Because of an unfortunate mistake by authors,the Project(5227010679)of Foundation item was wrong.The corrected Project is shown as follows:Project(52271073).
A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energ...A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energy inside Al-core and promote rapid pyrolysis of ammonium perchlorate(AP)at a lower temperature in aluminized propellants.The microstructure of Al@Ni-P-Cu demonstrates that a three-layer Ni-P-Cu shell,with the thickness of~100 nm,is uniformly supported byμAl carrier(fuel unit),which has an amorphous surface with a thickness of~2.3 nm(catalytic unit).The peak temperature of AP with the addition of Al@Ni-P-Cu(3.5%)could significantly drop to 316.2℃ at high-temperature thermal decomposition,reduced by 124.3℃,in comparison to that of pure AP with 440.5℃.It illustrated that the introduction of Al@Ni-P-Cu could weaken or even eliminate the obstacle of AP pyrolysis due to its reduction of activation energy with 118.28 kJ/mol.The laser ignition results showed that the ignition delay time of Al@Ni-P-Cu/AP mixture with 78 ms in air is shorter than that of Al@Ni-P/AP(118 ms),decreased by 33.90%.Those astonishing breakthroughs were attributed to the synergistic effects of adequate active sites on amorphous surface and oxidation exothermic reactions(7597.7 J/g)of Al@Ni-P-Cu,resulting in accelerated mass and/or heat transfer rate to catalyze AP pyrolysis and combustion.Moreover,it is believed to provide an alternative Al-based combustion catalyst for propellant designer,to promote the development the propellants toward a higher energy.展开更多
Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc...Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.展开更多
The process of preparing anodic oxide film containing active sites and electroless nickel plating on highly active rare earth magnesium alloy was developed.The formation mechanism of electroless nickel plating on acti...The process of preparing anodic oxide film containing active sites and electroless nickel plating on highly active rare earth magnesium alloy was developed.The formation mechanism of electroless nickel plating on active anodic oxide film and the structure and properties of the composite coating were studied by several surface and electrochemical techniques.The results showed that Ag nanograins with an average size of 10 nm were embedded into the anodic oxide film with pores of 0.1−2μm.Ag nanoparticles provided a catalytic site for the deposition of Ni-B alloy,and the Ni crystal nucleus was first grown in horizontal mode and then in cylindrical mode.The corrosion potential of the composite coating increased by 1.37 V and the corrosion current reduced two orders of magnitude due to the subsequent deposition of Ni-P alloy.The high corrosion resistance was attributed to the misaligning of these micro defects in the three different layers and the amorphous structure of the Ni-P alloy in the outer layer.These findings provide a new idea for electroless nickel plating on anodic oxide film.展开更多
In order to improve the hot corrosion resistance of DZ125 alloy,Ce-Y modified aluminum coatings were prepared on DZ125 alloy by pack cementation process at 950°C for 2 h.The microstructure,phase constitution and ...In order to improve the hot corrosion resistance of DZ125 alloy,Ce-Y modified aluminum coatings were prepared on DZ125 alloy by pack cementation process at 950°C for 2 h.The microstructure,phase constitution and formation mechanism of the coatings were investigated.The hot corrosion behaviors of DZ125 alloy and the coatings in molten salt environment of 25%K2SO4+75%Na2SO4(mass fraction)at 900°C were studied.Results show that the obtained Al-Ce-Y coatings were mainly composed of Al3Ni2,Al3Ni and Cr7Ni3,with a thickness of about 120μm.After hot corrosion test,DZ125 alloy suffered catastrophic hot corrosion and serious internal oxidation and internal sulfidation arose.Two layers of corrosion products formed on surfaces of DZ125 alloy,including the outer layer consisting of Cr2O3 and NiCr2O4,and the inner layer of Al2O3,Ni3S2 and Ni-base solid solution.After being coated with Al-Ce-Y coating,the hot corrosion resistance of DZ125 alloy is improved notably,due to the formation of a dense scale mainly consisting of Al-rich Al2O3 in the coating layer.展开更多
