A series of CuO/Ce1-xZrxO2 catalysts(x=0.2,0.4,0.6 and 0.8)are applied to elaborate the effect of the Zr/Ce ratio on the catalytic performance of CO2 hydrogenation to CH3OH.The best catalytic performance is achieved w...A series of CuO/Ce1-xZrxO2 catalysts(x=0.2,0.4,0.6 and 0.8)are applied to elaborate the effect of the Zr/Ce ratio on the catalytic performance of CO2 hydrogenation to CH3OH.The best catalytic performance is achieved with CuO/Ce0.4Zr0.6O2,exhibiting XCO2=13.2%and YCH3OH=9.47%(T=280℃,P=3 MPa).The formation of dispersed surface CuO species and larger number of oxygen vacancies are detected over CuO/Ce0.4Zr0.6O2 due to stronger interaction between CuO and Ce0.4Zr0.6O2,resulting in the superior activation ability for H2 and CO2 respectively.Additionally,the evidence is provided by in situ DRIFTS under the activity test pressure(3 MPa)that bi/m-HCOO* species are preferable for accumulating over ceria-rich(CuO/Ce0.6Zr0.4O2 and CuO/Ce0.8Zr0.2O2)catalysts while zirconia-rich(CuO/Ce0.4Zr0.6O2 and CuO/Ce0.2Zr0.8O2)catalysts are benefit to encourage the transformation of bi/m-HCOO* species to CH3OH.The abundant population and high activity of intermediate species over CuO/Ce0.4Zr0.6O2 give a strong positive effect on the catalytic performance.展开更多
An In2O3 supported nickel catalyst has been prepared by wet chemical reduction with sodium borohydride(NaBH4) as a reducing agent for selective hydrogenation of carbon dioxide to methanol. Highly dispersed Ni species ...An In2O3 supported nickel catalyst has been prepared by wet chemical reduction with sodium borohydride(NaBH4) as a reducing agent for selective hydrogenation of carbon dioxide to methanol. Highly dispersed Ni species with intense Ni-In2O3 interaction and enhanced oxygen vacancies have been achieved.The highly dispersed Ni species serve as the active sites for hydrogen activation and hydrogen spillover.Abundant H adatoms are thereby generated for the oxygen vacancy creation on the In2O3 surface. The enhanced surface oxygen vacancies further lead to improved CO2 conversion. As a result, an effective synergy between the active Ni sites and surface oxygen vacancies on In2O3 causes a superior catalytic performance for CO2 hydrogenation with high methanol selectivity. Carbon monoxide is the only by product detected. The formation of methane can be ignored. When the reaction temperature is lower than 225 ℃,the selectivity of methanol is 100%. It is higher than 64% at the temperature range between 225 ℃ and 275 ℃. The methanol selectivity is still higher than 54% at 300 ℃ with a CO2 conversion of 18.47% and a methanol yield of 0.55 gMeOHg-1cath-1(at 5 MPa). The activity of Ni/In2O3 is higher than most of the reported In2O3-based catalysts.展开更多
A series of composite catalysts were prepared by the wet mixing method, and the mass ratio of CuO-ZnO-Al2O3-ZrO2 component to HZSM-5 zeolite （molar ratio of SiO2 to Al2O3 being 25） was 2：1. The CuO-ZnO-Al2O3-ZrO2 ...A series of composite catalysts were prepared by the wet mixing method, and the mass ratio of CuO-ZnO-Al2O3-ZrO2 component to HZSM-5 zeolite （molar ratio of SiO2 to Al2O3 being 25） was 2：1. The CuO-ZnO-Al2O3-ZrO2 （CuO/ZnO/Al2O3=3/6/1 by weight） component was prepared by a modified ＇two-step＇ co-precipitation method. The effects of ZrO2 on the performance of CuO-ZnO-Al2O3/HZSMo5 catalyst for dimethyl ether synthesis from CO2 hydrogenation were investigated. It was found that ZrO2 improved the properties of CuO-ZnO-Al2O3/HZSM-5 as a structural promoter.展开更多
In the present work, different silica-based supported cobalt （Co） catalysts were synthesized and used for CO2 hydrogenation for methanation. Different supports, such as SSP, MCM-41, TiSSP and TiMCM were used to prep...In the present work, different silica-based supported cobalt （Co） catalysts were synthesized and used for CO2 hydrogenation for methanation. Different supports, such as SSP, MCM-41, TiSSP and TiMCM were used to prepare Co catalysts with 20 wt% Co loading. The supports and catalysts were characterized by means of N2 physisorption, XRD, SEM/EDX, XPS, TPR and CO chemisorption. It is found that after calcination of catalysts, Ti is present in the form of anatase. The introduction of Ti plays important roles in the properties of Co catalysts by：（i） facilitating the reduction of Co oxides species which are strongly interacted with support, （ii） preventing the formation of silicate compounds, and （iii） inhibiting the RWGS reaction. Based on CO2 hydrogenation, the CoTiMCM catalyst exhibites the highest activity and stability.展开更多
