The aim of present study is to analyze the influence of volume percentage(vol.%) of nano-sized particles(TiB_2: average size is 35 nm) on microstructure, mechanical and tribological behavior of 6061-T6 Al alloy surfac...The aim of present study is to analyze the influence of volume percentage(vol.%) of nano-sized particles(TiB_2: average size is 35 nm) on microstructure, mechanical and tribological behavior of 6061-T6 Al alloy surface nano composite prepared via Friction stir process(FSP). The microstructure of the fabricated surface nanocomposites is examined using optical microscopy(OM) and scanning electron microscope(SEM) for distribution of TiB_2 nano reinforcement particles, thickness of nano composite layer formed on the Aluminum alloy substrate and fracture features. The depth of surface nano composite layer is measured as 3683.82 m m along the cross section of stir zone of nano composite perpendicular to FSP. It was observed that increase in volume percentage of TiB_2 particles, the microhardness is increased up to132 Hv and it is greater than as-received Al alloy's microhardness(104 Hv). It is also observed that at 4volume percentage higher tensile properties exhibited as compared with the 2 and 8 vol. %. It is found that high wear resistance exhibited at 4 volume percentage as-compared with the 2 and 8 vol. %. The observed wear and mechanical properties are interrelated with microstructure, fractography and worn morphology.展开更多
High strength-to-weight ratio of non-ferrous alloys, such as aluminium, magnesium and titanium alloys, are considered to be possible replacement of widely accepted steels in transportation and automobile sectors. Amon...High strength-to-weight ratio of non-ferrous alloys, such as aluminium, magnesium and titanium alloys, are considered to be possible replacement of widely accepted steels in transportation and automobile sectors. Among these alloys, magnesium is self explosive and titanium is costlier, and aluminium is most likely to replace steels. Application of aluminium or its alloys is also thought of as an appropriate replacement in defence field, especially to enhance the easiness in mobility of combat vehicles while maintaining the same standard as that of conventional armour grade steels. Hence most of the investigations have been confined to aluminium or its alloys as base material and open an era of developing the newer composite materials to address the major limitation, i.e. tribological properties. The surface composites can be fabricated by incorporating the ceramic carbides like silicon carbide, carbides of transition metals and oxides of aluminium using surface modification techniques, such as high energy laser melt treatment, high energy electron beam irradiation and thermal spray process which are based on fusion route. These techniques yield the fusion related problems, such as interfacial reaction, pin holes, shrinkage cavities or voids and other casting related defects, and pave the way to need of an efficient technique which must be based on solid state. Recently developed friction stir processing technique was used in the present investigation for surface modification of AA7075 aluminum alloy, which is an alternative to steels. In the present investigation, 160 μm sized boron carbide powder was procured and was reduced to 60 μm and 30 μm using high energy ball mill. Subsequently these powders were used to fabricate the surface composites using friction stir processing.Ballistic performance testing as per the military standard(JIS.0108.01) was carried out. In the present work, an analytical method of predicting the ballistic behavior of surface composites was developed. This method was based on energy balance, i.e., the initial energy of impact is same as that of energy absorbed by multi layers. An attempt also has been made to validate the analytical results with the experimental findings. Variation between the analytical and experimental results may be accounted due to the assumptions considering such as isotropic behavior of target and shearing area of contact as cylindrical instead of conical interface As the analytical model yields the ballistic performance in the closer proximity of experimentally obtained, it can be considered to be an approximation to evaluate the ballistic performance of targets.展开更多
Friction stir processing and post process artificial ageing was successfully carried out on AA7075 with and without reinforcement of SiC particles producing defect free processed zone with uniform distribution of fill...Friction stir processing and post process artificial ageing was successfully carried out on AA7075 with and without reinforcement of SiC particles producing defect free processed zone with uniform distribution of filler material.Effect of SiC particle reinforcement and artificial ageing times on the microstructural modifications was characterized using optical and electron microscopy,electron backscattered diffraction and X-Ray diffraction.Hardness,impact and wear tests were carried out to investigate mechanical behaviour before and after processing.Reinforcement of SiC particles during FSP and subsequent age hardening treatment brought about nearly twofold increase in hardness and impact toughness values by the combined effect of grain refinement,Zener pinning,dispersion strengthening and precipitation hardening.Significant improvement in wear resistance in terms of wear loss was also observed after processing compared to the reference material AA7075-T6.Fractured surface of post FSP age hardened AA7075 alloy exhibited features of ductile fracture during Charpy impact test.展开更多