The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray ...The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray technique. The relationship among the composition, structure and property of the coatings are investiga ted by means of optical microscope, scanning electronic microscope and the experiments of thermal shock resistance cycling and high temperature oxidation resistance. The results show that the structure design of introdu cing a transition layer between Ni alloy substrate and ZrO 2 ceramic coating guarantees the high quality and properties of the coatings; ZrO 2 coatings doped with a little SiO 2 possesses better thermal shock resistance and more excellent hot corrosion resistance as compared with ZrO 2 coating materials without SiO 2 ;the improvement in performance of ZrO 2 coating doped with SiO 2 is due to forming more dense coating structure by self closing effects of the flaws and pores in the ZrO 2 coatings.展开更多
Despite the great achievements made in improvement of wear resistance properties of aluminum alloys, their applications in heavy surface load-bearing are limited. Single coating is insufficient to produce the desired ...Despite the great achievements made in improvement of wear resistance properties of aluminum alloys, their applications in heavy surface load-bearing are limited. Single coating is insufficient to produce the desired combination of surface properties. These problems can be solved through the duplex coatings. The aim of the present study is to overview the research advances on processes of duplex coatings on (aluminum) alloys combined with micro plasma oxidation process and with other modern processes such as physical vapour deposition and plasma assisted chemical vapour deposition and also to evaluate the performance of micro plasma oxidation coatings in improving the load-bearing, friction and wear resistance properties of aluminum alloys in comparison with other coatings. Wherein, a more detailed presentation of the processes and their performances and disadvantages are given as well.展开更多
Ti-X-N (X=Al,Si or Al+Si) coatings were grown onto cemented carbide substrates by cathodic arc evaporation. The hardness of the coatings was obtained by nanoindentation and the microstructure was investigated by XRD,X...Ti-X-N (X=Al,Si or Al+Si) coatings were grown onto cemented carbide substrates by cathodic arc evaporation. The hardness of the coatings was obtained by nanoindentation and the microstructure was investigated by XRD,XPS and SEM. Solid solution hardening results in a hardness increase from 24 GPa for TiN to 31.2 GPa for TiAlN. The higher hardness values of 36.7 GPa for TiSiN and 42.4 GPa for TiAlSiN are obtained by the incorporation of Si into TiN (TiAlN) coatings due to the formation of special three-dimensional net structure consisting of nanocrystalline (nc) TiN (TiAlN) encapsulated in an amorphous (a) Si3N4 matrix phase. Furthermore,the nc-TiAlN/a-Si3N4 coating shows the best machining performance.展开更多
In order to obtain a high-performance surface on TiAl alloy that can meet the requirements in hot corrosion environment,Si-Al-Y coatings were fabricated by pack cementation process at 1050℃for 4 h.Corrosion behaviors...In order to obtain a high-performance surface on TiAl alloy that can meet the requirements in hot corrosion environment,Si-Al-Y coatings were fabricated by pack cementation process at 1050℃for 4 h.Corrosion behaviors of the TiAl alloy with and without Si-Al-Y coatings are compared to illustrate the factors and corresponding mechanism in molten salt environment of 25 wt%K2SO4 and 75 wt%Na2SO4 at 900°C.The obtained Si-Al-Y coating was mainly composed of a TiSi2 outer layer,a(Ti,X)5Si4 and(Ti,X)5Si3(X represents Nb or Cr element)middle layer,a TiAl2 inner layer and a Al-rich inter-diffusion zone.The inter-phase selective corrosion containing corrosion pits extending alongα2 phase from lamellar interfaces in hot corrosion tested TiAl alloy was observed.However,by being coated with Si-Al-Y coating,the hot corrosion performance of TiAl alloy was improved remarkably.展开更多
Functionalized implants demonstrate an upgraded approach in orthopedic implants,aiming to achieve long term success through improved bio integration.Bioceramic coatings with multifunctionality have arisen as an effect...Functionalized implants demonstrate an upgraded approach in orthopedic implants,aiming to achieve long term success through improved bio integration.Bioceramic coatings with multifunctionality have arisen as an effective substitute for conventional coatings,owing to their combination of various properties that are essential for bio-implants,such as osteointegration and antibacterial character.In the present study,thin hopeite coatings were produced by Pulsed laser deposition(PLD)and radio frequency magnetron sputtering(RFMS)on Ti64 substrates.The obtained