The oxidation behaviors of Ni-16Cr-xAl （x=4.5%, 9.0%, mass fraction） superalloy foams in air at 1000℃ were investigated. The effects of AI content on the resistance to high temperature oxidation were examined. The ...The oxidation behaviors of Ni-16Cr-xAl （x=4.5%, 9.0%, mass fraction） superalloy foams in air at 1000℃ were investigated. The effects of AI content on the resistance to high temperature oxidation were examined. The oxidation mechanisms of the foams were discussed. The results show that the resistance to the oxidation of the Ni-16Cr-xA1 based alloy at 1 000 ℃ increases with the content of A1 increasing from 4.5% to 9.0%. Complex oxide products are formed on the surface of the superalloy foams after the oxidation. Cr203 and A1203 are the predominant oxides for the scales of the foams with 4.5% A1 and 9% A1, respectively. Excellent high temperature oxidation resistance and superior pore conformation stability for the Ni-16Cr-xA1 based superalloy foam with 9% A1 can be mainly attributed to the formation of relatively continuous and protective A1203 oxides on the surface of the foam.展开更多
基金Project (51134003) supported by the National Natural Science Foundation of China
文摘The oxidation behaviors of Ni-16Cr-xAl （x=4.5%, 9.0%, mass fraction） superalloy foams in air at 1000℃ were investigated. The effects of AI content on the resistance to high temperature oxidation were examined. The oxidation mechanisms of the foams were discussed. The results show that the resistance to the oxidation of the Ni-16Cr-xA1 based alloy at 1 000 ℃ increases with the content of A1 increasing from 4.5% to 9.0%. Complex oxide products are formed on the surface of the superalloy foams after the oxidation. Cr203 and A1203 are the predominant oxides for the scales of the foams with 4.5% A1 and 9% A1, respectively. Excellent high temperature oxidation resistance and superior pore conformation stability for the Ni-16Cr-xA1 based superalloy foam with 9% A1 can be mainly attributed to the formation of relatively continuous and protective A1203 oxides on the surface of the foam.