To study the influence of silicon(Si)on 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane(CL-20),NC/CL-20 composite explosives and Si/NC/CL-20 composite explosives were prepared by the electrostatic spraying ...To study the influence of silicon(Si)on 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane(CL-20),NC/CL-20 composite explosives and Si/NC/CL-20 composite explosives were prepared by the electrostatic spraying method.The morphology,structure and thermal decomposition properties of the samples were analyzed using scanning electron microscopy(SEM),X-ray energy spectroscopy(EDS),infrared spectroscopy(FT-IR),and simultaneous thermal analyzer(TG-DSC).Additionally,the combustion process of the samples was tested using a high-speed camera.The results show that the addition of nano-Si contributes to the formation of composite explosives with regular morphology and smaller particle size.The Si/NC/CL-20 composite explosive has better and more uniform sphericity,with an average particle size of 73.4 nm,compared to the NC/CL-20 composite explosive.The Si/NC/CL-20 composite explosive which produced by the electrostatic spraying method,achieves physically uniform distribution of the components including NC,CL-20,Si.The addition of Si promotes the thermal decomposition of CL-20.In comparison to the NC/CL-20 composite explosive,the activation energy of the Si/NC/CL-20 composite explosive decreases by 16.78 kJ/mol,and the self-accelerated decomposition temperature and the critical temperature of thermal explosion decreases by 3.12 K and 2.61 K,respectively.Furthermore,Si/NC/CL-20 composite explosive has shorter ignition delay time and faster combustion rate compared to the NC/CL-20 composite explosive,which shows that Si can improve the combustion performance of CL-20.展开更多
CAB is a binder commonly utilized in CL-20-based mixed explosives.Based on the requirements of CL-20-based polymer bonded explosives in formability,safety,and detonation energy,we explored a hightoughness and low dosa...CAB is a binder commonly utilized in CL-20-based mixed explosives.Based on the requirements of CL-20-based polymer bonded explosives in formability,safety,and detonation energy,we explored a hightoughness and low dosage CAB binder system.CAB was subjected to different toughening modifications and the effects of the modified CAB binders on the bonding and coating of CL-20 crystals,as well as the formability,safety,and mechanical properties of CL-20-based polymer bonded explosive molding powder(MP)were evaluated.The changes in glass transition temperature(Tg)and mechanical properties of the modified binders were investigated using the molecular dynamics simulation at first.A series of modified binders with different molecular weights were then synthesized and characterized by FTIR,1H NMR,^(13)C NMR and SEC.The T_(g) and cross-sectional morphologies of the binder membranes were determined by DSC and SEM.The tensile properties of the binder membranes with different molecular weights and their mixtures with the plasticizer were evaluated at different temperature.With the optimized modified binder,CL-20/CAB and CL-20/CAB-g-PCL-3 MPs with the same plasticizer ratio and Cl-20/CAB-g-PCL-3 MP with a lower plasticizer ratio and higher CL-20 content were prepared and evaluated for the bonding and coating effects,crystal form,mechanical sensitivity and specific heat capacity(C_(p))by SEM,XRD,sensitivity testing and DSC,respectively.Their compressive strengths and splitting tensile strengths were measured at different temperature using a universal testing machine.Our work has provided a high-toughness and low-dosage binder system for CL-20-based MPs and offers a novel strategy to improve the formability,safety,and energy of CL-20 based polymer bonded explosives.展开更多