Industrial applications of aluminium and its alloys are restricted because of their poor tribological properties. Thermal spraying, laser surfacing, electron beam welding are the most widely used techniques to alter t...Industrial applications of aluminium and its alloys are restricted because of their poor tribological properties. Thermal spraying, laser surfacing, electron beam welding are the most widely used techniques to alter the surface morphology of base metal. Preliminary studies reveal that the coating and layering of aluminium alloys with ceramic particles enhance the ballistic resistance. Furthermore, among aluminium alloys,7075 aluminium alloy exhibits high strength which can be compared to that of steels and has profound applications in the designing of lightweight fortification structures and integrated protection systems. Having limitations such as poor bond integrity, formation of detrimental phases and interfacial reaction between reinforcement and substrate using fusion route to deposit hard particles paves the way to adopt friction stir processing for fabricating surface composites using different sizes of boron carbide particles as reinforcement on armour grade 7075 aluminium alloy as matrix in the present investigation. Wear and ballistic tests were carried out to assess the performance of friction stir processed AA7075 alloy. Significant improvement in wear resistance of friction stir processed surface composites is attributed to the change in wear mechanism from abrasion to adhesion. It has also been observed that the surface metal matrix composites have shown better ballistic resistance compared to the substrate AA7075 alloy. Addition of solid lubricant Mo S2 has reduced the depth of penetration of the projectile to half that of base metal AA7075 alloy. For the first time, the friction stir processing technique was successfully used to improve the wear and ballistic resistances of armour grade high strength AA7075 alloy.展开更多
The present work aims to enhance the ballistic resistance of AA7005 alloy by incorporating the TiB2 and B4C ceramic reinforcement particles. Surface composites with different weight fractions of TiB2 and B4C particles...The present work aims to enhance the ballistic resistance of AA7005 alloy by incorporating the TiB2 and B4C ceramic reinforcement particles. Surface composites with different weight fractions of TiB2 and B4C particles were processed by friction stir processing. Micro-hardness and depth of penetration tests were carried out to evaluate the ballistic properties of the surface composites. The surface hardness of the composite was found to be nearly 70 HV higher than base alloy. The depth of penetration of the steel projectile was 20e26mm in the composites as compared to 37mm in the base alloy. Ballistic mass efficiency factor of the surface composite was found to be 1.6 times higher than base alloy. This is mainly attributed to the dispersion strengthening from the reinforcement particles.展开更多
The influence of three factors, such as volume percentage of reinforcement particles(i.e. Al2O3), tool tilt angle and concave angle of shoulder, on the mechanical properties of Cue Al2O3 surface composites fabricated ...The influence of three factors, such as volume percentage of reinforcement particles(i.e. Al2O3), tool tilt angle and concave angle of shoulder, on the mechanical properties of Cue Al2O3 surface composites fabricated via friction stir processing was studied. Taguchi method was used to optimize these factors for maximizing the mechanical properties of surface composites. The fabricated surface composites were examined by optical microscope for dispersion of reinforcement particles. It was found that Al2O3 particles are uniformly dispersed in the stir zone. The tensile properties of the surface composites increased with the increase in the volume percentage of the Al2O3 reinforcement particles.This is due to the addition of the reinforcement particles which increases the temperature of recrystallization by pinning the grain boundaries of the copper matrix and blocking the movement of the dislocations. The observed mechanical properties are correlated with microstructure and fracture features.展开更多
