-thermal treatment prior to hot rolling and aging treatment on the anisotropy of mechanical properties of 2195 alloy sheet fabricated by gas atomization,hot pressing and hot rolling.The results demonstrate that pre-treatment at 450℃for 4 h promotes finer and more uniform distribution of precipitates,effectively mitigating mechanical anisotropy of the alloy sheet.Additionally,this treatment facilitates recrystallization during hot rolling,further reducing mechanical anisotropy.The in-plane anisotropy(IPA)factors for ultimate tensile strength(UTS)and yield strength(YS)are 1.15%and 0.77%,respectively.Subsequent aging treatment enhances grain refinement and the uniformity of the T_(1) phase,suppresses the formation of precipitation-free zones(PFZs),significantly improving the strength and toughness of the alloy sheet.After peak aging at 165℃for 48 h,the alloy sheet exhibits YS of 547 MPa,UTS of 590 MPa,and elongation(EL)of 7.7%.展开更多
In this paper,equal channel angular pressing and thermomechanical treatment was employed to improve the strength and electrical conductivity of an aging strengthened Cu-Ti-Cr-Mg alloy,and the microstructure and proper...In this paper,equal channel angular pressing and thermomechanical treatment was employed to improve the strength and electrical conductivity of an aging strengthened Cu-Ti-Cr-Mg alloy,and the microstructure and properties of the alloy were investigated in detail.The results showed that the samples deformed by the combination of cryogenic equal channel angular pressing(ECAP)and rolling had good comprehensive properties after aging at 400℃.The tensile strength of the peak-aged and over-aged samples was 1120 MPa and 940 MPa,with their corresponding electrical conductivity of 14.7%IACS and 22.1%IACS,respectively.ECAP and cryogenic rolling introduced high density dislocations,leading to the inhibition of the softening effects and refinement of the grains.After a long time aging at 400℃,the alloy exhibited ultra-high strength with obvious increasing electrical conductivity.The high strength was attributed to the synergistic effect of work hardening,grain refinement strengthening and precipitation strengthening.The precipitation of a large amount of Ti atoms from the matrix led to the high electrical conductivity of the over-aged sample.展开更多
This paper studied the influence of aging treatment on the corrosion behavior and mechanism of Mg-Y alloys with different Y content through corrosion mass loss test, electrochemical test and corrosion morphologies obs...This paper studied the influence of aging treatment on the corrosion behavior and mechanism of Mg-Y alloys with different Y content through corrosion mass loss test, electrochemical test and corrosion morphologies observation. Results show that the peak-aging times of Mg-（0.25, 2.5, 5, 8 and 15） Y alloys at 250 ℃ were 4, 6, 10, 12 and 16 h. The aging treatment reduced the corrosion resistance of Mg-Y alloys, and the corrosion resistance of Mg-Y alloys became worse with increasing of the aging time. The change magnitude of the open circuit potentials for Mg-（0.25, 2.5）Y alloys was greater than that of Mg-（5, 8 and 15）-Y alloys. The polarization curves of Mg （0.25, 2.5, 5, 8 and 15） Y alloys had the similar shape after aging treatment, and the slopes of the anodic branch were greater than those of the cathodic branches. After aging treatment, the corrosion modes of Mg-0.25Y and Mg-（2.5, 5, 8 and 15） Y alloys were uniform corrosion and pitting corrosion with small local deep corrosion.展开更多
The magnetic performance and mechanical properties including hardness, brittleness, fracture toughness and strength characteristics of the as-sintered and the optimal aged Nd-Fe-B magnets were examined in this work. A...The magnetic performance and mechanical properties including hardness, brittleness, fracture toughness and strength characteristics of the as-sintered and the optimal aged Nd-Fe-B magnets were examined in this work. A new method of Vickers hardness indentation combined with acoustic emission was used to test the brittleness of the magnets.The results show that the magnetic properties of the magnets could be improved through aging treatment, especially the intrinsic coercive force. But it is accompanied by a decrease of strength and fracture toughness. Theoretical calculation confirms that acoustic emission energy accumulated count value could be used to characterize the material brittleness. The bending fracture morphologies of the as-sintered and the optimal aged Nd Fe B magnets were investigated with the emphasis on the relationship between mechanical properties and microstructure using a field emission scanning electron microscopy(FE-SEM). The research results indicate that the intergranular fracture is the primary fracture mechanism for both as-sintered and optimal aged Nd Fe B magnets. Aging treatment changes the morphology and distribution of the Nd-rich phases, reducing the sliding resistance between Nd_2Fe_(14)B main crystal grains and lowers the grain boundary strength, which is the main reason for the strength and fracture toughness decrease of the aged Nd-Fe-B magnets.展开更多
