The wear failure course of gas-valve/valve-seat in engine was investigated with a simulating tester. The results show that the failure of the contact conical surface is mainly caused by the elastic and plastic deforma...The wear failure course of gas-valve/valve-seat in engine was investigated with a simulating tester. The results show that the failure of the contact conical surface is mainly caused by the elastic and plastic deformation and the fatigue micro-crack and spalling. The creep-deformation and corrosion atmosphere accelerated wear failure course at the high temperature. The wear failure course of the gas-valve/valve-seat in engine follows general wear rules of mechanical elements, but the rate of wear in the sharp wear stage is faster.展开更多
文摘The wear failure course of gas-valve/valve-seat in engine was investigated with a simulating tester. The results show that the failure of the contact conical surface is mainly caused by the elastic and plastic deformation and the fatigue micro-crack and spalling. The creep-deformation and corrosion atmosphere accelerated wear failure course at the high temperature. The wear failure course of the gas-valve/valve-seat in engine follows general wear rules of mechanical elements, but the rate of wear in the sharp wear stage is faster.