The surface of copper-chromium alloy was processed by Al-Si-Ni multi-permeation and friction stir processing,and the microstructure and mechanical properties of the surface layer were tested by scanning electron micro...The surface of copper-chromium alloy was processed by Al-Si-Ni multi-permeation and friction stir processing,and the microstructure and mechanical properties of the surface layer were tested by scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS),microhardness tester and friction testing machine.The results show that Al,Si and Ni elements are fully permeated into the surface of copper-chromium alloy after multielement co-infiltration and friction stir processing.In the observation of the microstructures,we found that the reticular structure is fragmented and distributed in the stir zone region.Microstructure becomes finer and grains refinement.The micro hardness of the copper-chromium alloy increased to 129 HV,44.9%higher than that of the original matrix.The main reasons of microhardness enhancement are solid solution strengthening,fine grains strengthening and dispersion strengthening.The friction test results show that the friction coefficient is basically stable at 0.69 and the wear mass is only 0.0017 g after 10 min of friction test.The improvement of wear resistance was attributed to the increase of microhardness of the alloy surface.展开更多
Aluminium matrix surface composites are gaining alluring role especially in aerospace, defence, and marine industries. Friction stir processing(FSP) is a promising novel solid state technique for surface composites fa...Aluminium matrix surface composites are gaining alluring role especially in aerospace, defence, and marine industries. Friction stir processing(FSP) is a promising novel solid state technique for surface composites fabrication. In this study, AA6061/SiC surface composites were fabricated and the effect of tool plunge depth on pattern of reinforcement particles dispersion in metal matrix was investigated. Six varying tool plunge depths were chosen at constant levels of shoulder diameter and tool tilt angle to observe the exclusive effect of plunge variation. Process parameters chosen for the experimentation are speed of rotation, travel speed and tool tilt angle which were taken as 1400 rpm, 40 mm/min, and 2.5 °respectively. Macro and the microstructural study were performed using stereo zoom and optical microscope respectively. Results reflected that lower plunge depth levels lead to insufficient heat generation and cavity formation towards the stir zone center. On the other hand, higher levels of plunge depth result in ejection of reinforcement particles and even sticking of material to tool shoulder. Thus, an optimal plunge depth is needed in developing defect free surface composites.展开更多
The heat treatable aluminum-copper alloy AA2014 finds wide application in the aerospace and defence industry due to its high strength-toweight ratio and good ductility. Friction stir welding(FSW) process, an emerging ...The heat treatable aluminum-copper alloy AA2014 finds wide application in the aerospace and defence industry due to its high strength-toweight ratio and good ductility. Friction stir welding(FSW) process, an emerging solid state joining process, is suitable for joining this alloy compared to fusion welding processes. This work presents the formulation of a mathematical model with process parameters and tool geometry to predict the responses of friction stir welds of AA 2014-T6 aluminum alloy, viz yield strength, tensile strength and ductility. The most influential process parameters considered are spindle speed, welding speed, tilt angle and tool pin profile. A four-factor, five-level central composite design was used and a response surface methodology(RSM) was employed to develop the regression models to predict the responses.The mechanical properties, such as yield strength(YS), ultimate tensile strength(UTS) and percentage elongation(%El), are considered as responses. Method of analysis of variance was used to determine the important process parameters that affect the responses. Validation trials were carried out to validate these results. These results indicate that the friction stir welds of AA 2014-T6 aluminum alloy welded with hexagonal tool pin profile have the highest tensile strength and elongation, whereas the joints fabricated with conical tool pin profile have the lowest tensile strength and elongation.展开更多
