制备了NaYF_4∶Er^(3+),Yb^(3+)纳米晶,表征了纳米晶的形貌,通过物理掺杂的方式将纳米粒子掺杂到SU-8中作为光波导放大器的芯层材料,优化了波导放大器的尺寸,利用旋涂、刻蚀等工艺,在二氧化硅衬底上制备了光波导放大器。实验中用光漂白...制备了NaYF_4∶Er^(3+),Yb^(3+)纳米晶,表征了纳米晶的形貌,通过物理掺杂的方式将纳米粒子掺杂到SU-8中作为光波导放大器的芯层材料,优化了波导放大器的尺寸,利用旋涂、刻蚀等工艺,在二氧化硅衬底上制备了光波导放大器。实验中用光漂白法和湿法刻蚀两种方法制备光波导放大器,分别给出了两种方法制备的器件的结构、工艺流程、光场模拟结果,并对两种方法制备的器件的放大特性进行了测试。测试结果表明,当980 nm波长的泵浦光功率为241 m W且1 550 nm波长的信号光功率为0.1 m W时,使用湿法刻蚀法制备的放大器得到2.7 d B的相对增益。当980 nm波长的泵浦光功率为235 m W且1 550 nm波长的信号光功率为0.1 m W时,使用光漂白法制备的放大器得到4.5 d B的相对增益。根据以上测试结果,分析了两种工艺对器件性能的影响。展开更多
Yb^3＋：Er^3＋：Tm^3＋co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are meas...Yb^3＋：Er^3＋：Tm^3＋co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are measured, and the mechanisms of energy transfer among Yb^3＋ Er^3＋ and Tm^3＋ ions are discussed. The results show that there is an unexpected wavelength at 900-nm emission from Yb^3＋ Stark splitting levels to pump Tm^3＋ ions and there exists an optimum pump power. The concentration of the Tm^3＋ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the yb^3＋：Er^3＋：Tm^3＋ co-doped borosilicate glasses.展开更多
文摘制备了NaYF_4∶Er^(3+),Yb^(3+)纳米晶,表征了纳米晶的形貌,通过物理掺杂的方式将纳米粒子掺杂到SU-8中作为光波导放大器的芯层材料,优化了波导放大器的尺寸,利用旋涂、刻蚀等工艺,在二氧化硅衬底上制备了光波导放大器。实验中用光漂白法和湿法刻蚀两种方法制备光波导放大器,分别给出了两种方法制备的器件的结构、工艺流程、光场模拟结果,并对两种方法制备的器件的放大特性进行了测试。测试结果表明,当980 nm波长的泵浦光功率为241 m W且1 550 nm波长的信号光功率为0.1 m W时,使用湿法刻蚀法制备的放大器得到2.7 d B的相对增益。当980 nm波长的泵浦光功率为235 m W且1 550 nm波长的信号光功率为0.1 m W时,使用光漂白法制备的放大器得到4.5 d B的相对增益。根据以上测试结果,分析了两种工艺对器件性能的影响。
基金Project supported by the National Natural Science Foundation of China (Grant No. 10804015)the Science Foundation of the Education Department of Liaoning Province of China (Grant No. 2009A417)
文摘Yb^3＋：Er^3＋：Tm^3＋co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are measured, and the mechanisms of energy transfer among Yb^3＋ Er^3＋ and Tm^3＋ ions are discussed. The results show that there is an unexpected wavelength at 900-nm emission from Yb^3＋ Stark splitting levels to pump Tm^3＋ ions and there exists an optimum pump power. The concentration of the Tm^3＋ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the yb^3＋：Er^3＋：Tm^3＋ co-doped borosilicate glasses.