The impact safety of explosive charges has been focused in these decades. The fragment impact is widely used to evaluate the response of explosive charges. In our work, the explosive detonation driving technique was u...The impact safety of explosive charges has been focused in these decades. The fragment impact is widely used to evaluate the response of explosive charges. In our work, the explosive detonation driving technique was used to generate a high velocity fragment with large mass. When the fragment masses are10 g, 16 g, 25 g, and 50 g, the highest velocity of fragments can reach 2400 m/s, 2100 m/s, 1900 m/s, and1400 m/s, respectively. The high velocity fragment with large mass was used to evaluate the safety of two kinds of CL-20 based explosive charges. The effects of the fragment mass and velocity were analyzed.Especially, the reaction extent was obtained based on visible phenomenon. The CL-20-based explosive charge containing Al had a higher safety level than that without Al. It was because Al had good ductility,and further improved the mechanical property of the material. Also, the numerical simulation was conducted to understand the reaction characteristics of the CL-20-based explosive charge. The results showed that as the fragment mass and velocity increased, the reaction became more violent.展开更多
The new CL-20(hexanitrohexaazaisowurtzitane)type aluminized explosives in the overdrive detonation(ODD)conditions of the core problem is how to accurately represent the state of the overdrive detonation products.To th...The new CL-20(hexanitrohexaazaisowurtzitane)type aluminized explosives in the overdrive detonation(ODD)conditions of the core problem is how to accurately represent the state of the overdrive detonation products.To this end,this paper is based on the impedance matching method to test the ODD conditions of CL-20 type aluminium explosive particle velocity.Calculated the interfacial pressure of the shock wave in different media.Determined the characteristic parameters of the reaction zone of the detonation of CL-20 aluminized explosives.Calibrated the parameters of the JoneseWilkinseLee(JWL)+γ equation for the detonation products(DPs).Revealed the effect of different DPs equation of state(EOS)on the Hugoniot pressure of ODD.The results indicate that when the content of aluminum powder ranges from 0%to 30%,the duration of the ODD reaction zone and the width of the detonation reaction zone of the CL-20-based aluminized explosive are directly proportional to the content of aluminum powder.The width of the detonation reaction zone is increased by 1.97 times to 2.7 times compared to that of the reaction zone without the addition of aluminum powder.However,the energy release efficiency of the detonation reaction zone is inversely proportional to the content of aluminum powder.When the aluminum powder content was held constant,the incorporation of AP caused a 25%reduction in the energy release efficiency of the detonation reaction zone.Compared with existing ODD state equations,the JWL +γ equation is superior in calibrating overpressure Hugoniot data and the isentropic expansion in the C-J state.The deviation between calculated pressure results and experimental measurements is within 6%.展开更多
基金National Natural Science Foundation of China(No.22275150)。
文摘To study the influence of silicon(Si)on 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane(CL-20),NC/CL-20 composite explosives and Si/NC/CL-20 composite explosives were prepared by the electrostatic spraying method.The morphology,structure and thermal decomposition properties of the samples were analyzed using scanning electron microscopy(SEM),X-ray energy spectroscopy(EDS),infrared spectroscopy(FT-IR),and simultaneous thermal analyzer(TG-DSC).Additionally,the combustion process of the samples was tested using a high-speed camera.The results show that the addition of nano-Si contributes to the formation of composite explosives with regular morphology and smaller particle size.The Si/NC/CL-20 composite explosive has better and more uniform sphericity,with an average particle size of 73.4 nm,compared to the NC/CL-20 composite explosive.The Si/NC/CL-20 composite explosive which produced by the electrostatic spraying method,achieves physically uniform distribution of the components including NC,CL-20,Si.The addition of Si promotes the thermal decomposition of CL-20.In comparison to the NC/CL-20 composite explosive,the activation energy of the Si/NC/CL-20 composite explosive decreases by 16.78 kJ/mol,and the self-accelerated decomposition temperature and the critical temperature of thermal explosion decreases by 3.12 K and 2.61 K,respectively.Furthermore,Si/NC/CL-20 composite explosive has shorter ignition delay time and faster combustion rate compared to the NC/CL-20 composite explosive,which shows that Si can improve the combustion performance of CL-20.
基金supported by"the Fundamental Research Funds for the Central Universities".