The effects of pre-aging treatments on subsequent artificial aging response were investigated by means of transmission electron microscopy observations and hardness test in age hardened Al-3.95Cu-(1.32Mg)-0.52Mn-0.11 ...The effects of pre-aging treatments on subsequent artificial aging response were investigated by means of transmission electron microscopy observations and hardness test in age hardened Al-3.95Cu-(1.32Mg)-0.52Mn-0.11 Zr alloys. In Al-3.95Cu-0.52Mn-0.11 Zr alloy, when the pre-aging temperature is 25 °C, the pre-aging treatment has no evident effect on the peak hardness of subsequent artificial aging, while a positive effect(increase of peak hardness) appears when pre-aging temperature is50 °C. However, in Al-3.95Cu-1.32Mg-0.52Mn-0.11 Zr alloy, it is found that whether the pre-aging temperature is 25 °C or 50 °C,the peak artificial aging hardness is lower than that of T6 treated alloy, that is to say, pre-aging treatment has a negative effect on the peak hardness of subsequent artificial aging in the alloys.展开更多
Superior properties of maraging steels make them suitable for the fabrication of components used for military applications like missile covering, rocket motor casing and ship hulls. Welding is the main process for fab...Superior properties of maraging steels make them suitable for the fabrication of components used for military applications like missile covering, rocket motor casing and ship hulls. Welding is the main process for fabrication of these components, while the maraging steels can be fusion welded using gas tungsten arc welding(GTAW) process. All these fabricated components require longer storage life and a major problem in welds is susceptible to stress corrosion cracking(SCC). The present study is aimed at studying the SCC behaviour of MDN 250(18% Ni) steel and its welds with respect to microstructural changes. In the present study, 5.2 mm thick sheets made of MDN 250 steel in the solution annealed condition was welded using GTAW process. Post-weld heat treatments of direct ageing(480 C for 3 h), solutionizing(815 C for 1 h) followed by ageing and homogenizing(1150 C for 1 h) followed by ageing were carried out. A mixture of martensite and austenite was observed in the microstructure of the fusion zone of solutionized and direct aged welds and only martensite in as-welded condition. Homogenization and ageing treatment have eliminated reverted austenite and elemental segregation. Homogenized welds also exhibited a marginal improvement in the corrosion resistance compared to those in the as-welded, solutionized and aged condition. Constant load SCC test data clearly revealed that the failure time of homogenized weld is much longer compared to other post weld treatments, and the homogenization treatment is recommended to improve the SCC life of GTA welds of MDN 250 Maraging steel.展开更多
V-5Cr-5Ti alloys have been fabricated using a laser melting deposition(LMD)additive manufacturing process,showing precipitates aggregated near the grain/dendrite boundaries.Since the mechanical properties of vanadium ...V-5Cr-5Ti alloys have been fabricated using a laser melting deposition(LMD)additive manufacturing process,showing precipitates aggregated near the grain/dendrite boundaries.Since the mechanical properties of vanadium alloys considerably depend on the precipitates,solution and aging treatments have been applied to eliminating the aggregations of the precipitates.The results show that as the solution temperature increases from 800 to 1560℃,the densities and the lengths of the precipitates are reduced,while the widths of the precipitates are increased.When the solution temperature reaches 1560℃,most impurity elements diffuse into the matrix and form into a nearly uniform supersaturated solid solution.Aging treatments have been applied to the 1560℃solution treated samples.It shows that as the aging temperature increases from 800 to 1200℃,the precipitate length increases,and the shapes of precipitates change from near-spherical to lath-like.Compared to 800 and 1200℃,aging at 1000℃results in the highest precipitate density.Compared to the LMD and solution-treated samples,the aged samples have the highest micro-hardness,due to the precipitation strengthening.展开更多
基金Project(52274369)supported by the National Natural Science Foundation of ChinaProject(623020034)supported by the National Key Laboratory of Science and Technology on High-strength Structural Materials,China。
文摘The pronounced anisotropy in mechanical properties presents a major obstacle to the extensive application of aluminum-lithium(Al-Li)alloys,primarily attributed to heterogeneous precipitate distribution,grain structure variations,and crystallographic texture.This study investigates the impact of pre-thermal treatment prior to hot rolling and aging treatment on the anisotropy of mechanical properties of 2195 alloy sheet fabricated by gas atomization,hot pressing and hot rolling.The results demonstrate that pre-treatment at 450℃for 4 h promotes finer and more uniform distribution of precipitates,effectively mitigating mechanical anisotropy of the alloy sheet.Additionally,this treatment facilitates recrystallization during hot rolling,further reducing mechanical anisotropy.The in-plane anisotropy(IPA)factors for ultimate tensile strength(UTS)and yield strength(YS)are 1.15%and 0.77%,respectively.Subsequent aging treatment enhances grain refinement and the uniformity of the T_(1) phase,suppresses the formation of precipitation-free zones(PFZs),significantly improving the strength and toughness of the alloy sheet.After peak aging at 165℃for 48 h,the alloy sheet exhibits YS of 547 MPa,UTS of 590 MPa,and elongation(EL)of 7.7%.
