A series of glass are synthesized via a melt quenching technique based on the Li_(2)O-Ni O-P_(2)O_(5) system.The concentration of nickel oxide varies from 5%to 15%in molar fraction.XRD pattern verifies the amorphous n...A series of glass are synthesized via a melt quenching technique based on the Li_(2)O-Ni O-P_(2)O_(5) system.The concentration of nickel oxide varies from 5%to 15%in molar fraction.XRD pattern verifies the amorphous nature of prepared glass samples with 5%,and 10%nickel oxide in molar fraction.While Li_(3)P and Ni_(2)P_(4)O_(12)phases are precipitated with a high nickel content up to 15%in molar fraction.As nickel is substituted for lithium,a systematic increase in glass transition temperature(T_(g))and glass softening temperatures(T_(s))is observed.This is greatly related to the increased structure,coherence in the glass network.Structural investigation showed that Ni_(2+) spectra are present in both octahedral and tetrahedral sites.Physical properties such as glass density((2.38±0.1)-(2.46±0.1)g/cm^(3)),and molar volume((42.28±0.1)-(39.15±0.1)cm^(3)/mol)are examined.The NiO/Li_(2)O replacements led to a decrease in the dissolution rate of the resultant amorphous materials from 1.53×10^(-5)to 3.20×10^(-6)g/(cm^(2)·min).Thermal expansion coefficients CTE of the glasses are diverse from 157×10^(-7) to 96×10^(-7)℃^(-1) over the temperature range of 25-250℃.The prepared glasses are expected to be useful as a low-temperature sealing material.展开更多
The characteristics of a new Li-NiO cathode were investigated. The crystal structure of Li-NiO was explored by XRD. Electrochemical behaviors of Li-NiO composite cathode were revealed by impedance spectroscopy from 40...The characteristics of a new Li-NiO cathode were investigated. The crystal structure of Li-NiO was explored by XRD. Electrochemical behaviors of Li-NiO composite cathode were revealed by impedance spectroscopy from 400℃ to 650℃. The diameter of deformed arc increased with the decrease of temperature. Above the melting point of the eutectic salt in composite electrolyte, the Li-NiO curves are similar with two deformed semicircular arcs at high frequency which partially overlaps each other and corresponds...展开更多
文摘A series of glass are synthesized via a melt quenching technique based on the Li_(2)O-Ni O-P_(2)O_(5) system.The concentration of nickel oxide varies from 5%to 15%in molar fraction.XRD pattern verifies the amorphous nature of prepared glass samples with 5%,and 10%nickel oxide in molar fraction.While Li_(3)P and Ni_(2)P_(4)O_(12)phases are precipitated with a high nickel content up to 15%in molar fraction.As nickel is substituted for lithium,a systematic increase in glass transition temperature(T_(g))and glass softening temperatures(T_(s))is observed.This is greatly related to the increased structure,coherence in the glass network.Structural investigation showed that Ni_(2+) spectra are present in both octahedral and tetrahedral sites.Physical properties such as glass density((2.38±0.1)-(2.46±0.1)g/cm^(3)),and molar volume((42.28±0.1)-(39.15±0.1)cm^(3)/mol)are examined.The NiO/Li_(2)O replacements led to a decrease in the dissolution rate of the resultant amorphous materials from 1.53×10^(-5)to 3.20×10^(-6)g/(cm^(2)·min).Thermal expansion coefficients CTE of the glasses are diverse from 157×10^(-7) to 96×10^(-7)℃^(-1) over the temperature range of 25-250℃.The prepared glasses are expected to be useful as a low-temperature sealing material.
基金supported by China National Hydrogen Project (No. G2000026410, 2001AA515080)
文摘The characteristics of a new Li-NiO cathode were investigated. The crystal structure of Li-NiO was explored by XRD. Electrochemical behaviors of Li-NiO composite cathode were revealed by impedance spectroscopy from 400℃ to 650℃. The diameter of deformed arc increased with the decrease of temperature. Above the melting point of the eutectic salt in composite electrolyte, the Li-NiO curves are similar with two deformed semicircular arcs at high frequency which partially overlaps each other and corresponds...