Na0.44MnO2 nanorods have been prepared by a hydrothermal method.The experimental parameters have been systematically investigated and optimized.The results show that Na0.44MnO2 nanorods obtained via the hydrothermal t...Na0.44MnO2 nanorods have been prepared by a hydrothermal method.The experimental parameters have been systematically investigated and optimized.The results show that Na0.44MnO2 nanorods obtained via the hydrothermal treatment at 200℃for 16 h show the best electrochemical properties,which deliver the high initial discharge capacity of 110.7 mA·h/g at 50 mA/g in potential window 2.0-4.0 V.To further improve their electrochemical properties,a ball milling process with graphene has been carried out to obtain Na0.44MnO2/graphene composite.The initial discharge capacity of Na0.44MnO2/graphene composite is 106.9 mA·h/g at a current density of 50 mA/g.After 100 cycles,the residual discharge capacity is 91.8 mA·h/g and the capacity retention rate is 85.9%,which is much higher than that of pristine Na0.44MnO2 nanorods(74.7%)at the same condition.What is more,when the current density reaches 500 and 1000 mA/g,the corresponding discharge capacities of Na0.44MnO2/graphene composite are about 89 and 78 mA·h/g,respectively,indicating outstanding rate capability.展开更多
基金Project(51672234)supported by the National Natural Science Foundation of ChinaProject(1337304)supported by the Program for Innovative Research Cultivation Team in University,Ministry of Education,China
文摘Na0.44MnO2 nanorods have been prepared by a hydrothermal method.The experimental parameters have been systematically investigated and optimized.The results show that Na0.44MnO2 nanorods obtained via the hydrothermal treatment at 200℃for 16 h show the best electrochemical properties,which deliver the high initial discharge capacity of 110.7 mA·h/g at 50 mA/g in potential window 2.0-4.0 V.To further improve their electrochemical properties,a ball milling process with graphene has been carried out to obtain Na0.44MnO2/graphene composite.The initial discharge capacity of Na0.44MnO2/graphene composite is 106.9 mA·h/g at a current density of 50 mA/g.After 100 cycles,the residual discharge capacity is 91.8 mA·h/g and the capacity retention rate is 85.9%,which is much higher than that of pristine Na0.44MnO2 nanorods(74.7%)at the same condition.What is more,when the current density reaches 500 and 1000 mA/g,the corresponding discharge capacities of Na0.44MnO2/graphene composite are about 89 and 78 mA·h/g,respectively,indicating outstanding rate capability.