The preparation process of electrically conductive filler for anisotropic conductive adhesive was performed and discussed.The spherical filler contains tri-layer structures: resin core,Ni-P intermediate coating layer,...The preparation process of electrically conductive filler for anisotropic conductive adhesive was performed and discussed.The spherical filler contains tri-layer structures: resin core,Ni-P intermediate coating layer,Au outer coating layer.The 4 μm resin spherical cores were synthesized by monodispersion polymerization method.Then they were contributed to electrical conductivity by electrolessly plating Ni-P layer and gold layer.These particles have good corrosion resistance,high stability,and enough mechanical strength.When mixed with thermosetting epoxy resin to produce anisotropic conductive adhesive(ACA),it can realize a good conductive bonding between bumps on dies and pads on substrates.This environmentally friendly conductive material offers numerous advantages over conventional solder technology and is an ideal substitute for the lead-contained solder in electronics packaging.展开更多
The viscoelastic properties of the suspension of monodisperse spherical silica produced by hydrolysis of tetraethoxysilane in alcohol solvent with ammonia as a catalyst in polyethylene glycol （PEG） were studied. The...The viscoelastic properties of the suspension of monodisperse spherical silica produced by hydrolysis of tetraethoxysilane in alcohol solvent with ammonia as a catalyst in polyethylene glycol （PEG） were studied. The results show that the SiO2/PEG suspension possesses the reversible shear thinning and shear thickening behaviors. In the shear thinning region, the loss modulus （G＂） almost remains unchanged, whereas the storage modulus （G＇） decreases. In the shear thickening region, G＂ and G＇ increase for the formation of the ＂clusters＂. The larger G＂ over G＇ in all the stress studied shows that the system mainly possesses the viscous property, and that the energy dissipated（Ed） is larger than that stored. Ed of this suspension is proportional to the maximum strain （Tmax） rising with the exponent of 1.92 under low shear stress; however, in the shear thickening region, Ed is proportional to γ max rising with the exponent of 5.00.展开更多
Monodispersed manganese ferrite （MnFe2O4） nanocrystals could be successfully synthesized in large quantities via a facile synthetic technique based on the pyrolysis of organometallic compound precursor, in which oct...Monodispersed manganese ferrite （MnFe2O4） nanocrystals could be successfully synthesized in large quantities via a facile synthetic technique based on the pyrolysis of organometallic compound precursor, in which octadecene was used as solvent, and oleic acid and oleylamine were used as capping ligands. MnFe204 nanocrystals were obtained with size in a tunable range of 4- 15 nm and their morphologies could be tuned from spherical to triangle-shaped by varying the surfactants. The phase structure, morphology, and size of the products were characterized in detail by X-ray diffraction （XRD） and transmission electron microscopy （TEM）. Magnetic properties of MnFe2O4 nanocrystals with different morphologies were measured using a superconducting quantum interference device （SQUID）. Both monodisperse MnFe204 nanocrystals with spherical and triangle-shapes are superparamagnetic at room temperature while ferromagnetic at 2 K. The pyrolysis method may provide an effective route to synthesize other spinel ferrites or metal oxides nanocrystals.展开更多
基金The National Natural Science Foundation of China(No.10474024)NSFC-RGC Joint Research Scheme(No.60318002)+1 种基金Youth Chenguang Project of Science and Technology of Wuhan City of China(No.20065004116-10)StateKey Lab.of Advanced Technology for Materials Synthesis and Processing(Wuhan University of Technology,No.WUT2004 M08)
文摘The preparation process of electrically conductive filler for anisotropic conductive adhesive was performed and discussed.The spherical filler contains tri-layer structures: resin core,Ni-P intermediate coating layer,Au outer coating layer.The 4 μm resin spherical cores were synthesized by monodispersion polymerization method.Then they were contributed to electrical conductivity by electrolessly plating Ni-P layer and gold layer.These particles have good corrosion resistance,high stability,and enough mechanical strength.When mixed with thermosetting epoxy resin to produce anisotropic conductive adhesive(ACA),it can realize a good conductive bonding between bumps on dies and pads on substrates.This environmentally friendly conductive material offers numerous advantages over conventional solder technology and is an ideal substitute for the lead-contained solder in electronics packaging.
基金Projects(50774096 50606017) supported by the National Natural Science Foundation of China
文摘The viscoelastic properties of the suspension of monodisperse spherical silica produced by hydrolysis of tetraethoxysilane in alcohol solvent with ammonia as a catalyst in polyethylene glycol （PEG） were studied. The results show that the SiO2/PEG suspension possesses the reversible shear thinning and shear thickening behaviors. In the shear thinning region, the loss modulus （G＂） almost remains unchanged, whereas the storage modulus （G＇） decreases. In the shear thickening region, G＂ and G＇ increase for the formation of the ＂clusters＂. The larger G＂ over G＇ in all the stress studied shows that the system mainly possesses the viscous property, and that the energy dissipated（Ed） is larger than that stored. Ed of this suspension is proportional to the maximum strain （Tmax） rising with the exponent of 1.92 under low shear stress; however, in the shear thickening region, Ed is proportional to γ max rising with the exponent of 5.00.
基金Project(2010QZZD008) supported by the Prospect Key Projects of Fundamental Research Funds for the Central UniversitiesProject(2007FJ3008) supported by the Hunan Provincial Key Science and Technology Program of China
文摘Monodispersed manganese ferrite （MnFe2O4） nanocrystals could be successfully synthesized in large quantities via a facile synthetic technique based on the pyrolysis of organometallic compound precursor, in which octadecene was used as solvent, and oleic acid and oleylamine were used as capping ligands. MnFe204 nanocrystals were obtained with size in a tunable range of 4- 15 nm and their morphologies could be tuned from spherical to triangle-shaped by varying the surfactants. The phase structure, morphology, and size of the products were characterized in detail by X-ray diffraction （XRD） and transmission electron microscopy （TEM）. Magnetic properties of MnFe2O4 nanocrystals with different morphologies were measured using a superconducting quantum interference device （SQUID）. Both monodisperse MnFe204 nanocrystals with spherical and triangle-shapes are superparamagnetic at room temperature while ferromagnetic at 2 K. The pyrolysis method may provide an effective route to synthesize other spinel ferrites or metal oxides nanocrystals.