LiNi0. 45 Co0. 10 Mn0. 4sO2 was synthesized from Li2CO3 and a triple oxide of nickel, cobalt and manganese at 950 ℃ in air. The structures and characteristics of LiNi0. 45 Co0.10 Mn0. 45 O2, LiCoO2 and LiMn2 O4 were ...LiNi0. 45 Co0. 10 Mn0. 4sO2 was synthesized from Li2CO3 and a triple oxide of nickel, cobalt and manganese at 950 ℃ in air. The structures and characteristics of LiNi0. 45 Co0.10 Mn0. 45 O2, LiCoO2 and LiMn2 O4 were investigated by XRD, SEM and electrochemical measurements. The results show that LiNi0.4s Co0.10 Mn0. 45 O2 has a layered structure with hexagonal lattice. The commercial LicoO2 has sphere-like appearance and smooth surfaces, while the LiMn2 O4 and LiNi0.45 Co0. 10 Mn0. 45 O2 consist of cornered and uneven particles. LiNi0. 45 Co0.10 Mn0. 45 O2 has a large disLiMn2 O4 and LiCoO2, respectively. LiCoO2 and LiMn2 O4 have higher discharge voltage and better rate-capability than LiNi0. 45Co0.10 Mn0. 45 O2. All the three cathodes have excellent cycling performance with capacity retention of above 89.3 % at the 250th cycle. Batteries with LiMn2 O4 or LiNi0.45 Co0.10 Mn0. 45 O2 cathodes show better safety performance under abusive conditions than those with LiCoO2 cathodes.展开更多
Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indica...Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.展开更多
The spinel LiMn2O4 used as cathode materials for lithium-ion batteries was synthesized by mechanochemistry fluid activation process, and modified by doping rare-earth Sm. Testing of X-ray diffraction, cyclic voltammog...The spinel LiMn2O4 used as cathode materials for lithium-ion batteries was synthesized by mechanochemistry fluid activation process, and modified by doping rare-earth Sm. Testing of X-ray diffraction, cyclic voltammograms, charge-discharge and SEM was carried out for LiMn2O4 cathode materials and the modified materials.The results show that the cathode materials doped rare earth LixMn2-ySmxO4 (0.95≤x≤1.2, 0≤y≤0.3, 0≤z≤0.2) exhibit standard spinel structure, high reversibility of electrochemistry and excellent properties of charge-discapacity is deteriorated less than 15% after 300 cycles at room temperature and less than 20% after 200 cycles at 55 C.At the same time, Crystal Field Theory was applied to explain the function and mechanism of doped rare earth element.展开更多
With citric acid as a polymeric agent layered LiNi0.8Co0.2O2 materials were synthesized by a spray pyrolysis method. The LiNi0.sCo0.2O2 particles were characterized by means of XRD, SEM and TEM. The electrochemical pe...With citric acid as a polymeric agent layered LiNi0.8Co0.2O2 materials were synthesized by a spray pyrolysis method. The LiNi0.sCo0.2O2 particles were characterized by means of XRD, SEM and TEM. The electrochemical performances of LiNi0.8Co0.2O2 particles were studied in a voltage window of 3.00-4.35 V and at a current density of 30 mA/g. The results show that in the pilot-scale spray pyrolysis process, the morphology of particles is dependent upon the precursor concentration and flux of carrier gas. The initial discharge capacity of the LiNi0.8Co0.2O2particles at 720 ℃ for 12 h is 187.3 mA.h/g, and the capacity remains 96.8% with excellent cycleability after 30 cycles. The LiNi0.8Co0.2O2 samples synthesized under the optimized conditions by the spray pyrolysis method shows a good electrochemical performance.展开更多
A simple strategy to prepare a hybrid of nanocomposites of anatase TiO2/graphene nanosheets （GNS） as anode materials for lithium-ion batteries was reported.The morphology and crystal structure were studied by X-ray ...A simple strategy to prepare a hybrid of nanocomposites of anatase TiO2/graphene nanosheets （GNS） as anode materials for lithium-ion batteries was reported.The morphology and crystal structure were studied by X-ray diffraction （XRD）,field emission scanning electron microscopy （FE-SEM） and transmission electron microscopy （TEM）.The electrochemical performance was evaluated by galvanostatic charge-lischarge tests and alternating current （AC） impedance spectroscopy.The results show that the TiO2/GNS electrode exhibit higher electrochemical performance than that of TiO2 electrode regardless of the rate.Even at 500 mA/g,the capacity of TiO2/GNS is 120.3 mAh/g,which is higher than that of TiO2 61.6 mAh/g.The high performance is attributed to the addition of graphene to improve electrical conductivity and reduce polarization.展开更多
