Kaolinite was hydrothermally synthesized from alumina gel and silicate by dissolving alumina gel in oxalic acid before it was mixed with silicate, effects of the amount of addition on the species of synthetic products...Kaolinite was hydrothermally synthesized from alumina gel and silicate by dissolving alumina gel in oxalic acid before it was mixed with silicate, effects of the amount of addition on the species of synthetic products were discussed. The reaction product was characterized by X ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that analcite is the only phase of the reaction solution without oxalic acid, the proportion of kaolinite in product increases with the amount of addition, and kaolinite is the main species when the molar ratio of oxalic acid to alumina reaches 0.6∶1.0. This is because oxalic acid addition is beneficial to the formation of kaolinite through changing the coordination number of aluminium from four to six, while the mixture of alumina gel, before it was dissolved in oxalic acid with silicate interfered with the crystallization of kaolinite.展开更多
Lanthanum titanate （La2/3 TiO3） powders were synthesized by hydrothermal method based on the reaction of TiO2, La（NO3）3 and KOH at 160℃ for 24 h followed by the treatment of acidification. The microstructure, mor...Lanthanum titanate （La2/3 TiO3） powders were synthesized by hydrothermal method based on the reaction of TiO2, La（NO3）3 and KOH at 160℃ for 24 h followed by the treatment of acidification. The microstructure, morphology and dielectric properties were investigated by using X-ray diffraction, scanning electron microscope, transmission electron microscope and impedance method. The results show that the La2/3TiO3 particles consist of nearly homogenous and lamellar grains. The particles can be sintered into porous ceramics above 1150℃. The dielectric properties of La2/3 TiO3 show that both the dielectric constant and the dielectric loss tangent decrease with the increase of frequency.展开更多
Currently,the carbothermal reduction-nitridation(CRN)process is the predominant method for preparing aluminum nitride(AlN)powder.Although AlN powder prepared by CRN process exhibits high purity and excellent sintering...Currently,the carbothermal reduction-nitridation(CRN)process is the predominant method for preparing aluminum nitride(AlN)powder.Although AlN powder prepared by CRN process exhibits high purity and excellent sintering activity,it also presents challenges such as the necessity for high reaction temperatures and difficulties in achieving uniform mixing of its raw materials.This study presents a comprehensive investigation into preparation process of AlN nanopowders using a combination of hydrothermal synthesis and CRN.In the hydrothermal reaction,a homogeneous composite precursor consisting of carbon and boehmite(γ-AlOOH)is synthesized at 200℃using aluminum nitrate as the aluminum source,sucrose as the carbon source,and urea as the precipitant.During the hydrothermal process,the precursor develops a core-shell structure,with boehmite tightly coated with carbon(γ-AlOOH@C)due to electrostatic attraction.Compared with conventional precursor,the hydrothermal hybrid offers many advantages,such as ultrafine particles,uniform particle size distribution,good dispersion,high reactivity,and environmental friendliness.The carbon shell enhances thermodynamic stability of γ-Al_(2)O_(3) compared to the corundum phase(α-Al_(2)O_(3))by preventing the loss of the surface area in alumina.This stability enables γ-Al_(2)O_(3) to maintain high reactivity during CRN process,which initiates at 1300℃,and concludes at 1400℃.The underlying mechanisms are substantiated through experiments and thermodynamic calculations.This research provides a robust theoretical and experimental foundation for the hydrothermal combined carbothermal preparation of non-oxide ceramic nanopowders.展开更多
Magnesium oxysulfate （MgSO4·5Mg（OH）2·2H2O） flake powders with an average diameter of 2 ~tm and a thickness of 0.052 μm were prepared using magnesium sulfate and sodium hydroxide as raw materials by hydr...Magnesium oxysulfate （MgSO4·5Mg（OH）2·2H2O） flake powders with an average diameter of 2 ~tm and a thickness of 0.052 μm were prepared using magnesium sulfate and sodium hydroxide as raw materials by hydrothermal synthesis process. The composition, morphology and structural features of the hydrothermal products were examined with X-ray powder diffraction （XRD）, scanning electron microscopy （SEM） and Fourier transform infrared spectroscopy （FTIR）. The experimental results indicate that in the conditions of n（NaOH）/n（MgSO4） of 1.25, the dosage of w（Na3PO4） crystal additives of 1.0% w（MgSO4）, stirring for 5 h at 180 ℃, the morphology of MgSO4·5Mg（OH）2·2H2O products is flaky and laminar, which is a kind of complex magnesium singlecrystal. The recycling of MgSO4 mother liquor was also investigated to make a full use of the materials and reduce disposal. The results prove that there is no adverse effect on the yield and purity of the products.展开更多
