Cracks resulting from cyclic wetting and drying of expansive soils create discontinuities and anisotropy in the soil.The representative elementary volume(REV)defined by the continuous-media theory cannot be applied to...Cracks resulting from cyclic wetting and drying of expansive soils create discontinuities and anisotropy in the soil.The representative elementary volume(REV)defined by the continuous-media theory cannot be applied to cracked expansive soils that are considered discontinuous media.In this study,direct shear tests of three different scales(30 cm^(2),900 cm^(2),1963 cm^(2))and crack image analysis were carried out on undisturbed soil samples subjected to drying-wetting cycles in-situ.The REV size of expansive soil was investigated using the crack intensity factor(CIF)and soil cohesion.The results show that soil cohesion decreased with increasing sample area,and the development of secondary cracks further exacerbated the size effect of sample on cohesion of the soil.As shrinkage cracks developed,the REV size of the soil gradually increased and plateaued after 3−5 cycles.Under the same drying-wetting cycle conditions,the REV size determined using soil cohesion(REV-C)is 1.75 to 2.97 times the REV size determined using CIF(REV-CIF).Under the influence of shrinkage cracks,the average CIF is positively correlated with the REV size determined using different maximum permissible errors,with the coefficient of correlation greater than 0.9.A method for determining the REV-C based on crack image analysis is proposed,and the REV-C of expansive soil in the study area under different exposure times is given.展开更多
The damage process of concrete exposed to sodium sulfate attack and drying-wetting cycles was investigated. The water to binder(W/B) ratio and the concentration of sulfate solution were taken as variable parameters. T...The damage process of concrete exposed to sodium sulfate attack and drying-wetting cycles was investigated. The water to binder(W/B) ratio and the concentration of sulfate solution were taken as variable parameters. Through the experiment, visual change, relative dynamic modulus of elasticity(RDME) and the surface damage layer thickness of concrete were measured.Furthermore, SEM and thermal analysis were used to investigate the changing of microstructure and corrosion products of concrete.The test results show that the ultrasonic velocity is related to the damage layer of concrete. It approves that an increase in damage layer thickness reduces the compactness and the ultrasonic velocity. The deterioration degree of concrete could be estimated effectively by measuring the surface damage layer and the RDME of concrete. It is also found that the content of gypsum in concrete is less than that of ettringite in test, and some gypsum is checked only after a certain corrosion extent. When the concrete is with high W/B ratio or exposed to high concentration of sulfate solution, the content of ettringite first increases and then decreases with corrosion time. However, the content of gypsum increases at a steady rate. The content of corrosion products does not correspond well with the observations of RDME change, and extensive amount of corrosion products can be formed before obvious damage occurs.展开更多
基金Project(41472240)supported by the National Natural Science Foundation of ChinaProjects(2015B25514,2015B17214)supported by the Fundamental Research Funds for the Central Universities,China。
文摘Cracks resulting from cyclic wetting and drying of expansive soils create discontinuities and anisotropy in the soil.The representative elementary volume(REV)defined by the continuous-media theory cannot be applied to cracked expansive soils that are considered discontinuous media.In this study,direct shear tests of three different scales(30 cm^(2),900 cm^(2),1963 cm^(2))and crack image analysis were carried out on undisturbed soil samples subjected to drying-wetting cycles in-situ.The REV size of expansive soil was investigated using the crack intensity factor(CIF)and soil cohesion.The results show that soil cohesion decreased with increasing sample area,and the development of secondary cracks further exacerbated the size effect of sample on cohesion of the soil.As shrinkage cracks developed,the REV size of the soil gradually increased and plateaued after 3−5 cycles.Under the same drying-wetting cycle conditions,the REV size determined using soil cohesion(REV-C)is 1.75 to 2.97 times the REV size determined using CIF(REV-CIF).Under the influence of shrinkage cracks,the average CIF is positively correlated with the REV size determined using different maximum permissible errors,with the coefficient of correlation greater than 0.9.A method for determining the REV-C based on crack image analysis is proposed,and the REV-C of expansive soil in the study area under different exposure times is given.
基金Project(51278403)supported by the National Natural Science Foundation of China
文摘The damage process of concrete exposed to sodium sulfate attack and drying-wetting cycles was investigated. The water to binder(W/B) ratio and the concentration of sulfate solution were taken as variable parameters. Through the experiment, visual change, relative dynamic modulus of elasticity(RDME) and the surface damage layer thickness of concrete were measured.Furthermore, SEM and thermal analysis were used to investigate the changing of microstructure and corrosion products of concrete.The test results show that the ultrasonic velocity is related to the damage layer of concrete. It approves that an increase in damage layer thickness reduces the compactness and the ultrasonic velocity. The deterioration degree of concrete could be estimated effectively by measuring the surface damage layer and the RDME of concrete. It is also found that the content of gypsum in concrete is less than that of ettringite in test, and some gypsum is checked only after a certain corrosion extent. When the concrete is with high W/B ratio or exposed to high concentration of sulfate solution, the content of ettringite first increases and then decreases with corrosion time. However, the content of gypsum increases at a steady rate. The content of corrosion products does not correspond well with the observations of RDME change, and extensive amount of corrosion products can be formed before obvious damage occurs.