Catalytic conversion of COinto chemicals and fuels is an alternative to alleviate climate change and ocean acidification.The catalytic reduction of COby Hcan lead to the formation of various products:carbon monoxide,c...Catalytic conversion of COinto chemicals and fuels is an alternative to alleviate climate change and ocean acidification.The catalytic reduction of COby Hcan lead to the formation of various products:carbon monoxide,carboxylic acids,aldehydes,alcohols and hydrocarbons.In this paper,a comprehensive thermodynamics analysis of COhydrogenation is conducted using the Gibbs free energy minimization method.The results show that COreduction to CO needs a high temperature and H/COratio to achieve a high COconversion.However,synthesis of methanol from COneeds a relatively high pressure and low temperature to minimize the reverse water-gas shift reaction.Direct COhydrogenation to formic acid or formaldehyde is thermodynamically limited.On the contrary,production of CHfrom COhydrogenation is the thermodynamically easiest reaction with nearly 100%CH4 yield at moderate conditions.In addition,complex reactions with more than one product are also calculated in this work.Among the considered carboxylic acids（HCOOH,CHCOOH and CHCOOH）,propionic acid dominates in the product stream（selectivity above 90%）.The same trend can also be found in the hydrogenation of COto aldehydes and alcohols with the major product of propionaldehyde and butanol,respectively.In the process of COhydrogenation to alkenes,low temperature,high pressure,and high Hpartial pressure favor the COconversion.CHis the most thermodynamically favorable among all considered alkynes under different temperatures and pressures.The thermodynamic calculations are validated with experimental results,suggesting that the Gibbs free energy minimization method is effective for thermodynamically understanding the reaction network involved in the COhydrogenation process,which is helpful for the development of high-performance catalysts.展开更多
Methanol synthesis from hydrogenation of CO2 is investigated over Cu/ZnO/Al2O3 catalysts prepared by decomposition of M（Cu,Zn）-ammonia complexes （DMAC） at various temperatures.The catalysts were characterized in d...Methanol synthesis from hydrogenation of CO2 is investigated over Cu/ZnO/Al2O3 catalysts prepared by decomposition of M（Cu,Zn）-ammonia complexes （DMAC） at various temperatures.The catalysts were characterized in detail,including X-ray diffraction,N2 adsorption-desorption,N2O chemisorption,temperature-programmed reduction and evolved gas analyses.The influences of DMAC temperature,reaction temperature and specific Cu surface area on catalytic performance are investigated.It is considered that the aurichalcite phase in the precursor plays a key role in improving the physiochemical properties and activities of the final catalysts.The catalyst from rich-aurichalcite precursor exhibits large specific Cu surface area and high space time yield of methanol （212 g/（Lcat·h）;T=513 K,p=3MPa,SV=12000 h-1）.展开更多
基金financially supported by the National Nature Science Foundation of China (21876019, 21577014)Strategic Priority Research Program of the Chinese Academy of Sciences (XDB17020000)the fund of the State Key Laboratory of Catalysis in DICP (N18-08)。
文摘A series of CuO/Ce1-xZrxO2 catalysts(x=0.2,0.4,0.6 and 0.8)are applied to elaborate the effect of the Zr/Ce ratio on the catalytic performance of CO2 hydrogenation to CH3OH.The best catalytic performance is achieved with CuO/Ce0.4Zr0.6O2,exhibiting XCO2=13.2%and YCH3OH=9.47%(T=280℃,P=3 MPa).The formation of dispersed surface CuO species and larger number of oxygen vacancies are detected over CuO/Ce0.4Zr0.6O2 due to stronger interaction between CuO and Ce0.4Zr0.6O2,resulting in the superior activation ability for H2 and CO2 respectively.Additionally,the evidence is provided by in situ DRIFTS under the activity test pressure(3 MPa)that bi/m-HCOO* species are preferable for accumulating over ceria-rich(CuO/Ce0.6Zr0.4O2 and CuO/Ce0.8Zr0.2O2)catalysts while zirconia-rich(CuO/Ce0.4Zr0.6O2 and CuO/Ce0.2Zr0.8O2)catalysts are benefit to encourage the transformation of bi/m-HCOO* species to CH3OH.The abundant population and high activity of intermediate species over CuO/Ce0.4Zr0.6O2 give a strong positive effect on the catalytic performance.
基金the National Natural Science Foundation of China(No.21536008 and 21621004)。
文摘An In2O3 supported nickel catalyst has been prepared by wet chemical reduction with sodium borohydride(NaBH4) as a reducing agent for selective hydrogenation of carbon dioxide to methanol. Highly dispersed Ni species with intense Ni-In2O3 interaction and enhanced oxygen vacancies have been achieved.The highly dispersed Ni species serve as the active sites for hydrogen activation and hydrogen spillover.Abundant H adatoms are thereby generated for the oxygen vacancy creation on the In2O3 surface. The enhanced surface oxygen vacancies further lead to improved CO2 conversion. As a result, an effective synergy between the active Ni sites and surface oxygen vacancies on In2O3 causes a superior catalytic performance for CO2 hydrogenation with high methanol selectivity. Carbon monoxide is the only by product detected. The formation of methane can be ignored. When the reaction temperature is lower than 225 ℃,the selectivity of methanol is 100%. It is higher than 64% at the temperature range between 225 ℃ and 275 ℃. The methanol selectivity is still higher than 54% at 300 ℃ with a CO2 conversion of 18.47% and a methanol yield of 0.55 gMeOHg-1cath-1(at 5 MPa). The activity of Ni/In2O3 is higher than most of the reported In2O3-based catalysts.