hopeite coatings were annealed at 500°C in ambient air and studied in terms of surface morphology,phase composition,surface roughness,adhesion strength,antibacterial efficacy,apatite forming ability,and surface wettability by scanning electron microscope(SEM),X-ray diffraction(XRD),atomic force microscope(AFM),tensometer,fluorescence-activated cell sorting(FACS),simulated body fluid(SBF)immersion test and contact angle goniometer,respectively.Furthermore,based on promising results obtained in the present work it can be summarized that the new generation multifunctional hopeite coating synthesized by two alternative new process routes of PLD and RFMS on Ti64 substrates,provides effective alternatives to conventional coatings,largely attributed to strong osteointegration and antibacterial character of deposited hopeite coating ensuring the overall stability of metallic orthopedic implants.展开更多
Ni-Co-Fe2O3 composite coatings were electrodeposited using cetyltrimethylammonium bromide(CTAB)-modified Watt's nickel bath with Fe2O3 particles dispersed in it.The effects of the plating parameters on the chemica...Ni-Co-Fe2O3 composite coatings were electrodeposited using cetyltrimethylammonium bromide(CTAB)-modified Watt's nickel bath with Fe2O3 particles dispersed in it.The effects of the plating parameters on the chemical composition,structural and morphological characteristics of the electrodeposited Ni-Co-Fe2O3 composite coatings were investigated by energy dispersive X-ray(EDS) spectroscopy,X-ray diffractometry(XRD) and scanning electron microscopy(SEM).The results reveal that Fe2O3 particles can be codeposited in the Ni-Co matrix.The codeposition of Fe2O3 particles with Ni-Co is favoured at high Fe2O3 particle concentration and medium stirring,and the deposition of Co is favoured at high concentration of CTAB.Moreover,the study of the textural perfection of the deposits reveals that the presence of particles leads to the worsening of the quality of the observed <220> preferred orientation.Composites with high concentration of embedded particles exhibit a preferred crystal orientation of <111>.The more the embedded Fe2O3 particles in the metallic matrix,the smaller the sizes of the crystallite for the composite deposits.展开更多
文摘Because of an unfortunate mistake by authors,the Project(5227010679)of Foundation item was wrong.The corrected Project is shown as follows:Project(52271073).
基金supported by the National Natural Science Foundation of China,China(Grant Nos.U20B2018,U21B2086,11972087)。
文摘A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energy inside Al-core and promote rapid pyrolysis of ammonium perchlorate(AP)at a lower temperature in aluminized propellants.The microstructure of Al@Ni-P-Cu demonstrates that a three-layer Ni-P-Cu shell,with the thickness of~100 nm,is uniformly supported byμAl carrier(fuel unit),which has an amorphous surface with a thickness of~2.3 nm(catalytic unit).The peak temperature of AP with the addition of Al@Ni-P-Cu(3.5%)could significantly drop to 316.2℃ at high-temperature thermal decomposition,reduced by 124.3℃,in comparison to that of pure AP with 440.5℃.It illustrated that the introduction of Al@Ni-P-Cu could weaken or even eliminate the obstacle of AP pyrolysis due to its reduction of activation energy with 118.28 kJ/mol.The laser ignition results showed that the ignition delay time of Al@Ni-P-Cu/AP mixture with 78 ms in air is shorter than that of Al@Ni-P/AP(118 ms),decreased by 33.90%.Those astonishing breakthroughs were attributed to the synergistic effects of adequate active sites on amorphous surface and oxidation exothermic reactions(7597.7 J/g)of Al@Ni-P-Cu,resulting in accelerated mass and/or heat transfer rate to catalyze AP pyrolysis and combustion.Moreover,it is believed to provide an alternative Al-based combustion catalyst for propellant designer,to promote the development the propellants toward a higher energy.
基金Projects(41827805,41976044)supported by the National Natural Science Foundation of ChinaProject(ZDYF2021GXJS210)supported by the Hainan Provincial Science and Technology Special Fund,China+2 种基金Project(2021CXLH0005)supported by the Hainan Provincial Joint Project of Sanya Yazhou Bay Science and Technology City,ChinaProject(2021WHZZB2301)supported by the Wenhai Program of the S&T Fund of Shandong Province for Pilot National Laboratory for Marine Science and Technology,ChinaProject(121311KYSB20210005)supported by the Overseas Science and Education Centers of Bureau of International Cooperation Chinese Academy of Sciences。
文摘Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.
