Two novel ashless additives - benzothiazole derivatives containing boron and chlorine, OBC and BBC, were synthesized. The tribological performances of OBC and BBC at different mass ratios as additives in rapeseed oil ...Two novel ashless additives - benzothiazole derivatives containing boron and chlorine, OBC and BBC, were synthesized. The tribological performances of OBC and BBC at different mass ratios as additives in rapeseed oil （RO） were examined on a four-ball machine. The worn surfaces of the lower steel balls lubricated by oil samples were analyzed by means of scanning electron microscopy （SEM）. The test results showed that OBC and BBC had good solubility in the base oil, and could effectively increase the load-carrying capacity of the base oil. The maximum non-seizure load of oil sample containing 1.5 m% BBC was 1117 N, which was 2.3 times as much as that of the base oil. Both OBC and BBC could improve the anti-wear and corrosion inhibiting performance and thermal stability of the base oil, whose initial decomposition temperatures was above 350 ~C. However, OBC and BBC at different concentrations could increase the friction coefficient of the base oil. The SEM morphology of steel balls lubricated by oil samples containing 1.5 m% additives seemed to be more uniform and smoother than that of the base oil, and the scars formed were very shallow.展开更多
By using PAO-10 as the base oil, the tribological behavior of 11 additives under high vacuum condition was evaluated. By adopting some surface analytical instruments, such as scanning electron microscopy(SEM), energy ...By using PAO-10 as the base oil, the tribological behavior of 11 additives under high vacuum condition was evaluated. By adopting some surface analytical instruments, such as scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS), the tribological mechanisms of these additives were studied. In air, O_2 can react with metal to form metal oxide that can protect the surfaces of rubbing pair during the tribological tests. According to the theory of the competitive adsorption, the function of some active elements is weakened. In a vacuum environment, the additives contributed more to the lubrication performance. The sulfur-containing additives could react with Fe to produce Fe Sx and "M—C" bonds("M" represents metal). They both had contributions to the lubrication. As for the phosphorus-containing additives, they only generated the phosphates during the tests. When the sulfur and phosphorus-containing additives were applied, the generated phosphates and Fe Sx had the primary contribution to the lubrication performance during the tests.展开更多
文摘Two novel ashless additives - benzothiazole derivatives containing boron and chlorine, OBC and BBC, were synthesized. The tribological performances of OBC and BBC at different mass ratios as additives in rapeseed oil （RO） were examined on a four-ball machine. The worn surfaces of the lower steel balls lubricated by oil samples were analyzed by means of scanning electron microscopy （SEM）. The test results showed that OBC and BBC had good solubility in the base oil, and could effectively increase the load-carrying capacity of the base oil. The maximum non-seizure load of oil sample containing 1.5 m% BBC was 1117 N, which was 2.3 times as much as that of the base oil. Both OBC and BBC could improve the anti-wear and corrosion inhibiting performance and thermal stability of the base oil, whose initial decomposition temperatures was above 350 ~C. However, OBC and BBC at different concentrations could increase the friction coefficient of the base oil. The SEM morphology of steel balls lubricated by oil samples containing 1.5 m% additives seemed to be more uniform and smoother than that of the base oil, and the scars formed were very shallow.
基金Financial support from the SINOPEC Research Program(No.ST13164-19]) is gratefully acknowledged
文摘By using PAO-10 as the base oil, the tribological behavior of 11 additives under high vacuum condition was evaluated. By adopting some surface analytical instruments, such as scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS), the tribological mechanisms of these additives were studied. In air, O_2 can react with metal to form metal oxide that can protect the surfaces of rubbing pair during the tribological tests. According to the theory of the competitive adsorption, the function of some active elements is weakened. In a vacuum environment, the additives contributed more to the lubrication performance. The sulfur-containing additives could react with Fe to produce Fe Sx and "M—C" bonds("M" represents metal). They both had contributions to the lubrication. As for the phosphorus-containing additives, they only generated the phosphates during the tests. When the sulfur and phosphorus-containing additives were applied, the generated phosphates and Fe Sx had the primary contribution to the lubrication performance during the tests.