基金Project(U2202255)supported by the National Natural Science Foundation of ChinaProject(2024JJ2076)supported by the Hunan Provincial Natural Science Foundation of ChinaProject(2023Z092)supported by the Key Technology Research Program of Ningbo,China。
文摘In this paper,equal channel angular pressing and thermomechanical treatment was employed to improve the strength and electrical conductivity of an aging strengthened Cu-Ti-Cr-Mg alloy,and the microstructure and properties of the alloy were investigated in detail.The results showed that the samples deformed by the combination of cryogenic equal channel angular pressing(ECAP)and rolling had good comprehensive properties after aging at 400℃.The tensile strength of the peak-aged and over-aged samples was 1120 MPa and 940 MPa,with their corresponding electrical conductivity of 14.7%IACS and 22.1%IACS,respectively.ECAP and cryogenic rolling introduced high density dislocations,leading to the inhibition of the softening effects and refinement of the grains.After a long time aging at 400℃,the alloy exhibited ultra-high strength with obvious increasing electrical conductivity.The high strength was attributed to the synergistic effect of work hardening,grain refinement strengthening and precipitation strengthening.The precipitation of a large amount of Ti atoms from the matrix led to the high electrical conductivity of the over-aged sample.
基金Projects(2011BAE22B01,2011BAE22B06)supported by the National Key Technology R&D Program,China
文摘This paper studied the influence of aging treatment on the corrosion behavior and mechanism of Mg-Y alloys with different Y content through corrosion mass loss test, electrochemical test and corrosion morphologies observation. Results show that the peak-aging times of Mg-（0.25, 2.5, 5, 8 and 15） Y alloys at 250 ℃ were 4, 6, 10, 12 and 16 h. The aging treatment reduced the corrosion resistance of Mg-Y alloys, and the corrosion resistance of Mg-Y alloys became worse with increasing of the aging time. The change magnitude of the open circuit potentials for Mg-（0.25, 2.5）Y alloys was greater than that of Mg-（5, 8 and 15）-Y alloys. The polarization curves of Mg （0.25, 2.5, 5, 8 and 15） Y alloys had the similar shape after aging treatment, and the slopes of the anodic branch were greater than those of the cathodic branches. After aging treatment, the corrosion modes of Mg-0.25Y and Mg-（2.5, 5, 8 and 15） Y alloys were uniform corrosion and pitting corrosion with small local deep corrosion.
基金Project((2012)1743)supported by the China National Major Special Program for the Rare Earth and Rare Metallic Materials
文摘The magnetic performance and mechanical properties including hardness, brittleness, fracture toughness and strength characteristics of the as-sintered and the optimal aged Nd-Fe-B magnets were examined in this work. A new method of Vickers hardness indentation combined with acoustic emission was used to test the brittleness of the magnets.The results show that the magnetic properties of the magnets could be improved through aging treatment, especially the intrinsic coercive force. But it is accompanied by a decrease of strength and fracture toughness. Theoretical calculation confirms that acoustic emission energy accumulated count value could be used to characterize the material brittleness. The bending fracture morphologies of the as-sintered and the optimal aged Nd Fe B magnets were investigated with the emphasis on the relationship between mechanical properties and microstructure using a field emission scanning electron microscopy(FE-SEM). The research results indicate that the intergranular fracture is the primary fracture mechanism for both as-sintered and optimal aged Nd Fe B magnets. Aging treatment changes the morphology and distribution of the Nd-rich phases, reducing the sliding resistance between Nd_2Fe_(14)B main crystal grains and lowers the grain boundary strength, which is the main reason for the strength and fracture toughness decrease of the aged Nd-Fe-B magnets.