Good castability and high strength properties of Ale Si alloys are useful in defence applications like torpedoes,manufacture of Missile bodies,and parts of automobile such as engine cylinders and pistons.Poor wear res...Good castability and high strength properties of Ale Si alloys are useful in defence applications like torpedoes,manufacture of Missile bodies,and parts of automobile such as engine cylinders and pistons.Poor wear resistance of the alloys is major limitation for their use.Friction stir processing(FSP) is a recognized surfacing technique as it overcomes the problems of fusion route surface modification methods.Keeping in view of the requirement of improving wear resistance of cast aluminiumesilicon alloy,friction stir processing was attempted for surface modification with boron carbide(B4C) and molybdenum disulfide(Mo S2) powders.Metallography,micro compositional analysis,hardness and pin-on-disc wear testing were used for characterizing the surface composite coating.Microscopic study revealed breaking of coarse silicon needles and uniformly distributed carbides in the A356 alloy matrix after FSP.Improvement and uniformity in hardness was obtained in surface composite layer.Higher wear resistance was achieved in friction stir processed coating with carbide powders.Addition of solid lubricant Mo S2 powder was found to improve wear resistance of the base metal significantly.展开更多
文摘The aim of present study is to analyze the influence of volume percentage(vol.%) of nano-sized particles(TiB_2: average size is 35 nm) on microstructure, mechanical and tribological behavior of 6061-T6 Al alloy surface nano composite prepared via Friction stir process(FSP). The microstructure of the fabricated surface nanocomposites is examined using optical microscopy(OM) and scanning electron microscope(SEM) for distribution of TiB_2 nano reinforcement particles, thickness of nano composite layer formed on the Aluminum alloy substrate and fracture features. The depth of surface nano composite layer is measured as 3683.82 m m along the cross section of stir zone of nano composite perpendicular to FSP. It was observed that increase in volume percentage of TiB_2 particles, the microhardness is increased up to132 Hv and it is greater than as-received Al alloy's microhardness(104 Hv). It is also observed that at 4volume percentage higher tensile properties exhibited as compared with the 2 and 8 vol. %. It is found that high wear resistance exhibited at 4 volume percentage as-compared with the 2 and 8 vol. %. The observed wear and mechanical properties are interrelated with microstructure, fractography and worn morphology.
基金Financial assistance from Armament research board,New Delhi,India
文摘High strength-to-weight ratio of non-ferrous alloys, such as aluminium, magnesium and titanium alloys, are considered to be possible replacement of widely accepted steels in transportation and automobile sectors. Among these alloys, magnesium is self explosive and titanium is costlier, and aluminium is most likely to replace steels. Application of aluminium or its alloys is also thought of as an appropriate replacement in defence field, especially to enhance the easiness in mobility of combat vehicles while maintaining the same standard as that of conventional armour grade steels. Hence most of the investigations have been confined to aluminium or its alloys as base material and open an era of developing the newer composite materials to address the major limitation, i.e. tribological properties. The surface composites can be fabricated by incorporating the ceramic carbides like silicon carbide, carbides of transition metals and oxides of aluminium using surface modification techniques, such as high energy laser melt treatment, high energy electron beam irradiation and thermal spray process which are based on fusion route. These techniques yield the fusion related problems, such as interfacial reaction, pin holes, shrinkage cavities or voids and other casting related defects, and pave the way to need of an efficient technique which must be based on solid state. Recently developed friction stir processing technique was used in the present investigation for surface modification of AA7075 aluminum alloy, which is an alternative to steels. In the present investigation, 160 μm sized boron carbide powder was procured and was reduced to 60 μm and 30 μm using high energy ball mill. Subsequently these powders were used to fabricate the surface composites using friction stir processing.Ballistic performance testing as per the military standard(JIS.0108.01) was carried out. In the present work, an analytical method of predicting the ballistic behavior of surface composites was developed. This method was based on energy balance, i.e., the initial energy of impact is same as that of energy absorbed by multi layers. An attempt also has been made to validate the analytical results with the experimental findings. Variation between the analytical and experimental results may be accounted due to the assumptions considering such as isotropic behavior of target and shearing area of contact as cylindrical instead of conical interface As the analytical model yields the ballistic performance in the closer proximity of experimentally obtained, it can be considered to be an approximation to evaluate the ballistic performance of targets.
基金The authors would like to acknowledge National Facility for Texture and OIM(A DST-IRPHA project),IIT Mumbai for XRD and EBSD measurements.One of the authors VDH would like to acknowledge Science and Engineering Research Board(SERB)for financial assistance(EEQ/2016/000422)to carry out project work.
