Grainy electrolytic manganese dioxide was prepared by electrodeposition in a 0.9 mol/L MnSO4 and 2.5 mol/LH2SO4 solution. The structure, particle size and appearance of the grainy electrolytic manganese dioxide were d...Grainy electrolytic manganese dioxide was prepared by electrodeposition in a 0.9 mol/L MnSO4 and 2.5 mol/LH2SO4 solution. The structure, particle size and appearance of the grainy electrolytic manganese dioxide were determined by powder X-ray diffraction, laser particle size analysis and scanning electron micrographs measurements. Current density has important effects on cell voltage, anodic current efficiency and particle size of the grainy electrolytic manganese dioxide, and the optimum current density is 30 A/dm2. The grainy electrolytic manganese dioxide electrodeposited under the optimum conditions consists of γ-MnO2 with an orthorhombic lattice structure; the grainy electrolytic manganese dioxide has a spherical or sphere-like appearance and a narrow particle size distribution with an average particle diameter of 7.237 μm.展开更多
为解决MnO_(2)材料在水系锌离子电池(ZIBs)中存在的导电性差、材料利用率低等问题,以农业废弃物椰壳为原料,将低成本、来源丰富、绿色可再生的生物质资源引入到电极材料中,通过高温碳化得到导电性优异的椰壳碳,用水热法在椰壳碳表面生长...为解决MnO_(2)材料在水系锌离子电池(ZIBs)中存在的导电性差、材料利用率低等问题,以农业废弃物椰壳为原料,将低成本、来源丰富、绿色可再生的生物质资源引入到电极材料中,通过高温碳化得到导电性优异的椰壳碳,用水热法在椰壳碳表面生长MnO_(2)纳米粒子,获得椰壳碳@MnO_(2)复合纳米材料。借助扫描电子显微镜(SEM)、X射线衍射仪(XRD)、电化学技术等表征测试手段,分析该复合材料的形貌结构以及电化学性能。结果表明椰壳碳@MnO_(2)在100 mA g^(-1)的电流密度下,经过300次循环,比容量仍高达到344.6 mA h g^(-1),性能远高于商用MnO_(2)材料(64.3 mA h g^(-1));椰壳碳@MnO_(2)优异的导电性,纳米化的结构设计提高了材料利用率,减少了离子扩散路径,带来更快的离子扩散速率,提高了材料的倍率性能,具有良好的应用前景。展开更多
研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水...研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水溶液中,MnO_2电极因二价锌离子的嵌入-脱出,容量明显提升,但衰减严重。当溶液中同时含有Zn^(2+)、Mn^(2+)离子时,基于Mn^(2+)和Zn^(2+)离子之间的协同作用和Mn^(2+)离子氧化/还原反应过程的作用,有效抑制MnO_2颗粒的聚集和结构塌陷,削弱碱式硫酸锌杂质不利的影响,保持了锌离子在MnO_2电极中嵌入-脱出的高容量特性(200 m Ah?g^(-1),电流密度:100m A?g^(-1)),及良好的循环稳定性。展开更多
文摘Grainy electrolytic manganese dioxide was prepared by electrodeposition in a 0.9 mol/L MnSO4 and 2.5 mol/LH2SO4 solution. The structure, particle size and appearance of the grainy electrolytic manganese dioxide were determined by powder X-ray diffraction, laser particle size analysis and scanning electron micrographs measurements. Current density has important effects on cell voltage, anodic current efficiency and particle size of the grainy electrolytic manganese dioxide, and the optimum current density is 30 A/dm2. The grainy electrolytic manganese dioxide electrodeposited under the optimum conditions consists of γ-MnO2 with an orthorhombic lattice structure; the grainy electrolytic manganese dioxide has a spherical or sphere-like appearance and a narrow particle size distribution with an average particle diameter of 7.237 μm.
文摘为解决MnO_(2)材料在水系锌离子电池(ZIBs)中存在的导电性差、材料利用率低等问题,以农业废弃物椰壳为原料,将低成本、来源丰富、绿色可再生的生物质资源引入到电极材料中,通过高温碳化得到导电性优异的椰壳碳,用水热法在椰壳碳表面生长MnO_(2)纳米粒子,获得椰壳碳@MnO_(2)复合纳米材料。借助扫描电子显微镜(SEM)、X射线衍射仪(XRD)、电化学技术等表征测试手段,分析该复合材料的形貌结构以及电化学性能。结果表明椰壳碳@MnO_(2)在100 mA g^(-1)的电流密度下,经过300次循环,比容量仍高达到344.6 mA h g^(-1),性能远高于商用MnO_(2)材料(64.3 mA h g^(-1));椰壳碳@MnO_(2)优异的导电性,纳米化的结构设计提高了材料利用率,减少了离子扩散路径,带来更快的离子扩散速率,提高了材料的倍率性能,具有良好的应用前景。
文摘研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水溶液中,MnO_2电极因二价锌离子的嵌入-脱出,容量明显提升,但衰减严重。当溶液中同时含有Zn^(2+)、Mn^(2+)离子时,基于Mn^(2+)和Zn^(2+)离子之间的协同作用和Mn^(2+)离子氧化/还原反应过程的作用,有效抑制MnO_2颗粒的聚集和结构塌陷,削弱碱式硫酸锌杂质不利的影响,保持了锌离子在MnO_2电极中嵌入-脱出的高容量特性(200 m Ah?g^(-1),电流密度:100m A?g^(-1)),及良好的循环稳定性。