WC particles reinforced CoCrFeNiMo high-entropy alloy(HEA)composite coatings were prepared on Cr12MoV steel successfully by laser cladding technology to improve the wear resistance of substrates.Effect of WC content o...WC particles reinforced CoCrFeNiMo high-entropy alloy(HEA)composite coatings were prepared on Cr12MoV steel successfully by laser cladding technology to improve the wear resistance of substrates.Effect of WC content on microstructure and wear property of the composite coatings was studied in detail.Large numbers of carbides with four main types:primary carbide crystals,eutectic structures,massive crystals growing along the periphery of the remaining WC particles and incompletely fused WC particles,were found to exist in the WC/CoCrFeNiMo composite coatings.With increasing WC content,the microhardness of coatings is gradually improved while the average friction coefficients follow the opposite trend due to solid solution strengthening and second phase strengthening effect.The maximum microhardness and minimum friction coefficient are HV_(0.2)689.7 and 0.72,respectively,for the composite coating with 30 wt.%WC,the wear resistance of the substrate is improved significantly,the wear mechanisms are spalling wear and abrasive wear due to their high microhardness.展开更多
The intermediate layer was prepared by nickel doped with WC particles electroplating.The parameters,including current density and temperature,were studied.The measured methods,which consisted of surface roughometer an...The intermediate layer was prepared by nickel doped with WC particles electroplating.The parameters,including current density and temperature,were studied.The measured methods,which consisted of surface roughometer and SEM,were used to character the roughness and micrograph.Based on the results,it was shown that the optimized parameters of the composite were as follows,temperature 65 ℃,current density 5 A/dm2 and pH 6.5.In the range of optimized parameters,the roughness Ra was from 4.5 to 6.7 μm.From the SEM micrograph,the particles on the surface were well distributed.The nickel content,which affected the binding force,was determined by the electroplating time.展开更多
基金Project(2021YFC2801904)supported by the National Key R&D Program of ChinaProject(KY10100230067)supported by the Basic Product Innovation Research Project,China+3 种基金Projects(52271130,52305344)supported by the National Natural Science Foundation of ChinaProjects(ZR2020ME017,ZR2020QE186)supported by the Natural Science Foundation of Shandong Province,ChinaProjects(AMGM2024F11,AMGM2021F10,AMGM2023F06)supported by the Science Fund of Shandong Laboratory of Advanced Materials and Green Manufacturing at Yantai,ChinaProject(KY90200210015)supported by Leading Scientific Research Project of China National Nuclear Corporation(CNNC),China。
文摘WC particles reinforced CoCrFeNiMo high-entropy alloy(HEA)composite coatings were prepared on Cr12MoV steel successfully by laser cladding technology to improve the wear resistance of substrates.Effect of WC content on microstructure and wear property of the composite coatings was studied in detail.Large numbers of carbides with four main types:primary carbide crystals,eutectic structures,massive crystals growing along the periphery of the remaining WC particles and incompletely fused WC particles,were found to exist in the WC/CoCrFeNiMo composite coatings.With increasing WC content,the microhardness of coatings is gradually improved while the average friction coefficients follow the opposite trend due to solid solution strengthening and second phase strengthening effect.The maximum microhardness and minimum friction coefficient are HV_(0.2)689.7 and 0.72,respectively,for the composite coating with 30 wt.%WC,the wear resistance of the substrate is improved significantly,the wear mechanisms are spalling wear and abrasive wear due to their high microhardness.
文摘The intermediate layer was prepared by nickel doped with WC particles electroplating.The parameters,including current density and temperature,were studied.The measured methods,which consisted of surface roughometer and SEM,were used to character the roughness and micrograph.Based on the results,it was shown that the optimized parameters of the composite were as follows,temperature 65 ℃,current density 5 A/dm2 and pH 6.5.In the range of optimized parameters,the roughness Ra was from 4.5 to 6.7 μm.From the SEM micrograph,the particles on the surface were well distributed.The nickel content,which affected the binding force,was determined by the electroplating time.