文摘CAB is a binder commonly utilized in CL-20-based mixed explosives.Based on the requirements of CL-20-based polymer bonded explosives in formability,safety,and detonation energy,we explored a hightoughness and low dosage CAB binder system.CAB was subjected to different toughening modifications and the effects of the modified CAB binders on the bonding and coating of CL-20 crystals,as well as the formability,safety,and mechanical properties of CL-20-based polymer bonded explosive molding powder(MP)were evaluated.The changes in glass transition temperature(Tg)and mechanical properties of the modified binders were investigated using the molecular dynamics simulation at first.A series of modified binders with different molecular weights were then synthesized and characterized by FTIR,1H NMR,^(13)C NMR and SEC.The T_(g) and cross-sectional morphologies of the binder membranes were determined by DSC and SEM.The tensile properties of the binder membranes with different molecular weights and their mixtures with the plasticizer were evaluated at different temperature.With the optimized modified binder,CL-20/CAB and CL-20/CAB-g-PCL-3 MPs with the same plasticizer ratio and Cl-20/CAB-g-PCL-3 MP with a lower plasticizer ratio and higher CL-20 content were prepared and evaluated for the bonding and coating effects,crystal form,mechanical sensitivity and specific heat capacity(C_(p))by SEM,XRD,sensitivity testing and DSC,respectively.Their compressive strengths and splitting tensile strengths were measured at different temperature using a universal testing machine.Our work has provided a high-toughness and low-dosage binder system for CL-20-based MPs and offers a novel strategy to improve the formability,safety,and energy of CL-20 based polymer bonded explosives.
文摘The impact safety of explosive charges has been focused in these decades. The fragment impact is widely used to evaluate the response of explosive charges. In our work, the explosive detonation driving technique was used to generate a high velocity fragment with large mass. When the fragment masses are10 g, 16 g, 25 g, and 50 g, the highest velocity of fragments can reach 2400 m/s, 2100 m/s, 1900 m/s, and1400 m/s, respectively. The high velocity fragment with large mass was used to evaluate the safety of two kinds of CL-20 based explosive charges. The effects of the fragment mass and velocity were analyzed.Especially, the reaction extent was obtained based on visible phenomenon. The CL-20-based explosive charge containing Al had a higher safety level than that without Al. It was because Al had good ductility,and further improved the mechanical property of the material. Also, the numerical simulation was conducted to understand the reaction characteristics of the CL-20-based explosive charge. The results showed that as the fragment mass and velocity increased, the reaction became more violent.
基金supported by the National Natural Science Foundation of China(NSFC,Grant Nos.11872120,12102050)Key Laboratory of Explosion Science and Technology(Grant No.QNKT22-01).
文摘The new CL-20(hexanitrohexaazaisowurtzitane)type aluminized explosives in the overdrive detonation(ODD)conditions of the core problem is how to accurately represent the state of the overdrive detonation products.To this end,this paper is based on the impedance matching method to test the ODD conditions of CL-20 type aluminium explosive particle velocity.Calculated the interfacial pressure of the shock wave in different media.Determined the characteristic parameters of the reaction zone of the detonation of CL-20 aluminized explosives.Calibrated the parameters of the JoneseWilkinseLee(JWL)+γ equation for the detonation products(DPs).Revealed the effect of different DPs equation of state(EOS)on the Hugoniot pressure of ODD.The results indicate that when the content of aluminum powder ranges from 0%to 30%,the duration of the ODD reaction zone and the width of the detonation reaction zone of the CL-20-based aluminized explosive are directly proportional to the content of aluminum powder.The width of the detonation reaction zone is increased by 1.97 times to 2.7 times compared to that of the reaction zone without the addition of aluminum powder.However,the energy release efficiency of the detonation reaction zone is inversely proportional to the content of aluminum powder.When the aluminum powder content was held constant,the incorporation of AP caused a 25%reduction in the energy release efficiency of the detonation reaction zone.Compared with existing ODD state equations,the JWL +γ equation is superior in calibrating overpressure Hugoniot data and the isentropic expansion in the C-J state.The deviation between calculated pressure results and experimental measurements is within 6%.