The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The...The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The results show that there is a nonlinear relationship between the ratio of Fe-Al compound at the interface and the interfacial shear strength. When the ratio of Fe-Al compound at the interface is smaller than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength increases gradually; when the ratio of Fe-Al compound at the interface is larger than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength decreases continuously; when the ratio of Fe-Al compound at the interface is 71.4%, the largest interfacial shear strength 70.2MPa is obtained.展开更多
Interfacial adhesion between carbon fibers(CF)and polyetherketoneketone(PEKK)is a key factor that affects the mechanical performances of their composites.It is therefore of great importance to impregnate the CF bundle...Interfacial adhesion between carbon fibers(CF)and polyetherketoneketone(PEKK)is a key factor that affects the mechanical performances of their composites.It is therefore of great importance to impregnate the CF bundles with PEKK as effi-ciently as possible.We report that PEKK with a good dispersion in a mixed solution of 4-chlorophenol and 1,2-dichloroethane can be introduced onto CF surfaces by solution impregnation and curing at 280,320,340 and 360℃.The excellent wettability or infiltra-tion of the PEKK solution guarantees a full covering and its tight binding to CFs,making it possible to evaluate the interfacial shear strength(IFSS)with the microdroplet method.The interior of the CF bundles is completely and uniformly filled with PEKK by solu-tion impregnation,leading to a high interlaminar shear strength(ILSS).The maximum IFSS and ILSS reached 107.8 and 99.3 MPa,respectively.Such superior shear properties are ascribed to the formation of amorphous PEKK in the small spaces between CFs.展开更多
文摘The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The results show that there is a nonlinear relationship between the ratio of Fe-Al compound at the interface and the interfacial shear strength. When the ratio of Fe-Al compound at the interface is smaller than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength increases gradually; when the ratio of Fe-Al compound at the interface is larger than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength decreases continuously; when the ratio of Fe-Al compound at the interface is 71.4%, the largest interfacial shear strength 70.2MPa is obtained.
文摘Interfacial adhesion between carbon fibers(CF)and polyetherketoneketone(PEKK)is a key factor that affects the mechanical performances of their composites.It is therefore of great importance to impregnate the CF bundles with PEKK as effi-ciently as possible.We report that PEKK with a good dispersion in a mixed solution of 4-chlorophenol and 1,2-dichloroethane can be introduced onto CF surfaces by solution impregnation and curing at 280,320,340 and 360℃.The excellent wettability or infiltra-tion of the PEKK solution guarantees a full covering and its tight binding to CFs,making it possible to evaluate the interfacial shear strength(IFSS)with the microdroplet method.The interior of the CF bundles is completely and uniformly filled with PEKK by solu-tion impregnation,leading to a high interlaminar shear strength(ILSS).The maximum IFSS and ILSS reached 107.8 and 99.3 MPa,respectively.Such superior shear properties are ascribed to the formation of amorphous PEKK in the small spaces between CFs.
