A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through ...A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through a facile solution casting approach. The simple, but effective monomer sulfonation was performed for SFMC to create compact and rigid hydrophobic backbone structures, while conventional random sulfonation was carried-out for SPEEK. Hydrophilic-hydrophobic-hydrophilic structure of SFMC enhances the compatibility with SPEEK and GO and allows for an unprecedented approach to alter me- chanical strength and proton conductivity of ternary hybrid membrane, as verified from universal test machine （UTM） curves and alternating current （AC） impedance plots. The impact of GO integration on the morphology and roughness of hybrid membrane was scrutinized using field emission scanning electron microscope （FE-SEM） and atomic force microscope （AFM）. Ternary hybrid showed uniform intercalation of GO nanosheets throughout the entire surface of membrane with an increased surface roughness of 8.91 nm. The constructed ternary hybrid membrane revealed excellent water absorption, ion exchange capacity and gas barrier properties, while retaining reasonable dimensional stability. The well-optimized ternary hybrid membrane containing 5 wt% GO revealed a maximum proton conductivity of 111.9 mS/cm, which is higher by a factor of two-fold with respect to that of bare SFMC membrane. The maximum PEMFC power density of 528.07mW/cm2 was yielded by ternary hybrid membrane at a load current density of 1321.1 mA/cm2 when operating the cell at 70 ℃ under 100% relative humidity （RH）. In comparison, a maximum power density of only 182.06 mW/cm2 was exhibited by the bare SFMC membrane at a load current density of 455.56 mA/cm2 under same operating conditions.展开更多
A kind of highly fluorinated bisphenol monomer was synthesized. It was characterized by FTIR, 1H NMR and MS. 6F PEEK and 6F PEEKK were prepared via aromatic nucleophilic substitution, based on [3,5 di(trifluoromethyl)...A kind of highly fluorinated bisphenol monomer was synthesized. It was characterized by FTIR, 1H NMR and MS. 6F PEEK and 6F PEEKK were prepared via aromatic nucleophilic substitution, based on [3,5 di(trifluoromethyl)] phenylhydroquinone and difluoro monomers. The T gs of 6F PEEK and 6F PEEKK are 423 and 436 K, respectively. The 6F polymers exhibit a high thermal stability and good solubility. The flexible, creasable and transparent thin films were easily obtained by compression moulding and solution casting.展开更多
The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The cros...The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The crosslinking behavior was studied by DSC. There is a remarkable increase of T g after crosslinking of the poly(aryl ethers). The T g values of crosslinked polymers were 437 and 446 K, respectively. The crosslinked polymers could not be soluble in common organic solvents, such as N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, chloroform, and tetrahydrofuran. The temperatures at a 5% mass loss of the crosslinked polymers in air were above 789 K. They showed a good optical property, too. This kind of polymers will be the promising materials used as the microelectronics and optical waveguide devices.展开更多
A kind of high Fluorine-containing poly(aryl ether) without side reaction was synthesized in a two-step synthesis. Its structure was confirmed by FTIR, 1H NMR and 19F NMR. The polymer shows an excellent thermal stabil...A kind of high Fluorine-containing poly(aryl ether) without side reaction was synthesized in a two-step synthesis. Its structure was confirmed by FTIR, 1H NMR and 19F NMR. The polymer shows an excellent thermal stability, good solubility, low water absorption, low dielectric constant and low refractive index. Flexible and transparant thin film can be easily obtained by compression moulding or solution casting. The polymer would be a promising material used for microelectronics and waveguide devices.展开更多
A novel bifluoro-monomer containing naphthalene moieties was synthesized and characterized by using FTIR, MS and NMR. Different poly(aryl ether ketone)s based on 1,4-bis(4,4′-fluorobenzoyl) naphthalene were prepared ...A novel bifluoro-monomer containing naphthalene moieties was synthesized and characterized by using FTIR, MS and NMR. Different poly(aryl ether ketone)s based on 1,4-bis(4,4′-fluorobenzoyl) naphthalene were prepared via aromatic nucleophilic substitution reaction. The polymers with a high molecular weight can be readily obtained due to the highly activity of the used monomer. 3F-PEEK-nK and 6F-PEEK-nK polymers were determined to exhibit good thermal stabilities with high T-g of 450 K and 457 K, respectively. Moreover, these polymers show a satisfactory solubility and can be cast into flexible and transparent films.展开更多