Nanometer Ni0.5Zn0.5Fe2O4 powders with spinel phase were prepared by the hydrothermal method using purified FeSO4 solution from sodium jarosite＇s slag as materials. The results show that the spinel phase of Ni0.5Zn0....Nanometer Ni0.5Zn0.5Fe2O4 powders with spinel phase were prepared by the hydrothermal method using purified FeSO4 solution from sodium jarosite＇s slag as materials. The results show that the spinel phase of Ni0.5Zn0.5Fe2O4 powders begins to form at a relatively low temperature （130 ℃） and a shorter holding time （1 h） when pH=8. The crystallization kinetics equation at 200℃ is ln[-ln（1-x）] =-0.78＋0.951n t. The growth activation energy of Ni0.5Zn0.5Fe2O4 grains is 41.6 kJ/moL in hydrothermal synthesis process. With the increase of sintering temperature, the density and diameter shrinkage of ferrite circulus increase, whereas its pores decrease. The results of magnetic measurements show that saturation magnetic flux density Bs increases and the coercivity Hc decreases with the increase of their sintering temperature. Magnetic parameters of all the investigated samples satisfy the character demand of high Bs, low Br and low Hc of soft magnetic ferrite materials.展开更多
In this paper,the synthesis of a novel polyoxovanadiumborate[Li(H2O)3]3[V12B18O48(OH)12(OH)]·(H2O)5by hydrothermal method.FTIR,2DFTIR and UV-Vis absorption spectroscopy were employed to explore the relationships ...In this paper,the synthesis of a novel polyoxovanadiumborate[Li(H2O)3]3[V12B18O48(OH)12(OH)]·(H2O)5by hydrothermal method.FTIR,2DFTIR and UV-Vis absorption spectroscopy were employed to explore the relationships between structure and properties of 3-D compound 1.展开更多
An aluminoborate,Na_(2.5)Rb[Al{B_(5)O_(10)}{B_(3)O_(5)}]·0.5NO_(3)·H_(2)O(1),was synthesized under hydrothermal condition,which was built by mixed oxoboron clusters and AlO_(4)tetrahedra.In the structure,the...An aluminoborate,Na_(2.5)Rb[Al{B_(5)O_(10)}{B_(3)O_(5)}]·0.5NO_(3)·H_(2)O(1),was synthesized under hydrothermal condition,which was built by mixed oxoboron clusters and AlO_(4)tetrahedra.In the structure,the[B_(5)O_(10)]^(5-)and[B_(3)O_(7)]^(5-)clusters are alternately connected to form 1D[B_(8)O_(15)]_(n)^(6n-)chains,which are further linked by AlO_(4)units to form a 2D monolayer with 7‑membered ring and 10‑membered ring windows.Two adjacent monolayers with opposite orientations further form a porous‑layered structure with six channels through B—O—Al bonds.Compound 1 was characterized by single crystal X‑ray diffraction,powder X‑ray diffraction(PXRD),IR spectroscopy,UV‑Vis diffuse reflection spectroscopy,and thermogravimetric analysis(TGA),respectively.UV‑Vis diffuse reflectance analysis indicates that compound 1 shows a wide transparency range with a short cutoff edge of 201 nm,suggesting it may have potential application in UV regions.CCDC:2383923.展开更多
文摘Kaolinite was hydrothermally synthesized from alumina gel and silicate by dissolving alumina gel in oxalic acid before it was mixed with silicate, effects of the amount of addition on the species of synthetic products were discussed. The reaction product was characterized by X ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that analcite is the only phase of the reaction solution without oxalic acid, the proportion of kaolinite in product increases with the amount of addition, and kaolinite is the main species when the molar ratio of oxalic acid to alumina reaches 0.6∶1.0. This is because oxalic acid addition is beneficial to the formation of kaolinite through changing the coordination number of aluminium from four to six, while the mixture of alumina gel, before it was dissolved in oxalic acid with silicate interfered with the crystallization of kaolinite.
文摘Lanthanum titanate （La2/3 TiO3） powders were synthesized by hydrothermal method based on the reaction of TiO2, La（NO3）3 and KOH at 160℃ for 24 h followed by the treatment of acidification. The microstructure, morphology and dielectric properties were investigated by using X-ray diffraction, scanning electron microscope, transmission electron microscope and impedance method. The results show that the La2/3TiO3 particles consist of nearly homogenous and lamellar grains. The particles can be sintered into porous ceramics above 1150℃. The dielectric properties of La2/3 TiO3 show that both the dielectric constant and the dielectric loss tangent decrease with the increase of frequency.
