Using novolac phenolic resin, aniline and formaldehyde as raw materials, benzoxazine-phenolic copolymers with different percentages of benzoxazine rings were prepared. FT-IR was adopted to characterize the molecular s...Using novolac phenolic resin, aniline and formaldehyde as raw materials, benzoxazine-phenolic copolymers with different percentages of benzoxazine rings were prepared. FT-IR was adopted to characterize the molecular structure of the novolac-type phenolic resin and the benzoxazine-phenolic copolymer BP31. In order to understand the curing process of the copolymers, the curing behavior and curing kinetic characteristics were studied by differential scanning calorimetry （DSC）, and the catalytical effect of phenolic hydroxyl on the curing behavior of copolymers was investigated. To investigate the thermal properties of this resin, the thermal degradation behaviors of the cured samples were studied by thermal gravimetric （TG） method, and glass-transition temperatures （Tg） of the cured copolymers were also evaluated by DSC. The dynamic Ozawa method was adopted to determine the kinetic parameters of the curing process as well. The activation energy is 78.8 kJ/mol and the reaction rate constant is in the range from 40.0 to 5.2 （K/min）＂ according to reaction temperatures. The Ozawa exponent decreases from 2.4 to 0.7 with the increase of reaction temperature, and curing mechanism is expounded briefly according to the results. TG result shows that the highest char yield of copolymers is 50.3%. The highest Tg of copolymers is 489 K, which is much higher than that of pure benzoxazine resin.展开更多
In this manuscript,the neat epoxy(EP)and functionalized Fe_(3)O_(4)(G-Fe_(3)O_(4))reinforced epoxy(G-Fe_(3)O_(4)/EP)coatings were cured under different temperatures,and the effect of the low curing temperature on the ...In this manuscript,the neat epoxy(EP)and functionalized Fe_(3)O_(4)(G-Fe_(3)O_(4))reinforced epoxy(G-Fe_(3)O_(4)/EP)coatings were cured under different temperatures,and the effect of the low curing temperature on the anticorrosion performance was investigated.The experimental results show that the epoxy-amine ring-open addition reaction mainly exists in the curing process,and the activation energies of the reaction for the two coatings are 55.84 and 53.29 kJ/mol,respectively.For the coatings cured at the low temperature,almost no pores could be detected on the fracture surface,but the presentence of the rough regions reflects the poor curing state.As compared with the samples cured at the high temperature,the anticorrosion performance of the coatings with the low curing temperature is worse,and the decrease rate of the anticorrosion performance is slower,because of the poor curing state and low adhesion obtained at the low temperature.展开更多
基金Project (20050106) supported by the Key Science and Technology Item of Guangdong Province,China
文摘Using novolac phenolic resin, aniline and formaldehyde as raw materials, benzoxazine-phenolic copolymers with different percentages of benzoxazine rings were prepared. FT-IR was adopted to characterize the molecular structure of the novolac-type phenolic resin and the benzoxazine-phenolic copolymer BP31. In order to understand the curing process of the copolymers, the curing behavior and curing kinetic characteristics were studied by differential scanning calorimetry （DSC）, and the catalytical effect of phenolic hydroxyl on the curing behavior of copolymers was investigated. To investigate the thermal properties of this resin, the thermal degradation behaviors of the cured samples were studied by thermal gravimetric （TG） method, and glass-transition temperatures （Tg） of the cured copolymers were also evaluated by DSC. The dynamic Ozawa method was adopted to determine the kinetic parameters of the curing process as well. The activation energy is 78.8 kJ/mol and the reaction rate constant is in the range from 40.0 to 5.2 （K/min）＂ according to reaction temperatures. The Ozawa exponent decreases from 2.4 to 0.7 with the increase of reaction temperature, and curing mechanism is expounded briefly according to the results. TG result shows that the highest char yield of copolymers is 50.3%. The highest Tg of copolymers is 489 K, which is much higher than that of pure benzoxazine resin.
基金Project(U2106216)supported by the National Natural Science Foundation of China。
文摘In this manuscript,the neat epoxy(EP)and functionalized Fe_(3)O_(4)(G-Fe_(3)O_(4))reinforced epoxy(G-Fe_(3)O_(4)/EP)coatings were cured under different temperatures,and the effect of the low curing temperature on the anticorrosion performance was investigated.The experimental results show that the epoxy-amine ring-open addition reaction mainly exists in the curing process,and the activation energies of the reaction for the two coatings are 55.84 and 53.29 kJ/mol,respectively.For the coatings cured at the low temperature,almost no pores could be detected on the fracture surface,but the presentence of the rough regions reflects the poor curing state.As compared with the samples cured at the high temperature,the anticorrosion performance of the coatings with the low curing temperature is worse,and the decrease rate of the anticorrosion performance is slower,because of the poor curing state and low adhesion obtained at the low temperature.