A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was ox...A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was oxidized into colloidal antimony peroxide. Then antimony peroxide and isooctyl thioglycollate reacted stoichiometrically for 2 h with the yield of 87%. This compound was used as thermal stabilizer for polyvinyl chloride（PVC）. The results show that the thermal stability time is 52min at 200℃ by heat-ageing oven test when adding 2.5% thermal stabilizer to PVC resin. Compared with antimony tris（isooctyl thiolycollate）, the initial thermal stability of antimony pent（isooctyl thioglycollate） is better than that of antimony tris（isooctyl thioglycollate）, while the long-term thermal stability time is shorter than that of antimony tris（isooctyl thioglycollate）. Meanwhile, the synergism of antimony pent（isooctyl thioglycollate） with calcium stearate was studied, indicating that when the mass ratio of antimony pent（isooctyl thioglycollate） to calcium stearate is （2∶1,） the thermal stability time of PVC is 58min.展开更多
A novel type of thermal stabilizer-antimony tris (thioethyl stearate) (ATS) was synthsized. Its thermal stability was measured by heat-aging oven test when incorporated into PVC. ATS was synthesized from stearic acid,...A novel type of thermal stabilizer-antimony tris (thioethyl stearate) (ATS) was synthsized. Its thermal stability was measured by heat-aging oven test when incorporated into PVC. ATS was synthesized from stearic acid, antimony trioxide and 2-mercaptoethanol in two steps. The reaction conditions of synthesis were optimized through orthogonal test. Experimental results show that the molar ratio of stearic acid and antimony tris (2-hydroxyethylthiolate) was 1.2, adding 0.6%tetra-n-butyl titanate as catalyst and xylene as azeotropic solvent, heating and refluxing for about 4 h, and the yield of ATS is 83.9%. The thermal stability time is about 40 min(at 200 °C) when added 2phr(per hundred resin) in PVC. The thermal stability of ATS is better than that of Ca-Zn complex and basic lead stabilizers, and equal to that of dibutyltin dilaurate.展开更多
Professor Zhao Tiancong is a famous specialist of our country in nonferrous merallurgy field and a doctoral teacher of Central South University of Technology. He has been devoting diligently his life to the developmen...Professor Zhao Tiancong is a famous specialist of our country in nonferrous merallurgy field and a doctoral teacher of Central South University of Technology. He has been devoting diligently his life to the development of the antimony metallurgy.展开更多
潜热通量产品的验证与分析对于研究气候变化及能量循环具有重要意义。全球陆表高分辨率蒸散产品(high resolution global lAnd surface evapotranspiration product,Hi-GLASS ET)融合了5种传统蒸散算法,能够生产出较高精度的陆表潜热通...潜热通量产品的验证与分析对于研究气候变化及能量循环具有重要意义。全球陆表高分辨率蒸散产品(high resolution global lAnd surface evapotranspiration product,Hi-GLASS ET)融合了5种传统蒸散算法,能够生产出较高精度的陆表潜热通量产品,但目前没有针对此产品的验证研究。利用Ameriflux通量观测站点的潜热通量观测值与相应的Hi-GLASS陆表潜热通量产品估算值进行对比,获取多组有效验证数据。验证结果显示,所选站点实际观测值与产品估算值的决定系数(R 2)为0.6,均方根误差(RMSE)为34.4 W/m^(2),平均偏差(Bias)为-13.4 W/m^(2),克林-古普塔效率(Kling-Gupta efficiency,KGE)为0.49,Hi-GLASS潜热通量产品具有较高的精度,算法的拟合结果较好;此外,空间分布也表明Hi-GLASS陆表潜热通量产品符合正常的自然规律。由于数据获取的局限性,仅采用了美国地区18个站点数据对产品进行验证,在其他地区仍需进一步验证。展开更多
基金Project supported by the Postdoctoral Foundation of Central South University
文摘A new type of thermal stabilizer, antimony pent（isooctyl thioglycollate）(Sb(SCH2COOC8H17)5), was synthesized by using antimony trioxide, isooctanol and thioglycolic acid in 2 steps. Firstly, antimony trioxide was oxidized into colloidal antimony peroxide. Then antimony peroxide and isooctyl thioglycollate reacted stoichiometrically for 2 h with the yield of 87%. This compound was used as thermal stabilizer for polyvinyl chloride（PVC）. The results show that the thermal stability time is 52min at 200℃ by heat-ageing oven test when adding 2.5% thermal stabilizer to PVC resin. Compared with antimony tris（isooctyl thiolycollate）, the initial thermal stability of antimony pent（isooctyl thioglycollate） is better than that of antimony tris（isooctyl thioglycollate）, while the long-term thermal stability time is shorter than that of antimony tris（isooctyl thioglycollate）. Meanwhile, the synergism of antimony pent（isooctyl thioglycollate） with calcium stearate was studied, indicating that when the mass ratio of antimony pent（isooctyl thioglycollate） to calcium stearate is （2∶1,） the thermal stability time of PVC is 58min.
文摘A novel type of thermal stabilizer-antimony tris (thioethyl stearate) (ATS) was synthsized. Its thermal stability was measured by heat-aging oven test when incorporated into PVC. ATS was synthesized from stearic acid, antimony trioxide and 2-mercaptoethanol in two steps. The reaction conditions of synthesis were optimized through orthogonal test. Experimental results show that the molar ratio of stearic acid and antimony tris (2-hydroxyethylthiolate) was 1.2, adding 0.6%tetra-n-butyl titanate as catalyst and xylene as azeotropic solvent, heating and refluxing for about 4 h, and the yield of ATS is 83.9%. The thermal stability time is about 40 min(at 200 °C) when added 2phr(per hundred resin) in PVC. The thermal stability of ATS is better than that of Ca-Zn complex and basic lead stabilizers, and equal to that of dibutyltin dilaurate.
文摘Professor Zhao Tiancong is a famous specialist of our country in nonferrous merallurgy field and a doctoral teacher of Central South University of Technology. He has been devoting diligently his life to the development of the antimony metallurgy.