The acidic modulations of a series of HZSM-5 catalysts were successfully made by calcination at different treatment temperatures, i.e. 500, 600, 650, 700 and 800 ℃, respectively. The results indicated that the total ...The acidic modulations of a series of HZSM-5 catalysts were successfully made by calcination at different treatment temperatures, i.e. 500, 600, 650, 700 and 800 ℃, respectively. The results indicated that the total acid amounts, their density and the amount of B-type acid of HZSM-5 catalysts rapidly decreased, while the amounts of L-type acid had almost no change and thus the ratio of L/B was obviously enhanced with the increase of calcination temperature （excluding 800 ℃）. The catalytic performances of modified HZSM-5 catalysts for the cracking of n-butane were also investigated. The main properties of these catalysts were characterized by means of XRD, N2 adsorption at low temperature, NH3-TPD, FTIR of pyridine adsorption and BET surface area measurements. The results showed that HZSM-5 zeolite pretreated at 800 ℃ had very low catalytic activity for n-butane cracking. In the calcination temperature range of 500-700 ℃, the total selectivity to olefins, propylene and butene were increased with the increase of calcination temperature, while, the selectivity for arene decreased with the calcination temperature. The HZSM-5 zeolite calcined at 700 ℃ produced light olefins with high yield, at the reaction temperature of 650 ℃ the yields of total olefins and ethylene were 52.8% and 29.4%, respectively. Besides, the more important role is that high calcination temperature treatment improved the duration stability of HZSM-5 zeolites. The effect of calcination temperature on the physico-chemical properties and catalytic performance of HZSM-5 for cracking of n-butane was explored. It was found that the calcination temperature had large effects on the surface area, crystallinity and acid properties of HZSM-5 catalyst, which further affected the catalytic performance for n-butane cracking.展开更多
Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673 K were investigated. The acidity and distribution of acidic sites were studied by infrared spect...Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673 K were investigated. The acidity and distribution of acidic sites were studied by infrared spectroscopy using pyridine as probe molecule and temperature programmed desorption (TPD) of ammonia. The structure of the samples was characterized by XRD, and the textural properties of the catalysts were determined by nitrogen isothermal adsorption-desorption measurements and scanning electron microscopy (SEM). The XRD results show that the modified samples have no novel crystalline phase, indicating a high dispersion of phosphorus and boron species. After treatment, the microporous volume and surface area of the samples markedly decrease, implying the blockage of the channel. The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of isothermal type I and IV, and all hysteresis loops resemble the H4-type in the IUPAC classification. The total acidity of the modified samples, determined by pyridine adsorption IR and TPD of ammonia, decreases in contrast to that of the parent HZSM-5. The conversion of n-heptane over P and B steam-modified HZSM-5 is higher than that of P and B-modified HZSM-5 zeolites but lower than that of the parent HZSM-5.展开更多
基金The authors would like to thank the financial support from the National Basic Research Program of China fgrant No．2004CB 217806)the National Natural Science Foundation of China (Grant No．20373043) the Scientific Research Key Foundation for the Returned Overseas Chinese Scholars of State Education Ministry．
文摘The acidic modulations of a series of HZSM-5 catalysts were successfully made by calcination at different treatment temperatures, i.e. 500, 600, 650, 700 and 800 ℃, respectively. The results indicated that the total acid amounts, their density and the amount of B-type acid of HZSM-5 catalysts rapidly decreased, while the amounts of L-type acid had almost no change and thus the ratio of L/B was obviously enhanced with the increase of calcination temperature （excluding 800 ℃）. The catalytic performances of modified HZSM-5 catalysts for the cracking of n-butane were also investigated. The main properties of these catalysts were characterized by means of XRD, N2 adsorption at low temperature, NH3-TPD, FTIR of pyridine adsorption and BET surface area measurements. The results showed that HZSM-5 zeolite pretreated at 800 ℃ had very low catalytic activity for n-butane cracking. In the calcination temperature range of 500-700 ℃, the total selectivity to olefins, propylene and butene were increased with the increase of calcination temperature, while, the selectivity for arene decreased with the calcination temperature. The HZSM-5 zeolite calcined at 700 ℃ produced light olefins with high yield, at the reaction temperature of 650 ℃ the yields of total olefins and ethylene were 52.8% and 29.4%, respectively. Besides, the more important role is that high calcination temperature treatment improved the duration stability of HZSM-5 zeolites. The effect of calcination temperature on the physico-chemical properties and catalytic performance of HZSM-5 for cracking of n-butane was explored. It was found that the calcination temperature had large effects on the surface area, crystallinity and acid properties of HZSM-5 catalyst, which further affected the catalytic performance for n-butane cracking.
基金Financial support from Catalytic Key Laboratory of China Petroleum and Natural Gas Group Corpo- ration (University of Petroleum) was greatly appre- ciated. We thank the National Science Foundation Committee for Grant NSFC 20233030.
文摘Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673 K were investigated. The acidity and distribution of acidic sites were studied by infrared spectroscopy using pyridine as probe molecule and temperature programmed desorption (TPD) of ammonia. The structure of the samples was characterized by XRD, and the textural properties of the catalysts were determined by nitrogen isothermal adsorption-desorption measurements and scanning electron microscopy (SEM). The XRD results show that the modified samples have no novel crystalline phase, indicating a high dispersion of phosphorus and boron species. After treatment, the microporous volume and surface area of the samples markedly decrease, implying the blockage of the channel. The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of isothermal type I and IV, and all hysteresis loops resemble the H4-type in the IUPAC classification. The total acidity of the modified samples, determined by pyridine adsorption IR and TPD of ammonia, decreases in contrast to that of the parent HZSM-5. The conversion of n-heptane over P and B steam-modified HZSM-5 is higher than that of P and B-modified HZSM-5 zeolites but lower than that of the parent HZSM-5.