Hexagonal porous Nb2O5 was synthesized for the first time via a facile solid-state reaction.The structure and electrochemical properties have been optimized through tuning heating temperature.X-ray diffraction results...Hexagonal porous Nb2O5 was synthesized for the first time via a facile solid-state reaction.The structure and electrochemical properties have been optimized through tuning heating temperature.X-ray diffraction results indicate that pseudo hexagonal Nb2O5(TT-Nb2O5)and orthorhombic Nb2O5 have been synthesized at different temperatures.Hexagonal sheet and porous structure of Nb2O5 were characterized by scanning electron microscopy and N2-adsorption-desorption isotherms.The as-prepared TT-Nb2O5(heated at 600℃)shows the best performance with a remarkable charge capacity of 178 mA∙h/g at 0.2C,which is higher than that of T-Nb2O5.Even at 20℃,TT-Nb2O5 offers unprecedented rate capability up to 86 mA∙h/g.The high rate capacity is due to pseudocapacitive Li+intercalation mechanism of TT-Nb2O5.The reported results demonstrate that Nb2O5 with good crystal structure and high specific surface area is a powerful composite design for high-rate and safe anode materials.展开更多
Li2FeSiO4 is deemed to be a potential candidate for large-scale applications because of its abundance,low cost and high safety,etc.Unfortunately,its low conductivity,resulting in poor rate performance,has become a mai...Li2FeSiO4 is deemed to be a potential candidate for large-scale applications because of its abundance,low cost and high safety,etc.Unfortunately,its low conductivity,resulting in poor rate performance,has become a main obstacle to its applications in power battery and energy storage system.In this work,C-Ag coated Li2FeSiO4 is introduced to improve the innate electronic conductivity and Li-ion diffusion ability.The results demonstrate that Li2FeSiO4/C/Ag composite exhibits better electrochemical performance.It possesses a specific discharge capacity of 152,121,108 mA.h/g at 0.2C,5C and 10C,respectively.At the same time,the Li2FeSiO4/C/Ag composite shows good cycle stability and a capacity retention ratio of 97.9%after 100 cycles at 1C.展开更多
Sb-based materials have been considered one of the most promising anode electrode materials for lithium-ion batteries,whereas they were commonly synthesized through time-consuming and costly processes.Here,Sb@Sb2O3/re...Sb-based materials have been considered one of the most promising anode electrode materials for lithium-ion batteries,whereas they were commonly synthesized through time-consuming and costly processes.Here,Sb@Sb2O3/reduced graphene oxide(Sb@Sb2O3/rGO)composite was successfully synthesized by a facile one-pot chemical method at ambient temperature.Based on the XRD and TGA analysis,the mass fractions of Sb and Sb2O3 in the Sb@Sb2O3/rGO composite are ca.34.05%and 26.6%,respectively.When used as an alternative electrode for lithium ion batteries,a high reversible capacity of 790.9 mA·h/g could be delivered after 200 cycles with the capacity retention of 93.8%at a current density of 200 mA/g.And a capacity of 260 mA·h/g could be maintained even at 2000 mA/g.These excellent electrochemical properties can be attributed to its well-constructed nanostructure.The Sb and Sb2O3 particles with size of 10 nm were tightly anchored on rGO sheets through electronic coupling,which could not only alleviate the stress induced by the volume expansion,suppress the aggregation of Sb and Sb2O3 particles,but also improve the electron transfer ability during cycling.展开更多
基金Project(50302016) supported by the National Natural Science Foundation of China Project(2005037698) supported by the Postdoctoral Science Foundation of China
