Wood has no inherent natural resistance against agents of biodegradation. We evaluated the effects of metal bath heat treatment(MBHT) on decay resistance and dimensional stability of Chinese parasol(Firmiana simplex) ...Wood has no inherent natural resistance against agents of biodegradation. We evaluated the effects of metal bath heat treatment(MBHT) on decay resistance and dimensional stability of Chinese parasol(Firmiana simplex) and Chinese fir(Cunninghamia lanceolata) wood. A low melting point alloy was used as heating medium in the treatment of the wood samples at 150, 180, and 210 °C for2, 4, and 8 h. Heat-treated and control samples were exposed to brown rot fungus(Poria placenta) and white rot fungus(Coriolus versicolor) for decay resistance testing and anti-swelling efficiency(ASE). The improved decay resistance with increase temperatures with low mass losses of 7.3 and 7.3% for F. simplex, and 3.9 and 3.6% for C.lanceolata at 210 °C for 8 h against Coriolus versicolor and Poria placenta, respectively. ASE indicated that MBHT contributed to improved dimensional stability of both wood species after treatment. Scanning electron micrograph results indicate that metal bath-treated samples showed strong decay resistance. Therefore, our approach to thermally modify wood should be explored to overcome the energy utilization by using low melting point alloy for the heat treatment of wood.展开更多
Natural durability of two plantation woods, Chinese fir and I-214 poplar, was investigated thoroughly by three test- ing methods, namely an accelerated laboratory decay test, a fungus cellar test and a field test. Af...Natural durability of two plantation woods, Chinese fir and I-214 poplar, was investigated thoroughly by three test- ing methods, namely an accelerated laboratory decay test, a fungus cellar test and a field test. After the decay test using Postia pla- centa and Trametes versicolor, Chinese fir and the I-214 poplar showed 34% and 69% of mass loss, respectively, indicating they should be classified as slightly durable and non-durable wood. This conclusion was confirmed by the fungus cellar test and the field test. Like the performance in the decay test, I-214 poplar showed no resistance to termites either in the laboratory or in the field, whereas Chinese fir would be classified as moderately resistant.展开更多
For overcoming disadvantages of wood, an esterification process was employed and tetrabromophthalic anhydride (TBPA) was used as a reactive chemical agent to prepare an esterified wood with the high dimensional stabil...For overcoming disadvantages of wood, an esterification process was employed and tetrabromophthalic anhydride (TBPA) was used as a reactive chemical agent to prepare an esterified wood with the high dimensional stability, flame resistance, and resistance to biodegradation from water-leaching. The experimental results indicated that esterification of wood plus maleic anhydride / tetrabromophthalic anhydride / glycerol could endow wood with dimensional stability, the antiswelling efficiency during water absorption (ASEw), reduction in water absorptivity (RWA), antiswelling efficiency during moisture absorption (ASEm), moisture excluding efficiency (MEE), and oxygen index (OI) of treated wood increased with an increase in the weight percent gain (WPG). And the treated wood showed great decay resistance and resistance to water leaching, too.展开更多
基金financially supported by the Special Scientific Research Fund for Public Service Sectors of Forestry(Grant No.201504603)Science and Technology Projects of Fujian Province(2014NZ003)the National Natural Science Foundation of China(Grant Nos.31370560,31170520)
文摘Wood has no inherent natural resistance against agents of biodegradation. We evaluated the effects of metal bath heat treatment(MBHT) on decay resistance and dimensional stability of Chinese parasol(Firmiana simplex) and Chinese fir(Cunninghamia lanceolata) wood. A low melting point alloy was used as heating medium in the treatment of the wood samples at 150, 180, and 210 °C for2, 4, and 8 h. Heat-treated and control samples were exposed to brown rot fungus(Poria placenta) and white rot fungus(Coriolus versicolor) for decay resistance testing and anti-swelling efficiency(ASE). The improved decay resistance with increase temperatures with low mass losses of 7.3 and 7.3% for F. simplex, and 3.9 and 3.6% for C.lanceolata at 210 °C for 8 h against Coriolus versicolor and Poria placenta, respectively. ASE indicated that MBHT contributed to improved dimensional stability of both wood species after treatment. Scanning electron micrograph results indicate that metal bath-treated samples showed strong decay resistance. Therefore, our approach to thermally modify wood should be explored to overcome the energy utilization by using low melting point alloy for the heat treatment of wood.
基金Supported by Sino-Japanese Technical Cooperation Project Titled "Studies on Chinese Plantation Wood" (JICA PROJECT/033-1418-E-O)
文摘Natural durability of two plantation woods, Chinese fir and I-214 poplar, was investigated thoroughly by three test- ing methods, namely an accelerated laboratory decay test, a fungus cellar test and a field test. After the decay test using Postia pla- centa and Trametes versicolor, Chinese fir and the I-214 poplar showed 34% and 69% of mass loss, respectively, indicating they should be classified as slightly durable and non-durable wood. This conclusion was confirmed by the fungus cellar test and the field test. Like the performance in the decay test, I-214 poplar showed no resistance to termites either in the laboratory or in the field, whereas Chinese fir would be classified as moderately resistant.
文摘For overcoming disadvantages of wood, an esterification process was employed and tetrabromophthalic anhydride (TBPA) was used as a reactive chemical agent to prepare an esterified wood with the high dimensional stability, flame resistance, and resistance to biodegradation from water-leaching. The experimental results indicated that esterification of wood plus maleic anhydride / tetrabromophthalic anhydride / glycerol could endow wood with dimensional stability, the antiswelling efficiency during water absorption (ASEw), reduction in water absorptivity (RWA), antiswelling efficiency during moisture absorption (ASEm), moisture excluding efficiency (MEE), and oxygen index (OI) of treated wood increased with an increase in the weight percent gain (WPG). And the treated wood showed great decay resistance and resistance to water leaching, too.