LiMnOand LiNiAlyMnO（x= 0.50;y = 0.05-0.50） powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such...LiMnOand LiNiAlyMnO（x= 0.50;y = 0.05-0.50） powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such as thermo gravimetric analysis（TG/DTA）,X-ray diffraction（XRD）,Fourier transform infrared spectroscopy（FT-IR）,field-emission scanning electron microscopy（FESEM）,transmission electron microscopy（TEM） and electrochemical studies viz.,galvanostatic cycling properties,electrochemical impedance spectroscopy（EIS） and differential capacity curves（dQ/dE）.Finger print XRD patterns of LiMnOand LiNiAlMnOfortify the high degree of crystallinity with better phase purity.FESEM images of the undoped pristine spinel illustrate uniform spherical grains surface morphology with an average particle size of 0.5 μm while Ni doped particles depict the spherical grains growth（50nm） with ice-cube surface morphology.TEM images of the spinel LiMnOshows the uniform spherical morphology with particle size of（100 nm） while low level of Al-doping spinel（LiNio.5Alo.05Mn1.45O4） displaying cloudy particles with agglomerated particles of（50nm）.The LiMnOsamples calcined at 850℃ deliver the discharge capacity of 130 mAh/g in the first cycle corresponds to 94%coiumbic efficiency with capacity fade of 1.5 mAh/g/cycle over the investigated 10 cycles.Among all four dopant compositions investigated,LiNiAlMnOdelivers the maximum discharge capacity of 126 mAh/g during the first cycle and shows the stable cycling performance with low capacity fade of 1 mAh/g/cycle（capacity retention of 92%） over the investigated 10 cycles.Electrochemical impedance studies of spinel LiMnOand LiNiAlMnOdepict the high and low real polarization of 1562 and 1100 Ω.展开更多
Nano-sized trinitrotoluene(TNT) material restrained in silica gel has been prepared by using the sol-gel process to study the effect of varying porosity in gel on the sensitivity of TNT. The TNT content in the gel has...Nano-sized trinitrotoluene(TNT) material restrained in silica gel has been prepared by using the sol-gel process to study the effect of varying porosity in gel on the sensitivity of TNT. The TNT content in the gel has been varied from 60 to 90 wt %(at fixed acetone/tetramethoxysilane ratio of 50). Also, for a fixed TNT content of 75 wt %, the pore structure in the gel has been varied by changing the ratio of silica gel precursor to the solvent. The resultant TNT–silica gel composites have been characterized using scanning electron microscopy, thermal analysis, small angle X-ray scattering and surface area analysis techniques. Impact sensitivity studies were carried out using Fall Hammer Impact Test. The results showed that the sensitivity of nanostructured explosives prepared by sol-gel process can be tailored precisely by controlling the process parameters.展开更多
yb3＋/Dy3＋ co-doped A1203 nanopowders have been prepared by the non-aqueous sol-gel method and their up- conversion photoluminescence spectra are measured under excitation by a 980-nm semiconductor laser. The results...yb3＋/Dy3＋ co-doped A1203 nanopowders have been prepared by the non-aqueous sol-gel method and their up- conversion photoluminescence spectra are measured under excitation by a 980-nm semiconductor laser. The results show that there are comparatively abundant spectra of up-conversion emissions centered at 378, 408, 527 and 543, and 663 nm, corresponding to 4C9/2→ 6H13/2, 4C9/2→ 6Hll/2, 4115/2 → 6H13/2, and 4F9/2 →6Hll/2 transitions of Dy3＋, respectively. Two-photon and three-photon processes are involved in ultraviolet, violet, green, and red up-conversion emissions. The energy transition between Yb3＋ and Dy3＋ is discussed.展开更多