文摘LiNi0. 45 Co0. 10 Mn0. 4sO2 was synthesized from Li2CO3 and a triple oxide of nickel, cobalt and manganese at 950 ℃ in air. The structures and characteristics of LiNi0. 45 Co0.10 Mn0. 45 O2, LiCoO2 and LiMn2 O4 were investigated by XRD, SEM and electrochemical measurements. The results show that LiNi0.4s Co0.10 Mn0. 45 O2 has a layered structure with hexagonal lattice. The commercial LicoO2 has sphere-like appearance and smooth surfaces, while the LiMn2 O4 and LiNi0.45 Co0. 10 Mn0. 45 O2 consist of cornered and uneven particles. LiNi0. 45 Co0.10 Mn0. 45 O2 has a large disLiMn2 O4 and LiCoO2, respectively. LiCoO2 and LiMn2 O4 have higher discharge voltage and better rate-capability than LiNi0. 45Co0.10 Mn0. 45 O2. All the three cathodes have excellent cycling performance with capacity retention of above 89.3 % at the 250th cycle. Batteries with LiMn2 O4 or LiNi0.45 Co0.10 Mn0. 45 O2 cathodes show better safety performance under abusive conditions than those with LiCoO2 cathodes.
基金Projects(51472211,51502256)supported by the National Natural Science Foundation of ChinaProjects(2016GK4005,2016GK4030)supported by the Strategic New Industry of Hunan Province,ChinaProject(13C925)supported by the Research Foundation of Education Bureau of Hunan Province,China
文摘Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.
基金Project (02JJY2081) supported by the Natural Science Foundation of Hunan Province
文摘The spinel LiMn2O4 used as cathode materials for lithium-ion batteries was synthesized by mechanochemistry fluid activation process, and modified by doping rare-earth Sm. Testing of X-ray diffraction, cyclic voltammograms, charge-discharge and SEM was carried out for LiMn2O4 cathode materials and the modified materials.The results show that the cathode materials doped rare earth LixMn2-ySmxO4 (0.95≤x≤1.2, 0≤y≤0.3, 0≤z≤0.2) exhibit standard spinel structure, high reversibility of electrochemistry and excellent properties of charge-discapacity is deteriorated less than 15% after 300 cycles at room temperature and less than 20% after 200 cycles at 55 C.At the same time, Crystal Field Theory was applied to explain the function and mechanism of doped rare earth element.
基金Project(50604018) supported by the National Natural Science Foundation of China
文摘With citric acid as a polymeric agent layered LiNi0.8Co0.2O2 materials were synthesized by a spray pyrolysis method. The LiNi0.sCo0.2O2 particles were characterized by means of XRD, SEM and TEM. The electrochemical performances of LiNi0.8Co0.2O2 particles were studied in a voltage window of 3.00-4.35 V and at a current density of 30 mA/g. The results show that in the pilot-scale spray pyrolysis process, the morphology of particles is dependent upon the precursor concentration and flux of carrier gas. The initial discharge capacity of the LiNi0.8Co0.2O2particles at 720 ℃ for 12 h is 187.3 mA.h/g, and the capacity remains 96.8% with excellent cycleability after 30 cycles. The LiNi0.8Co0.2O2 samples synthesized under the optimized conditions by the spray pyrolysis method shows a good electrochemical performance.
基金Project(Y4110230)supported by Natural Science Foundation of Zhejiang Province,ChinaProject(51204146,51101140)supported by the National Natural Science Foundation of ChinaProject(2012M521197)supported by Postdoctoral Science Foundation of China
文摘A simple strategy to prepare a hybrid of nanocomposites of anatase TiO2/graphene nanosheets （GNS） as anode materials for lithium-ion batteries was reported.The morphology and crystal structure were studied by X-ray diffraction （XRD）,field emission scanning electron microscopy （FE-SEM） and transmission electron microscopy （TEM）.The electrochemical performance was evaluated by galvanostatic charge-lischarge tests and alternating current （AC） impedance spectroscopy.The results show that the TiO2/GNS electrode exhibit higher electrochemical performance than that of TiO2 electrode regardless of the rate.Even at 500 mA/g,the capacity of TiO2/GNS is 120.3 mAh/g,which is higher than that of TiO2 61.6 mAh/g.The high performance is attributed to the addition of graphene to improve electrical conductivity and reduce polarization.
