Mesoporous zirconium oxo phosphate-sulfate was synthesized by hydrothermal method with hexadecyltrithylammonium bromide(CTAB)as the template and with zirconium nitrate or zirconium oxychloride as zirconium source.The ...Mesoporous zirconium oxo phosphate-sulfate was synthesized by hydrothermal method with hexadecyltrithylammonium bromide(CTAB)as the template and with zirconium nitrate or zirconium oxychloride as zirconium source.The optimum two-stage process was established, ^(31)P MAS NMR showed that the states of phosphate species were changed with further postsynthesis treatment by sulfate acid. The transformations of the structures at different temperatures from room temperature to 1173 K were investigated by XRD. ...展开更多
The polyacrylamide(PAM)/α-zirconium phosphate(α-ZrP) nanocomposite was synthesized by in situ intercalative polymerization of acrylamide monomer with α-ZrP exfoliated by methylamine.Its structure and morphology wer...The polyacrylamide(PAM)/α-zirconium phosphate(α-ZrP) nanocomposite was synthesized by in situ intercalative polymerization of acrylamide monomer with α-ZrP exfoliated by methylamine.Its structure and morphology were characterized by X-ray diffraction(XRD) and transmission electron microscopy(TEM).The results demonstrated that the interlayer distance of α-ZrP was expanded effectively after the polymerization of acrylamide,even forming exfoliated nanocomposite.Both XRD and TEM image confirmed that the most of the layers of α-ZrP were dispersed well in the polymer matrix,and the PAM/α-ZrP intercalated nanocomposite with the d-spacing of about 1.5 nm can be obtained at a high loading of α-ZrP(mass fraction ≥10%).At the same time,some of the layers of α-ZrP were exfoliated and dispersed disorderly in the PMA matrix.展开更多
基金supported by the Knowledge Innovation Program of the Chinese Academy of Sciences (Grant: DICP K2000B3)
文摘Mesoporous zirconium oxo phosphate-sulfate was synthesized by hydrothermal method with hexadecyltrithylammonium bromide(CTAB)as the template and with zirconium nitrate or zirconium oxychloride as zirconium source.The optimum two-stage process was established, ^(31)P MAS NMR showed that the states of phosphate species were changed with further postsynthesis treatment by sulfate acid. The transformations of the structures at different temperatures from room temperature to 1173 K were investigated by XRD. ...
文摘The polyacrylamide(PAM)/α-zirconium phosphate(α-ZrP) nanocomposite was synthesized by in situ intercalative polymerization of acrylamide monomer with α-ZrP exfoliated by methylamine.Its structure and morphology were characterized by X-ray diffraction(XRD) and transmission electron microscopy(TEM).The results demonstrated that the interlayer distance of α-ZrP was expanded effectively after the polymerization of acrylamide,even forming exfoliated nanocomposite.Both XRD and TEM image confirmed that the most of the layers of α-ZrP were dispersed well in the polymer matrix,and the PAM/α-ZrP intercalated nanocomposite with the d-spacing of about 1.5 nm can be obtained at a high loading of α-ZrP(mass fraction ≥10%).At the same time,some of the layers of α-ZrP were exfoliated and dispersed disorderly in the PMA matrix.