文摘Friction stir processing and post process artificial ageing was successfully carried out on AA7075 with and without reinforcement of SiC particles producing defect free processed zone with uniform distribution of filler material.Effect of SiC particle reinforcement and artificial ageing times on the microstructural modifications was characterized using optical and electron microscopy,electron backscattered diffraction and X-Ray diffraction.Hardness,impact and wear tests were carried out to investigate mechanical behaviour before and after processing.Reinforcement of SiC particles during FSP and subsequent age hardening treatment brought about nearly twofold increase in hardness and impact toughness values by the combined effect of grain refinement,Zener pinning,dispersion strengthening and precipitation hardening.Significant improvement in wear resistance in terms of wear loss was also observed after processing compared to the reference material AA7075-T6.Fractured surface of post FSP age hardened AA7075 alloy exhibited features of ductile fracture during Charpy impact test.
基金Financial assistance from Armament Research Board, New Delhi, India
文摘Industrial applications of aluminium and its alloys are restricted because of their poor tribological properties. Thermal spraying, laser surfacing, electron beam welding are the most widely used techniques to alter the surface morphology of base metal. Preliminary studies reveal that the coating and layering of aluminium alloys with ceramic particles enhance the ballistic resistance. Furthermore, among aluminium alloys,7075 aluminium alloy exhibits high strength which can be compared to that of steels and has profound applications in the designing of lightweight fortification structures and integrated protection systems. Having limitations such as poor bond integrity, formation of detrimental phases and interfacial reaction between reinforcement and substrate using fusion route to deposit hard particles paves the way to adopt friction stir processing for fabricating surface composites using different sizes of boron carbide particles as reinforcement on armour grade 7075 aluminium alloy as matrix in the present investigation. Wear and ballistic tests were carried out to assess the performance of friction stir processed AA7075 alloy. Significant improvement in wear resistance of friction stir processed surface composites is attributed to the change in wear mechanism from abrasion to adhesion. It has also been observed that the surface metal matrix composites have shown better ballistic resistance compared to the substrate AA7075 alloy. Addition of solid lubricant Mo S2 has reduced the depth of penetration of the projectile to half that of base metal AA7075 alloy. For the first time, the friction stir processing technique was successfully used to improve the wear and ballistic resistances of armour grade high strength AA7075 alloy.
基金supported by Defence Institute of Advanced Technology(DIAT),Pune(DIAT-In house Project)
文摘The present work aims to enhance the ballistic resistance of AA7005 alloy by incorporating the TiB2 and B4C ceramic reinforcement particles. Surface composites with different weight fractions of TiB2 and B4C particles were processed by friction stir processing. Micro-hardness and depth of penetration tests were carried out to evaluate the ballistic properties of the surface composites. The surface hardness of the composite was found to be nearly 70 HV higher than base alloy. The depth of penetration of the steel projectile was 20e26mm in the composites as compared to 37mm in the base alloy. Ballistic mass efficiency factor of the surface composite was found to be 1.6 times higher than base alloy. This is mainly attributed to the dispersion strengthening from the reinforcement particles.
文摘The influence of three factors, such as volume percentage of reinforcement particles(i.e. Al2O3), tool tilt angle and concave angle of shoulder, on the mechanical properties of Cue Al2O3 surface composites fabricated via friction stir processing was studied. Taguchi method was used to optimize these factors for maximizing the mechanical properties of surface composites. The fabricated surface composites were examined by optical microscope for dispersion of reinforcement particles. It was found that Al2O3 particles are uniformly dispersed in the stir zone. The tensile properties of the surface composites increased with the increase in the volume percentage of the Al2O3 reinforcement particles.This is due to the addition of the reinforcement particles which increases the temperature of recrystallization by pinning the grain boundaries of the copper matrix and blocking the movement of the dislocations. The observed mechanical properties are correlated with microstructure and fracture features.