基金Projects(51974137,51774150)supported by the National Natural Science Foundation of ChinaProject(2020M671361)supported by China Postdoctoral Science Foundation。
文摘Hexagonal porous Nb2O5 was synthesized for the first time via a facile solid-state reaction.The structure and electrochemical properties have been optimized through tuning heating temperature.X-ray diffraction results indicate that pseudo hexagonal Nb2O5(TT-Nb2O5)and orthorhombic Nb2O5 have been synthesized at different temperatures.Hexagonal sheet and porous structure of Nb2O5 were characterized by scanning electron microscopy and N2-adsorption-desorption isotherms.The as-prepared TT-Nb2O5(heated at 600℃)shows the best performance with a remarkable charge capacity of 178 mA∙h/g at 0.2C,which is higher than that of T-Nb2O5.Even at 20℃,TT-Nb2O5 offers unprecedented rate capability up to 86 mA∙h/g.The high rate capacity is due to pseudocapacitive Li+intercalation mechanism of TT-Nb2O5.The reported results demonstrate that Nb2O5 with good crystal structure and high specific surface area is a powerful composite design for high-rate and safe anode materials.
基金Project(21771062)supported by the National Natural Science Foundation of ChinaProject(2016JJ2092)supported by the Hunan Provincial Natural Science Foundation,ChinaProject(2019013)supported by the Open Project Program of Key Laboratory of Preparation and Application of Environmental Friendly Materials,Ministry of Education,Jilin Normal University,China
文摘Li2FeSiO4 is deemed to be a potential candidate for large-scale applications because of its abundance,low cost and high safety,etc.Unfortunately,its low conductivity,resulting in poor rate performance,has become a main obstacle to its applications in power battery and energy storage system.In this work,C-Ag coated Li2FeSiO4 is introduced to improve the innate electronic conductivity and Li-ion diffusion ability.The results demonstrate that Li2FeSiO4/C/Ag composite exhibits better electrochemical performance.It possesses a specific discharge capacity of 152,121,108 mA.h/g at 0.2C,5C and 10C,respectively.At the same time,the Li2FeSiO4/C/Ag composite shows good cycle stability and a capacity retention ratio of 97.9%after 100 cycles at 1C.
基金Project(51462032)supported by the National Natural Science Foundation of ChinaProject(17JR5RA066)supported by the Foundation for Distinguished Young Scholars of Gansu Province,China
文摘Sb-based materials have been considered one of the most promising anode electrode materials for lithium-ion batteries,whereas they were commonly synthesized through time-consuming and costly processes.Here,Sb@Sb2O3/reduced graphene oxide(Sb@Sb2O3/rGO)composite was successfully synthesized by a facile one-pot chemical method at ambient temperature.Based on the XRD and TGA analysis,the mass fractions of Sb and Sb2O3 in the Sb@Sb2O3/rGO composite are ca.34.05%and 26.6%,respectively.When used as an alternative electrode for lithium ion batteries,a high reversible capacity of 790.9 mA·h/g could be delivered after 200 cycles with the capacity retention of 93.8%at a current density of 200 mA/g.And a capacity of 260 mA·h/g could be maintained even at 2000 mA/g.These excellent electrochemical properties can be attributed to its well-constructed nanostructure.The Sb and Sb2O3 particles with size of 10 nm were tightly anchored on rGO sheets through electronic coupling,which could not only alleviate the stress induced by the volume expansion,suppress the aggregation of Sb and Sb2O3 particles,but also improve the electron transfer ability during cycling.