The grafting polyacrylamide onto wood pulp cellulose (cell g PAM) was performed with cerous ammonium nitrate as the initiator and hydrolyzed to produce the super absorbent resin. The FTIR shows that the polyacrylami...The grafting polyacrylamide onto wood pulp cellulose (cell g PAM) was performed with cerous ammonium nitrate as the initiator and hydrolyzed to produce the super absorbent resin. The FTIR shows that the polyacrylamide is grafted on the cellulose. After hydrolyzation, part of acrylamino groups are transformed into carboxyl groups. The XRD analysis shows that the graft polymerization occurred at the amorphous section and the surface of the crystal section of cellulose. The SEM graph reveals that there is a layer of polymer on the surface of cellulose fiber and the fibril structure of the cellulose surface is covered. After hydrolyzation, the surface of the product is different from that of cell g PAM's and the surface is scraggy. The technical conditions to prepare high water absorbent resin were confirmed. Through the radical graft copolymerization, the high water absorbent resin can be produced from wood pulp cellulose.展开更多
The two kinds of super absorbent resins from carboxymethyl cellulose were synthesized with the potassium persulphate and methylenebisacrylamide as initiator and cross linker respectively by radical polymerization in a...The two kinds of super absorbent resins from carboxymethyl cellulose were synthesized with the potassium persulphate and methylenebisacrylamide as initiator and cross linker respectively by radical polymerization in aqueous solution. Thestructures of the two resins were characterized with Fourier transform infrared spectroscopy FTIR, scanning electron miscroscopy （SEM）, and environment scanning electron miscroscopy （ESEM）, the results indicate that the fibriform of the carboxymethyl cellulose （CMC） is disappeared and the crusslink networks in eopolymer of carboxymethyl cellulose-graft-polyacrylic acid（CMC-g-PAA） are denser than that of eopolymer of carboxymethyl cellulose-graft-poly （acrylic acid-co-N-vinyl Pyrrolidone） （CMC-g- PAA-co-PVP）. The comparison between the two resins in absorption capacities is that CMC-g-PAA is better in the water-keep capability being heated, while CMC-g-PAA-co-PVP is better in the water absorbency and salt resistance.展开更多
文摘The grafting polyacrylamide onto wood pulp cellulose (cell g PAM) was performed with cerous ammonium nitrate as the initiator and hydrolyzed to produce the super absorbent resin. The FTIR shows that the polyacrylamide is grafted on the cellulose. After hydrolyzation, part of acrylamino groups are transformed into carboxyl groups. The XRD analysis shows that the graft polymerization occurred at the amorphous section and the surface of the crystal section of cellulose. The SEM graph reveals that there is a layer of polymer on the surface of cellulose fiber and the fibril structure of the cellulose surface is covered. After hydrolyzation, the surface of the product is different from that of cell g PAM's and the surface is scraggy. The technical conditions to prepare high water absorbent resin were confirmed. Through the radical graft copolymerization, the high water absorbent resin can be produced from wood pulp cellulose.
基金Basic Research Foundation of Beijing Institute of Technology (BIT-UBF-200504E4202)
文摘The two kinds of super absorbent resins from carboxymethyl cellulose were synthesized with the potassium persulphate and methylenebisacrylamide as initiator and cross linker respectively by radical polymerization in aqueous solution. Thestructures of the two resins were characterized with Fourier transform infrared spectroscopy FTIR, scanning electron miscroscopy （SEM）, and environment scanning electron miscroscopy （ESEM）, the results indicate that the fibriform of the carboxymethyl cellulose （CMC） is disappeared and the crusslink networks in eopolymer of carboxymethyl cellulose-graft-polyacrylic acid（CMC-g-PAA） are denser than that of eopolymer of carboxymethyl cellulose-graft-poly （acrylic acid-co-N-vinyl Pyrrolidone） （CMC-g- PAA-co-PVP）. The comparison between the two resins in absorption capacities is that CMC-g-PAA is better in the water-keep capability being heated, while CMC-g-PAA-co-PVP is better in the water absorbency and salt resistance.