The kinetic behavior of leaching copper from low grade copper oxide ore was investigated. The effects of leaching temperature, H2SO4 concentration, particle size of crude ore and agitation rate on the leaching efficie...The kinetic behavior of leaching copper from low grade copper oxide ore was investigated. The effects of leaching temperature, H2SO4 concentration, particle size of crude ore and agitation rate on the leaching efficiency of copper were also evaluated. And the kinetic equations of the leaching process were obtained. The results show that the leaching process can be described with a reaction model of shrinking core. The reaction can be divided into three stages. The first stage is the dissolution of free copper oxide and copper oxide wrapped by hematite-limonite ore. At this stage, the leaching efficiency is very fast （leaching efficiency is larger than 60%）. The second stage is the leaching of diffiuent copper oxides, whose apparent activation energy is 43.26 kJ/mol. During this process, the chemical reaction is the control step, and the reaction order of H2SO4 is 0.433 84. The third stage is the leaching of copper oxide wrapped by hematite-limonite and silicate ore with apparent activation energy of 16.08 kJ/mol, which belongs to the mixed control.展开更多
Several researches have been reported about the characteristic of β-Ga_2O_3 nanowires which was synthesized on nickel oxide particle.But indeed,recent researches about synthesis of β-Ga_2O_3 nanowires on oxide-assis...Several researches have been reported about the characteristic of β-Ga_2O_3 nanowires which was synthesized on nickel oxide particle.But indeed,recent researches about synthesis of β-Ga_2O_3 nanowires on oxide-assisted transition metal are limited to nickel or cobalt oxide catalyst.In this work,Gallium oxide(β-Ga_2O_3)nanowires were synthesized by a simple thermal evaporation method from gallium powder in the range of 700-1000℃ using the iron,nickel,copper,cobalt and zinc oxide as a catalyst,respectively.The β-Ga_2O_3 nanowires with single crystalline without defects were successfully synthesized at the reaction temperature of 850,900 and 950℃ in all the catalysts.But optimum experimental condition in synthesis of nanowires varied with the kind of catalyst.As increasing synthesis temperature,the morphology of gallium oxide nanowires changed from nanowires to nanorods,and its diameter increased.From these results,we could be proposed that the growth mechanism of β-Ga_2O_3 nanowires was changed with synthesis temperature of nanowires.Microstructure and morphology of Synthesized nanowire was characterized by HR-TEM,FE-SEM,EDX and XRD.展开更多
基金Project(2005BA639C) supported by the National Science and Technology Development of China
文摘The kinetic behavior of leaching copper from low grade copper oxide ore was investigated. The effects of leaching temperature, H2SO4 concentration, particle size of crude ore and agitation rate on the leaching efficiency of copper were also evaluated. And the kinetic equations of the leaching process were obtained. The results show that the leaching process can be described with a reaction model of shrinking core. The reaction can be divided into three stages. The first stage is the dissolution of free copper oxide and copper oxide wrapped by hematite-limonite ore. At this stage, the leaching efficiency is very fast （leaching efficiency is larger than 60%）. The second stage is the leaching of diffiuent copper oxides, whose apparent activation energy is 43.26 kJ/mol. During this process, the chemical reaction is the control step, and the reaction order of H2SO4 is 0.433 84. The third stage is the leaching of copper oxide wrapped by hematite-limonite and silicate ore with apparent activation energy of 16.08 kJ/mol, which belongs to the mixed control.
文摘Several researches have been reported about the characteristic of β-Ga_2O_3 nanowires which was synthesized on nickel oxide particle.But indeed,recent researches about synthesis of β-Ga_2O_3 nanowires on oxide-assisted transition metal are limited to nickel or cobalt oxide catalyst.In this work,Gallium oxide(β-Ga_2O_3)nanowires were synthesized by a simple thermal evaporation method from gallium powder in the range of 700-1000℃ using the iron,nickel,copper,cobalt and zinc oxide as a catalyst,respectively.The β-Ga_2O_3 nanowires with single crystalline without defects were successfully synthesized at the reaction temperature of 850,900 and 950℃ in all the catalysts.But optimum experimental condition in synthesis of nanowires varied with the kind of catalyst.As increasing synthesis temperature,the morphology of gallium oxide nanowires changed from nanowires to nanorods,and its diameter increased.From these results,we could be proposed that the growth mechanism of β-Ga_2O_3 nanowires was changed with synthesis temperature of nanowires.Microstructure and morphology of Synthesized nanowire was characterized by HR-TEM,FE-SEM,EDX and XRD.