基金financial support from the National Natural Science Foundation of China (No. 51571214)Science Project of Shenzhen (JCYJ20180508151903646)
文摘The surface of copper-chromium alloy was processed by Al-Si-Ni multi-permeation and friction stir processing,and the microstructure and mechanical properties of the surface layer were tested by scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS),microhardness tester and friction testing machine.The results show that Al,Si and Ni elements are fully permeated into the surface of copper-chromium alloy after multielement co-infiltration and friction stir processing.In the observation of the microstructures,we found that the reticular structure is fragmented and distributed in the stir zone region.Microstructure becomes finer and grains refinement.The micro hardness of the copper-chromium alloy increased to 129 HV,44.9%higher than that of the original matrix.The main reasons of microhardness enhancement are solid solution strengthening,fine grains strengthening and dispersion strengthening.The friction test results show that the friction coefficient is basically stable at 0.69 and the wear mass is only 0.0017 g after 10 min of friction test.The improvement of wear resistance was attributed to the increase of microhardness of the alloy surface.
基金the University Grants Commission (UGC) for its financial assistance (vide sanction order No. F.3-40/2012 (SAP-II) under its SAP (DRS-I) sanctioned to the Department of Mechanical Engineering for the project entitled Friction Stir Welding, Ultrasonic Machining
文摘Aluminium matrix surface composites are gaining alluring role especially in aerospace, defence, and marine industries. Friction stir processing(FSP) is a promising novel solid state technique for surface composites fabrication. In this study, AA6061/SiC surface composites were fabricated and the effect of tool plunge depth on pattern of reinforcement particles dispersion in metal matrix was investigated. Six varying tool plunge depths were chosen at constant levels of shoulder diameter and tool tilt angle to observe the exclusive effect of plunge variation. Process parameters chosen for the experimentation are speed of rotation, travel speed and tool tilt angle which were taken as 1400 rpm, 40 mm/min, and 2.5 °respectively. Macro and the microstructural study were performed using stereo zoom and optical microscope respectively. Results reflected that lower plunge depth levels lead to insufficient heat generation and cavity formation towards the stir zone center. On the other hand, higher levels of plunge depth result in ejection of reinforcement particles and even sticking of material to tool shoulder. Thus, an optimal plunge depth is needed in developing defect free surface composites.
基金Financial assistance from Defence Research and Development Organization(DRDO)
文摘The heat treatable aluminum-copper alloy AA2014 finds wide application in the aerospace and defence industry due to its high strength-toweight ratio and good ductility. Friction stir welding(FSW) process, an emerging solid state joining process, is suitable for joining this alloy compared to fusion welding processes. This work presents the formulation of a mathematical model with process parameters and tool geometry to predict the responses of friction stir welds of AA 2014-T6 aluminum alloy, viz yield strength, tensile strength and ductility. The most influential process parameters considered are spindle speed, welding speed, tilt angle and tool pin profile. A four-factor, five-level central composite design was used and a response surface methodology(RSM) was employed to develop the regression models to predict the responses.The mechanical properties, such as yield strength(YS), ultimate tensile strength(UTS) and percentage elongation(%El), are considered as responses. Method of analysis of variance was used to determine the important process parameters that affect the responses. Validation trials were carried out to validate these results. These results indicate that the friction stir welds of AA 2014-T6 aluminum alloy welded with hexagonal tool pin profile have the highest tensile strength and elongation, whereas the joints fabricated with conical tool pin profile have the lowest tensile strength and elongation.
基金DRDO-ER&IPR (No:1104584\M\1387), New Delhi, India for the sponsoring the research project
文摘Good castability and high strength properties of Ale Si alloys are useful in defence applications like torpedoes,manufacture of Missile bodies,and parts of automobile such as engine cylinders and pistons.Poor wear resistance of the alloys is major limitation for their use.Friction stir processing(FSP) is a recognized surfacing technique as it overcomes the problems of fusion route surface modification methods.Keeping in view of the requirement of improving wear resistance of cast aluminiumesilicon alloy,friction stir processing was attempted for surface modification with boron carbide(B4C) and molybdenum disulfide(Mo S2) powders.Metallography,micro compositional analysis,hardness and pin-on-disc wear testing were used for characterizing the surface composite coating.Microscopic study revealed breaking of coarse silicon needles and uniformly distributed carbides in the A356 alloy matrix after FSP.Improvement and uniformity in hardness was obtained in surface composite layer.Higher wear resistance was achieved in friction stir processed coating with carbide powders.Addition of solid lubricant Mo S2 powder was found to improve wear resistance of the base metal significantly.