基金Project(5227010679)supported by the National Natural Science Foundation of China。
文摘The process of preparing anodic oxide film containing active sites and electroless nickel plating on highly active rare earth magnesium alloy was developed.The formation mechanism of electroless nickel plating on active anodic oxide film and the structure and properties of the composite coating were studied by several surface and electrochemical techniques.The results showed that Ag nanograins with an average size of 10 nm were embedded into the anodic oxide film with pores of 0.1−2μm.Ag nanoparticles provided a catalytic site for the deposition of Ni-B alloy,and the Ni crystal nucleus was first grown in horizontal mode and then in cylindrical mode.The corrosion potential of the composite coating increased by 1.37 V and the corrosion current reduced two orders of magnitude due to the subsequent deposition of Ni-P alloy.The high corrosion resistance was attributed to the misaligning of these micro defects in the three different layers and the amorphous structure of the Ni-P alloy in the outer layer.These findings provide a new idea for electroless nickel plating on anodic oxide film.
基金Project(51961003)supported by the National Natural Science Foundation of ChinaProject(NGY2018-148)supported by the Science and Technology Research of Ningxia Colleges,ChinaProject(NZ16083)supported by Key Program of Natural Science Foundation of Ningxia,China
文摘In order to improve the hot corrosion resistance of DZ125 alloy,Ce-Y modified aluminum coatings were prepared on DZ125 alloy by pack cementation process at 950°C for 2 h.The microstructure,phase constitution and formation mechanism of the coatings were investigated.The hot corrosion behaviors of DZ125 alloy and the coatings in molten salt environment of 25%K2SO4+75%Na2SO4(mass fraction)at 900°C were studied.Results show that the obtained Al-Ce-Y coatings were mainly composed of Al3Ni2,Al3Ni and Cr7Ni3,with a thickness of about 120μm.After hot corrosion test,DZ125 alloy suffered catastrophic hot corrosion and serious internal oxidation and internal sulfidation arose.Two layers of corrosion products formed on surfaces of DZ125 alloy,including the outer layer consisting of Cr2O3 and NiCr2O4,and the inner layer of Al2O3,Ni3S2 and Ni-base solid solution.After being coated with Al-Ce-Y coating,the hot corrosion resistance of DZ125 alloy is improved notably,due to the formation of a dense scale mainly consisting of Al-rich Al2O3 in the coating layer.
文摘The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray technique. The relationship among the composition, structure and property of the coatings are investiga ted by means of optical microscope, scanning electronic microscope and the experiments of thermal shock resistance cycling and high temperature oxidation resistance. The results show that the structure design of introdu cing a transition layer between Ni alloy substrate and ZrO 2 ceramic coating guarantees the high quality and properties of the coatings; ZrO 2 coatings doped with a little SiO 2 possesses better thermal shock resistance and more excellent hot corrosion resistance as compared with ZrO 2 coating materials without SiO 2 ;the improvement in performance of ZrO 2 coating doped with SiO 2 is due to forming more dense coating structure by self closing effects of the flaws and pores in the ZrO 2 coatings.
文摘Despite the great achievements made in improvement of wear resistance properties of aluminum alloys, their applications in heavy surface load-bearing are limited. Single coating is insufficient to produce the desired combination of surface properties. These problems can be solved through the duplex coatings. The aim of the present study is to overview the research advances on processes of duplex coatings on (aluminum) alloys combined with micro plasma oxidation process and with other modern processes such as physical vapour deposition and plasma assisted chemical vapour deposition and also to evaluate the performance of micro plasma oxidation coatings in improving the load-bearing, friction and wear resistance properties of aluminum alloys in comparison with other coatings. Wherein, a more detailed presentation of the processes and their performances and disadvantages are given as well.
基金Project(50721003) supported by Creative Research Group of National Natural Science Foundation of ChinaProject(2009ZX04012-021) supported by the National Major Special Science and Technology Program of China
文摘Ti-X-N (X=Al,Si or Al+Si) coatings were grown onto cemented carbide substrates by cathodic arc evaporation. The hardness of the coatings was obtained by nanoindentation and the microstructure was investigated by XRD,XPS and SEM. Solid solution hardening results in a hardness increase from 24 GPa for TiN to 31.2 GPa for TiAlN. The higher hardness values of 36.7 GPa for TiSiN and 42.4 GPa for TiAlSiN are obtained by the incorporation of Si into TiN (TiAlN) coatings due to the formation of special three-dimensional net structure consisting of nanocrystalline (nc) TiN (TiAlN) encapsulated in an amorphous (a) Si3N4 matrix phase. Furthermore,the nc-TiAlN/a-Si3N4 coating shows the best machining performance.