文摘A series of composite catalysts were prepared by the wet mixing method, and the mass ratio of CuO-ZnO-Al2O3-ZrO2 component to HZSM-5 zeolite （molar ratio of SiO2 to Al2O3 being 25） was 2：1. The CuO-ZnO-Al2O3-ZrO2 （CuO/ZnO/Al2O3=3/6/1 by weight） component was prepared by a modified ＇two-step＇ co-precipitation method. The effects of ZrO2 on the performance of CuO-ZnO-Al2O3/HZSMo5 catalyst for dimethyl ether synthesis from CO2 hydrogenation were investigated. It was found that ZrO2 improved the properties of CuO-ZnO-Al2O3/HZSM-5 as a structural promoter.
基金supported by the Thailand Research Fund(TRF)and Office of the Higher Education Commission(CHE)the National Research Council of Thailand(NRCT)NRU-CU(AM1088A)
文摘In the present work, different silica-based supported cobalt （Co） catalysts were synthesized and used for CO2 hydrogenation for methanation. Different supports, such as SSP, MCM-41, TiSSP and TiMCM were used to prepare Co catalysts with 20 wt% Co loading. The supports and catalysts were characterized by means of N2 physisorption, XRD, SEM/EDX, XPS, TPR and CO chemisorption. It is found that after calcination of catalysts, Ti is present in the form of anatase. The introduction of Ti plays important roles in the properties of Co catalysts by：（i） facilitating the reduction of Co oxides species which are strongly interacted with support, （ii） preventing the formation of silicate compounds, and （iii） inhibiting the RWGS reaction. Based on CO2 hydrogenation, the CoTiMCM catalyst exhibites the highest activity and stability.
基金funded by the National Research Foundation(NRF)Prime Minister’s Office,Singapore under its Campus for Research Excellence and Technological Enterprise(CREATE)Program
文摘Catalytic conversion of COinto chemicals and fuels is an alternative to alleviate climate change and ocean acidification.The catalytic reduction of COby Hcan lead to the formation of various products:carbon monoxide,carboxylic acids,aldehydes,alcohols and hydrocarbons.In this paper,a comprehensive thermodynamics analysis of COhydrogenation is conducted using the Gibbs free energy minimization method.The results show that COreduction to CO needs a high temperature and H/COratio to achieve a high COconversion.However,synthesis of methanol from COneeds a relatively high pressure and low temperature to minimize the reverse water-gas shift reaction.Direct COhydrogenation to formic acid or formaldehyde is thermodynamically limited.On the contrary,production of CHfrom COhydrogenation is the thermodynamically easiest reaction with nearly 100%CH4 yield at moderate conditions.In addition,complex reactions with more than one product are also calculated in this work.Among the considered carboxylic acids（HCOOH,CHCOOH and CHCOOH）,propionic acid dominates in the product stream（selectivity above 90%）.The same trend can also be found in the hydrogenation of COto aldehydes and alcohols with the major product of propionaldehyde and butanol,respectively.In the process of COhydrogenation to alkenes,low temperature,high pressure,and high Hpartial pressure favor the COconversion.CHis the most thermodynamically favorable among all considered alkynes under different temperatures and pressures.The thermodynamic calculations are validated with experimental results,suggesting that the Gibbs free energy minimization method is effective for thermodynamically understanding the reaction network involved in the COhydrogenation process,which is helpful for the development of high-performance catalysts.
基金supported by the National Basic Research Program of China (No. 2011CB201404)the financial support of the State Key Laboratory for Oxo Synthesis and Selective Oxidation (OSSO) of China
文摘Methanol synthesis from hydrogenation of CO2 is investigated over Cu/ZnO/Al2O3 catalysts prepared by decomposition of M（Cu,Zn）-ammonia complexes （DMAC） at various temperatures.The catalysts were characterized in detail,including X-ray diffraction,N2 adsorption-desorption,N2O chemisorption,temperature-programmed reduction and evolved gas analyses.The influences of DMAC temperature,reaction temperature and specific Cu surface area on catalytic performance are investigated.It is considered that the aurichalcite phase in the precursor plays a key role in improving the physiochemical properties and activities of the final catalysts.The catalyst from rich-aurichalcite precursor exhibits large specific Cu surface area and high space time yield of methanol （212 g/（Lcat·h）;T=513 K,p=3MPa,SV=12000 h-1）.