In this paper, M-type hexagonal barium ferrite powders are synthesized using the sol-gel method. A dried precursor heated in air is analyzed in the temperature range from 50 to 1200 ℃ using thermo-gravimetric analysi...In this paper, M-type hexagonal barium ferrite powders are synthesized using the sol-gel method. A dried precursor heated in air is analyzed in the temperature range from 50 to 1200 ℃ using thermo-gravimetric analysis and differential scanning calorimetry. The effects of the additives and the cacinating temperature on the magnetic properties are investigated, and the results show that single-phase barium ferrite powders can be formed. After heat-treating at 950 ℃ for 4h with 3 wt% additive, the coercivity and saturation magnetization are found to be 440 Oe and 57.9 emu/g, respectively.展开更多
Transparent zinc oxide（ZnO） thin films are fabricated by a simple sol-gel spin-coating technique on glass substrates with different solution concentrations（0.3-1.2 M） using zinc acetate dehydrate [Zn（CH_3COO）_2&...Transparent zinc oxide（ZnO） thin films are fabricated by a simple sol-gel spin-coating technique on glass substrates with different solution concentrations（0.3-1.2 M） using zinc acetate dehydrate [Zn（CH_3COO）_2·2H_2O] as precursor and isopropanol and monoethanolamine（MEA） as solvent and stabilizer, respectively. The molar ratio of zinc acetate dehydrate to MEA is 1.0. X-ray diffraction, ultraviolet-visible spectroscopy and photoluminescence spectroscopy are employed to investigate the effect of solution concentration on the structural and optical properties of the ZnO thin films. The obtained results of all thin films are discussed in detail and are compared with other experimental data.展开更多
The preparation of yttria-stabilised zirconia (YSZ) sol and the mechanismsof sol formation and sol-gel transition have been studied. The YSZ sol was prepared viacontrolled hydration of propanol zirconia alkoxide doped...The preparation of yttria-stabilised zirconia (YSZ) sol and the mechanismsof sol formation and sol-gel transition have been studied. The YSZ sol was prepared viacontrolled hydration of propanol zirconia alkoxide doped with yttrium nitrite. The sol formation process and gelling time are affected by many parameters such as water content,acetic acid content and the amount of propanol. The stability of the sol can be greatlyimproved by adding appropriate polymer.展开更多
基金support given under the "Brain Pool Program of the Korean Federation of Science and Technology Societies" (KOFST), Republic of South Koreasupported by the Human Resources Development Program (No. 20124010203270) of the Korea Institute of Energy Technology EvaluationPlanning (KETEP) grant funded by the Korea Government Ministry of Trade, Industry and Energy
文摘LiMnOand LiNiAlyMnO（x= 0.50;y = 0.05-0.50） powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such as thermo gravimetric analysis（TG/DTA）,X-ray diffraction（XRD）,Fourier transform infrared spectroscopy（FT-IR）,field-emission scanning electron microscopy（FESEM）,transmission electron microscopy（TEM） and electrochemical studies viz.,galvanostatic cycling properties,electrochemical impedance spectroscopy（EIS） and differential capacity curves（dQ/dE）.Finger print XRD patterns of LiMnOand LiNiAlMnOfortify the high degree of crystallinity with better phase purity.FESEM images of the undoped pristine spinel illustrate uniform spherical grains surface morphology with an average particle size of 0.5 μm while Ni doped particles depict the spherical grains growth（50nm） with ice-cube surface morphology.TEM images of the spinel LiMnOshows the uniform spherical morphology with particle size of（100 nm） while low level of Al-doping spinel（LiNio.5Alo.05Mn1.45O4） displaying cloudy particles with agglomerated particles of（50nm）.The LiMnOsamples calcined at 850℃ deliver the discharge capacity of 130 mAh/g in the first cycle corresponds to 94%coiumbic efficiency with capacity fade of 1.5 mAh/g/cycle over the investigated 10 cycles.Among all four dopant compositions investigated,LiNiAlMnOdelivers the maximum discharge capacity of 126 mAh/g during the first cycle and shows the stable cycling performance with low capacity fade of 1 mAh/g/cycle（capacity retention of 92%） over the investigated 10 cycles.Electrochemical impedance studies of spinel LiMnOand LiNiAlMnOdepict the high and low real polarization of 1562 and 1100 Ω.