基金Project(2006AA03Z517)supported by the National High-tech Research and Development Program of ChinaProject(CSUZC2013019)supported by Open Fund for the Precision Instruments of Central South University,China
文摘The effects of pre-aging treatments on subsequent artificial aging response were investigated by means of transmission electron microscopy observations and hardness test in age hardened Al-3.95Cu-(1.32Mg)-0.52Mn-0.11 Zr alloys. In Al-3.95Cu-0.52Mn-0.11 Zr alloy, when the pre-aging temperature is 25 °C, the pre-aging treatment has no evident effect on the peak hardness of subsequent artificial aging, while a positive effect(increase of peak hardness) appears when pre-aging temperature is50 °C. However, in Al-3.95Cu-1.32Mg-0.52Mn-0.11 Zr alloy, it is found that whether the pre-aging temperature is 25 °C or 50 °C,the peak artificial aging hardness is lower than that of T6 treated alloy, that is to say, pre-aging treatment has a negative effect on the peak hardness of subsequent artificial aging in the alloys.
基金Financial assistance from Defence Research Development Organization (DRDO)
文摘Superior properties of maraging steels make them suitable for the fabrication of components used for military applications like missile covering, rocket motor casing and ship hulls. Welding is the main process for fabrication of these components, while the maraging steels can be fusion welded using gas tungsten arc welding(GTAW) process. All these fabricated components require longer storage life and a major problem in welds is susceptible to stress corrosion cracking(SCC). The present study is aimed at studying the SCC behaviour of MDN 250(18% Ni) steel and its welds with respect to microstructural changes. In the present study, 5.2 mm thick sheets made of MDN 250 steel in the solution annealed condition was welded using GTAW process. Post-weld heat treatments of direct ageing(480 C for 3 h), solutionizing(815 C for 1 h) followed by ageing and homogenizing(1150 C for 1 h) followed by ageing were carried out. A mixture of martensite and austenite was observed in the microstructure of the fusion zone of solutionized and direct aged welds and only martensite in as-welded condition. Homogenization and ageing treatment have eliminated reverted austenite and elemental segregation. Homogenized welds also exhibited a marginal improvement in the corrosion resistance compared to those in the as-welded, solutionized and aged condition. Constant load SCC test data clearly revealed that the failure time of homogenized weld is much longer compared to other post weld treatments, and the homogenization treatment is recommended to improve the SCC life of GTA welds of MDN 250 Maraging steel.
基金Project(51871203)supported by the National Natural Science Foundation of ChinaProject(TZ2018006-0303-02)supported by the Science Challenge Project,ChinaProjects(2020ZDZX0017,2019YFG0217)supported by the Sichuan Science and Technology Program,China。
文摘V-5Cr-5Ti alloys have been fabricated using a laser melting deposition(LMD)additive manufacturing process,showing precipitates aggregated near the grain/dendrite boundaries.Since the mechanical properties of vanadium alloys considerably depend on the precipitates,solution and aging treatments have been applied to eliminating the aggregations of the precipitates.The results show that as the solution temperature increases from 800 to 1560℃,the densities and the lengths of the precipitates are reduced,while the widths of the precipitates are increased.When the solution temperature reaches 1560℃,most impurity elements diffuse into the matrix and form into a nearly uniform supersaturated solid solution.Aging treatments have been applied to the 1560℃solution treated samples.It shows that as the aging temperature increases from 800 to 1200℃,the precipitate length increases,and the shapes of precipitates change from near-spherical to lath-like.Compared to 800 and 1200℃,aging at 1000℃results in the highest precipitate density.Compared to the LMD and solution-treated samples,the aged samples have the highest micro-hardness,due to the precipitation strengthening.