Single hit compression tests were performed at 1 223-1 473 K and strain rate of 0.1-10 s-1 to study hot deformation behavior and flow stress model of F40MnV steel. The dependence of the peak stress, initial stress, sa...Single hit compression tests were performed at 1 223-1 473 K and strain rate of 0.1-10 s-1 to study hot deformation behavior and flow stress model of F40MnV steel. The dependence of the peak stress, initial stress, saturation stress, steady state stress and peak stain on Zener-Hollomon parameter were obtained. The mathematical models of dynamic recrystallization fraction and grain size were also obtained. Based on the tested data, the flow stress model of F40MnV steel was established in dynamic recovery region and dynamic recrystallization region, respectively. The results show that the activation energy for dynamic recrystallization is 278.6 kJ/mol by regression analysis. The flow stress model of F40MnV steel is proved to approximate the tested data and suitable for numerical simulation of hot forging.展开更多
基于热锻条件,使用销-盘摩擦设备对6061热锻铝合金和H13钢基自润滑模具材料进行了高温对磨实验,通过电子探针和能谱仪分析了不同工况下工件和模具的磨损机理。结果表明,随着载荷的增加,工件和模具之间的摩擦因数与磨损率先降低后升高;...基于热锻条件,使用销-盘摩擦设备对6061热锻铝合金和H13钢基自润滑模具材料进行了高温对磨实验,通过电子探针和能谱仪分析了不同工况下工件和模具的磨损机理。结果表明,随着载荷的增加,工件和模具之间的摩擦因数与磨损率先降低后升高;随着转速的增加,工件和模具之间的摩擦因数增大,磨损率呈倍数增加;当载荷为12 N、转速为100 r·min^(-1)时,工件和模具之间的摩擦因数最小,其值为0.416,磨损率仅为24.591 mm 3·N^(-1)·m^(-1);随着转速和载荷的增加,工件和模具之间的粘着磨损加重并且逐渐出现磨粒磨损和氧化磨损。展开更多
基金Project (50275094) supported by the National Natural Science Foundation of China
文摘Single hit compression tests were performed at 1 223-1 473 K and strain rate of 0.1-10 s-1 to study hot deformation behavior and flow stress model of F40MnV steel. The dependence of the peak stress, initial stress, saturation stress, steady state stress and peak stain on Zener-Hollomon parameter were obtained. The mathematical models of dynamic recrystallization fraction and grain size were also obtained. Based on the tested data, the flow stress model of F40MnV steel was established in dynamic recovery region and dynamic recrystallization region, respectively. The results show that the activation energy for dynamic recrystallization is 278.6 kJ/mol by regression analysis. The flow stress model of F40MnV steel is proved to approximate the tested data and suitable for numerical simulation of hot forging.
文摘基于热锻条件,使用销-盘摩擦设备对6061热锻铝合金和H13钢基自润滑模具材料进行了高温对磨实验,通过电子探针和能谱仪分析了不同工况下工件和模具的磨损机理。结果表明,随着载荷的增加,工件和模具之间的摩擦因数与磨损率先降低后升高;随着转速的增加,工件和模具之间的摩擦因数增大,磨损率呈倍数增加;当载荷为12 N、转速为100 r·min^(-1)时,工件和模具之间的摩擦因数最小,其值为0.416,磨损率仅为24.591 mm 3·N^(-1)·m^(-1);随着转速和载荷的增加,工件和模具之间的粘着磨损加重并且逐渐出现磨粒磨损和氧化磨损。