基金supported by the Korea Institute of Energy Technology Evaluation and Planning(KETEP)the Ministry of Trade,Industry&Energy(MOTIE)of the Republic of Korea(No.20164030201070)supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Science,ICT and future Planning(NRF-2017R1A2B4005230)
文摘A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through a facile solution casting approach. The simple, but effective monomer sulfonation was performed for SFMC to create compact and rigid hydrophobic backbone structures, while conventional random sulfonation was carried-out for SPEEK. Hydrophilic-hydrophobic-hydrophilic structure of SFMC enhances the compatibility with SPEEK and GO and allows for an unprecedented approach to alter me- chanical strength and proton conductivity of ternary hybrid membrane, as verified from universal test machine （UTM） curves and alternating current （AC） impedance plots. The impact of GO integration on the morphology and roughness of hybrid membrane was scrutinized using field emission scanning electron microscope （FE-SEM） and atomic force microscope （AFM）. Ternary hybrid showed uniform intercalation of GO nanosheets throughout the entire surface of membrane with an increased surface roughness of 8.91 nm. The constructed ternary hybrid membrane revealed excellent water absorption, ion exchange capacity and gas barrier properties, while retaining reasonable dimensional stability. The well-optimized ternary hybrid membrane containing 5 wt% GO revealed a maximum proton conductivity of 111.9 mS/cm, which is higher by a factor of two-fold with respect to that of bare SFMC membrane. The maximum PEMFC power density of 528.07mW/cm2 was yielded by ternary hybrid membrane at a load current density of 1321.1 mA/cm2 when operating the cell at 70 ℃ under 100% relative humidity （RH）. In comparison, a maximum power density of only 182.06 mW/cm2 was exhibited by the bare SFMC membrane at a load current density of 455.56 mA/cm2 under same operating conditions.
文摘A kind of highly fluorinated bisphenol monomer was synthesized. It was characterized by FTIR, 1H NMR and MS. 6F PEEK and 6F PEEKK were prepared via aromatic nucleophilic substitution, based on [3,5 di(trifluoromethyl)] phenylhydroquinone and difluoro monomers. The T gs of 6F PEEK and 6F PEEKK are 423 and 436 K, respectively. The 6F polymers exhibit a high thermal stability and good solubility. The flexible, creasable and transparent thin films were easily obtained by compression moulding and solution casting.
文摘The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The crosslinking behavior was studied by DSC. There is a remarkable increase of T g after crosslinking of the poly(aryl ethers). The T g values of crosslinked polymers were 437 and 446 K, respectively. The crosslinked polymers could not be soluble in common organic solvents, such as N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, chloroform, and tetrahydrofuran. The temperatures at a 5% mass loss of the crosslinked polymers in air were above 789 K. They showed a good optical property, too. This kind of polymers will be the promising materials used as the microelectronics and optical waveguide devices.
文摘A kind of high Fluorine-containing poly(aryl ether) without side reaction was synthesized in a two-step synthesis. Its structure was confirmed by FTIR, 1H NMR and 19F NMR. The polymer shows an excellent thermal stability, good solubility, low water absorption, low dielectric constant and low refractive index. Flexible and transparant thin film can be easily obtained by compression moulding or solution casting. The polymer would be a promising material used for microelectronics and waveguide devices.
文摘A novel bifluoro-monomer containing naphthalene moieties was synthesized and characterized by using FTIR, MS and NMR. Different poly(aryl ether ketone)s based on 1,4-bis(4,4′-fluorobenzoyl) naphthalene were prepared via aromatic nucleophilic substitution reaction. The polymers with a high molecular weight can be readily obtained due to the highly activity of the used monomer. 3F-PEEK-nK and 6F-PEEK-nK polymers were determined to exhibit good thermal stabilities with high T-g of 450 K and 457 K, respectively. Moreover, these polymers show a satisfactory solubility and can be cast into flexible and transparent films.