The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1...The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1% of catalyst with the molar ration of xylol to styrene being 7.5:1,at temperature of 140℃ for 3 h;The yield of diphenylethylane under such conditions was about 97.5%.展开更多
A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
文摘The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1% of catalyst with the molar ration of xylol to styrene being 7.5:1,at temperature of 140℃ for 3 h;The yield of diphenylethylane under such conditions was about 97.5%.
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.