基金Project(2020AAC02025)supported by the Natural Science Foundation of Ningxia Province,ChinaProject(51961003)supported by the National Natural Science Foundation of China+1 种基金Project(TJGC2019040)supported by the Ningxia Youth Talents Supporting Program,ChinaProject(2020xyzc103)supported by the Foundation of North Minzu University,China。
文摘In order to obtain a high-performance surface on TiAl alloy that can meet the requirements in hot corrosion environment,Si-Al-Y coatings were fabricated by pack cementation process at 1050℃for 4 h.Corrosion behaviors of the TiAl alloy with and without Si-Al-Y coatings are compared to illustrate the factors and corresponding mechanism in molten salt environment of 25 wt%K2SO4 and 75 wt%Na2SO4 at 900°C.The obtained Si-Al-Y coating was mainly composed of a TiSi2 outer layer,a(Ti,X)5Si4 and(Ti,X)5Si3(X represents Nb or Cr element)middle layer,a TiAl2 inner layer and a Al-rich inter-diffusion zone.The inter-phase selective corrosion containing corrosion pits extending alongα2 phase from lamellar interfaces in hot corrosion tested TiAl alloy was observed.However,by being coated with Si-Al-Y coating,the hot corrosion performance of TiAl alloy was improved remarkably.
文摘Functionalized implants demonstrate an upgraded approach in orthopedic implants,aiming to achieve long term success through improved bio integration.Bioceramic coatings with multifunctionality have arisen as an effective substitute for conventional coatings,owing to their combination of various properties that are essential for bio-implants,such as osteointegration and antibacterial character.In the present study,thin hopeite coatings were produced by Pulsed laser deposition(PLD)and radio frequency magnetron sputtering(RFMS)on Ti64 substrates.The obtained hopeite coatings were annealed at 500°C in ambient air and studied in terms of surface morphology,phase composition,surface roughness,adhesion strength,antibacterial efficacy,apatite forming ability,and surface wettability by scanning electron microscope(SEM),X-ray diffraction(XRD),atomic force microscope(AFM),tensometer,fluorescence-activated cell sorting(FACS),simulated body fluid(SBF)immersion test and contact angle goniometer,respectively.Furthermore,based on promising results obtained in the present work it can be summarized that the new generation multifunctional hopeite coating synthesized by two alternative new process routes of PLD and RFMS on Ti64 substrates,provides effective alternatives to conventional coatings,largely attributed to strong osteointegration and antibacterial character of deposited hopeite coating ensuring the overall stability of metallic orthopedic implants.
基金Project(2005CB623703) supported by the National Key Basic Research Program of ChinaProject(50474051) supported by the National Natural Science Foundation of China+2 种基金Project(CX2009B032) supported by Innovation Foundation for Postgraduate of Hunan Province of China Project(ZKJ2009024) supported by the Precious Apparatus Open Share Foundation of Central South University, ChinaProject(2009ybfz02) supported by Excellent Doctor Support Fund of Central South University,China
文摘Ni-Co-Fe2O3 composite coatings were electrodeposited using cetyltrimethylammonium bromide(CTAB)-modified Watt's nickel bath with Fe2O3 particles dispersed in it.The effects of the plating parameters on the chemical composition,structural and morphological characteristics of the electrodeposited Ni-Co-Fe2O3 composite coatings were investigated by energy dispersive X-ray(EDS) spectroscopy,X-ray diffractometry(XRD) and scanning electron microscopy(SEM).The results reveal that Fe2O3 particles can be codeposited in the Ni-Co matrix.The codeposition of Fe2O3 particles with Ni-Co is favoured at high Fe2O3 particle concentration and medium stirring,and the deposition of Co is favoured at high concentration of CTAB.Moreover,the study of the textural perfection of the deposits reveals that the presence of particles leads to the worsening of the quality of the observed <220> preferred orientation.Composites with high concentration of embedded particles exhibit a preferred crystal orientation of <111>.The more the embedded Fe2O3 particles in the metallic matrix,the smaller the sizes of the crystallite for the composite deposits.