基金National Key Research and Development Program of China(2022YFB3708500,2023YFB3611000)Fujian Science&Technology Innovation Laboratory for Optoelectronic Information of China(2020ZZ109)。
文摘Currently,the carbothermal reduction-nitridation(CRN)process is the predominant method for preparing aluminum nitride(AlN)powder.Although AlN powder prepared by CRN process exhibits high purity and excellent sintering activity,it also presents challenges such as the necessity for high reaction temperatures and difficulties in achieving uniform mixing of its raw materials.This study presents a comprehensive investigation into preparation process of AlN nanopowders using a combination of hydrothermal synthesis and CRN.In the hydrothermal reaction,a homogeneous composite precursor consisting of carbon and boehmite(γ-AlOOH)is synthesized at 200℃using aluminum nitrate as the aluminum source,sucrose as the carbon source,and urea as the precipitant.During the hydrothermal process,the precursor develops a core-shell structure,with boehmite tightly coated with carbon(γ-AlOOH@C)due to electrostatic attraction.Compared with conventional precursor,the hydrothermal hybrid offers many advantages,such as ultrafine particles,uniform particle size distribution,good dispersion,high reactivity,and environmental friendliness.The carbon shell enhances thermodynamic stability of γ-Al_(2)O_(3) compared to the corundum phase(α-Al_(2)O_(3))by preventing the loss of the surface area in alumina.This stability enables γ-Al_(2)O_(3) to maintain high reactivity during CRN process,which initiates at 1300℃,and concludes at 1400℃.The underlying mechanisms are substantiated through experiments and thermodynamic calculations.This research provides a robust theoretical and experimental foundation for the hydrothermal combined carbothermal preparation of non-oxide ceramic nanopowders.
基金Project(50704036) supported by the National Natural Science Foundation of ChinaProject(08JJ3027) supported by the Natural Science Foundation of Hunan Province, China
文摘Magnesium oxysulfate （MgSO4·5Mg（OH）2·2H2O） flake powders with an average diameter of 2 ~tm and a thickness of 0.052 μm were prepared using magnesium sulfate and sodium hydroxide as raw materials by hydrothermal synthesis process. The composition, morphology and structural features of the hydrothermal products were examined with X-ray powder diffraction （XRD）, scanning electron microscopy （SEM） and Fourier transform infrared spectroscopy （FTIR）. The experimental results indicate that in the conditions of n（NaOH）/n（MgSO4） of 1.25, the dosage of w（Na3PO4） crystal additives of 1.0% w（MgSO4）, stirring for 5 h at 180 ℃, the morphology of MgSO4·5Mg（OH）2·2H2O products is flaky and laminar, which is a kind of complex magnesium singlecrystal. The recycling of MgSO4 mother liquor was also investigated to make a full use of the materials and reduce disposal. The results prove that there is no adverse effect on the yield and purity of the products.
基金Project(50204001) supported by the National Natural Science Foundation of China
文摘Nanometer Ni0.5Zn0.5Fe2O4 powders with spinel phase were prepared by the hydrothermal method using purified FeSO4 solution from sodium jarosite＇s slag as materials. The results show that the spinel phase of Ni0.5Zn0.5Fe2O4 powders begins to form at a relatively low temperature （130 ℃） and a shorter holding time （1 h） when pH=8. The crystallization kinetics equation at 200℃ is ln[-ln（1-x）] =-0.78＋0.951n t. The growth activation energy of Ni0.5Zn0.5Fe2O4 grains is 41.6 kJ/moL in hydrothermal synthesis process. With the increase of sintering temperature, the density and diameter shrinkage of ferrite circulus increase, whereas its pores decrease. The results of magnetic measurements show that saturation magnetic flux density Bs increases and the coercivity Hc decreases with the increase of their sintering temperature. Magnetic parameters of all the investigated samples satisfy the character demand of high Bs, low Br and low Hc of soft magnetic ferrite materials.
基金the NNSFC(21473030,1371033)Fujian Provincial Natural Science Foundation(2013J01042)the Open Fund of State Key Laboratory of Structural Chemistry(20130015)
文摘In this paper,the synthesis of a novel polyoxovanadiumborate[Li(H2O)3]3[V12B18O48(OH)12(OH)]·(H2O)5by hydrothermal method.FTIR,2DFTIR and UV-Vis absorption spectroscopy were employed to explore the relationships between structure and properties of 3-D compound 1.
文摘An aluminoborate,Na_(2.5)Rb[Al{B_(5)O_(10)}{B_(3)O_(5)}]·0.5NO_(3)·H_(2)O(1),was synthesized under hydrothermal condition,which was built by mixed oxoboron clusters and AlO_(4)tetrahedra.In the structure,the[B_(5)O_(10)]^(5-)and[B_(3)O_(7)]^(5-)clusters are alternately connected to form 1D[B_(8)O_(15)]_(n)^(6n-)chains,which are further linked by AlO_(4)units to form a 2D monolayer with 7‑membered ring and 10‑membered ring windows.Two adjacent monolayers with opposite orientations further form a porous‑layered structure with six channels through B—O—Al bonds.Compound 1 was characterized by single crystal X‑ray diffraction,powder X‑ray diffraction(PXRD),IR spectroscopy,UV‑Vis diffuse reflection spectroscopy,and thermogravimetric analysis(TGA),respectively.UV‑Vis diffuse reflectance analysis indicates that compound 1 shows a wide transparency range with a short cutoff edge of 201 nm,suggesting it may have potential application in UV regions.CCDC:2383923.