文摘Nano-sized trinitrotoluene(TNT) material restrained in silica gel has been prepared by using the sol-gel process to study the effect of varying porosity in gel on the sensitivity of TNT. The TNT content in the gel has been varied from 60 to 90 wt %(at fixed acetone/tetramethoxysilane ratio of 50). Also, for a fixed TNT content of 75 wt %, the pore structure in the gel has been varied by changing the ratio of silica gel precursor to the solvent. The resultant TNT–silica gel composites have been characterized using scanning electron microscopy, thermal analysis, small angle X-ray scattering and surface area analysis techniques. Impact sensitivity studies were carried out using Fall Hammer Impact Test. The results showed that the sensitivity of nanostructured explosives prepared by sol-gel process can be tailored precisely by controlling the process parameters.
基金Project supported by the National Natural Science Foundation of China （Grant No. 11004092） and the Scientific Research Fund of Education Department of Liaoning Province, China （Grant No. 2009A417）.
文摘yb3＋/Dy3＋ co-doped A1203 nanopowders have been prepared by the non-aqueous sol-gel method and their up- conversion photoluminescence spectra are measured under excitation by a 980-nm semiconductor laser. The results show that there are comparatively abundant spectra of up-conversion emissions centered at 378, 408, 527 and 543, and 663 nm, corresponding to 4C9/2→ 6H13/2, 4C9/2→ 6Hll/2, 4115/2 → 6H13/2, and 4F9/2 →6Hll/2 transitions of Dy3＋, respectively. Two-photon and three-photon processes are involved in ultraviolet, violet, green, and red up-conversion emissions. The energy transition between Yb3＋ and Dy3＋ is discussed.
基金Project supported by the National Basic Research Program of China(Grant No.2007CB310407)the Science Fund for Creative Research Groups of the National Natural Science Foundation of China(Grant No.61021061)+1 种基金the National Natural Youth Fund of China(Grant No.61001025)National Programs for Science and Technology Development of Guangdong Province,China(Grant No.2010B090400314)
文摘In this paper, M-type hexagonal barium ferrite powders are synthesized using the sol-gel method. A dried precursor heated in air is analyzed in the temperature range from 50 to 1200 ℃ using thermo-gravimetric analysis and differential scanning calorimetry. The effects of the additives and the cacinating temperature on the magnetic properties are investigated, and the results show that single-phase barium ferrite powders can be formed. After heat-treating at 950 ℃ for 4h with 3 wt% additive, the coercivity and saturation magnetization are found to be 440 Oe and 57.9 emu/g, respectively.
文摘Transparent zinc oxide（ZnO） thin films are fabricated by a simple sol-gel spin-coating technique on glass substrates with different solution concentrations（0.3-1.2 M） using zinc acetate dehydrate [Zn（CH_3COO）_2·2H_2O] as precursor and isopropanol and monoethanolamine（MEA） as solvent and stabilizer, respectively. The molar ratio of zinc acetate dehydrate to MEA is 1.0. X-ray diffraction, ultraviolet-visible spectroscopy and photoluminescence spectroscopy are employed to investigate the effect of solution concentration on the structural and optical properties of the ZnO thin films. The obtained results of all thin films are discussed in detail and are compared with other experimental data.
文摘The preparation of yttria-stabilised zirconia (YSZ) sol and the mechanismsof sol formation and sol-gel transition have been studied. The YSZ sol was prepared viacontrolled hydration of propanol zirconia alkoxide doped with yttrium nitrite. The sol formation process and gelling time are affected by many parameters such as water content,acetic acid content and the amount of propanol. The stability of the sol can be greatlyimproved by adding appropriate polymer.