Mesoporous cerium-zirconium mixed oxides were prepared by hydrothermal method using cetyl trimethyl ammonium bromide (CTAB) as template. The effects of amount of template, pH value of solution and hydrothermal tempera...Mesoporous cerium-zirconium mixed oxides were prepared by hydrothermal method using cetyl trimethyl ammonium bromide (CTAB) as template. The effects of amount of template, pH value of solution and hydrothermal temperature on mesostructure of samples were systematically investigated. The final products were characterized by XRD, TEM, FT-IR, and BET. The results indicate that all the cerium-zirconium mixed oxides present a meso-structure. At molar ratio of n(CTAB)/n((Ce)+(Zr))= 0.15, pH value of 9, and hydrothermal temperature of 120 ℃, the samples obtained possess a specific surface area of 207.9 m2/g with pore diameter of 3.70 nm and pore volume of 0.19 cm3/g.展开更多
Ammonium dinitramide(ADN)based liquid monopropellants have been identified as environmentally benign substitutes for hydrazine monopropellant.However,new catalysts are to be developed for making ADN monopropellants co...Ammonium dinitramide(ADN)based liquid monopropellants have been identified as environmentally benign substitutes for hydrazine monopropellant.However,new catalysts are to be developed for making ADN monopropellants cold-start capable.In the present study,performance of Co and Ba doped CuCr_2O_4 nanocatalysts prepared by hydrothermal method was evaluated on the decomposition of aqueous ADN solution and ADN liquid monopropellant(LMP103X).The catalysts were characterized by PXRD(Powder X-ray Diffraction),FTIR(Fourier Transform Infrared spectroscopy),SEM(Scanning Electron Microscopy),TEM(Transmission Electron Microscopy),EDS(Energy Dispersive X-ray Spectroscopy),and XPS(X-ray Photoelectron Spectroscopy).The nanosize was confirmed by SEM and TEM,while the nanoflake morphology was confirmed by the SEM analysis.Further,we obtained the elemental composition from the EDS analysis.We investigated the catalytic activity of the catalysts by thermogravimetric(TG)analysis and the developed catalysts lowered the decomposition temperature of ADN monopropellant by about 55℃.The XPS analysis confirmed the presence of metal ions with different chemical states.Apparently,increase in the surface area of the catalysts and the mixed active sites as well as the development of oxygen vacancy on the catalyst surface introduced by metal doping are influencing the decomposition temperature of ADN samples.展开更多
基金Project(CHCL0501) supported by Hubei Provincial Open Fund of Key Laboratory of Catalytic Material Science and Technology
文摘Mesoporous cerium-zirconium mixed oxides were prepared by hydrothermal method using cetyl trimethyl ammonium bromide (CTAB) as template. The effects of amount of template, pH value of solution and hydrothermal temperature on mesostructure of samples were systematically investigated. The final products were characterized by XRD, TEM, FT-IR, and BET. The results indicate that all the cerium-zirconium mixed oxides present a meso-structure. At molar ratio of n(CTAB)/n((Ce)+(Zr))= 0.15, pH value of 9, and hydrothermal temperature of 120 ℃, the samples obtained possess a specific surface area of 207.9 m2/g with pore diameter of 3.70 nm and pore volume of 0.19 cm3/g.
基金financial support by DST-SERB (Grant No.SRG/2021/001182)DRDO (Grant No.ARMREB/HEM/2021/241)is gratefully acknowledged。
文摘Ammonium dinitramide(ADN)based liquid monopropellants have been identified as environmentally benign substitutes for hydrazine monopropellant.However,new catalysts are to be developed for making ADN monopropellants cold-start capable.In the present study,performance of Co and Ba doped CuCr_2O_4 nanocatalysts prepared by hydrothermal method was evaluated on the decomposition of aqueous ADN solution and ADN liquid monopropellant(LMP103X).The catalysts were characterized by PXRD(Powder X-ray Diffraction),FTIR(Fourier Transform Infrared spectroscopy),SEM(Scanning Electron Microscopy),TEM(Transmission Electron Microscopy),EDS(Energy Dispersive X-ray Spectroscopy),and XPS(X-ray Photoelectron Spectroscopy).The nanosize was confirmed by SEM and TEM,while the nanoflake morphology was confirmed by the SEM analysis.Further,we obtained the elemental composition from the EDS analysis.We investigated the catalytic activity of the catalysts by thermogravimetric(TG)analysis and the developed catalysts lowered the decomposition temperature of ADN monopropellant by about 55℃.The XPS analysis confirmed the presence of metal ions with different chemical states.Apparently,increase in the surface area of the catalysts and the mixed active sites as well as the development of oxygen vacancy on the catalyst surface introduced by metal doping are influencing the decomposition temperature of ADN samples.