The effects of hot extrusion and addition of Al_(2)O_(3p) on both microstructure and tribological behavior of 7075 composites were investigated via optical microscopy(OM),scanning electron microscopy(SEM),energy dispe...The effects of hot extrusion and addition of Al_(2)O_(3p) on both microstructure and tribological behavior of 7075 composites were investigated via optical microscopy(OM),scanning electron microscopy(SEM),energy dispersive spectrometry(EDS),and transmission electron microscopy(TEM).The experimental consequences reveal that the optimal addition of Al_(2)O_(3p) was 2 wt%.After hot extrusion,the Mg(Zn,Cu,Al)2 phases partially dissolve into the matrix and generate many uniformly distributed aging precipitation particles,the Al_(7)Cu_(2)Fe phases are squeezed and broken,and the Al_(2)O_(3p) become uniform distribution.The microhardness of as-extruded 2 wt%Al_(2)O_(3p)/7075 composites reaches HV 170.34,increased by 41.5%than as-cast composites.The wear rate of as-extruded 2 wt%Al_(2)O_(3p)/7075 composites is further lower than that of as-cast composites under the same condition.SEM-EDS analyses reveal that the reinforced wear resistance of composites can put down to the protective effect of the Al_(2)O_(3p) reinforced transition layer.After hot extrusion,the transition layer becomes stable,which determines the reinforced wear resistance of the as-extruded composites.展开更多
BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechan...BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechanical properties and plasma erosion resistance were also investigated. With the increase of h-BNp content, relative density and Vickers＇ hardness of the composite ceramics decrease, while the flexural strength, elastic modulus and fracture toughness increase and then decrease. The plasma erosion resistance linearly deteriorated with the increase of BNp content which is mainly determined by the density, crystal structure and atomic number of the elements.展开更多
A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventiona...A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventional method, the new catalysts prepared via the new method exhibit much higher BET surface area and pore size, much smaller crystallite size and higher catalytic activity and selectivity in CO 2 hydrogenation to methanol. It is also found that the molar ratio of Cu + to Cu 0 on the surface of the catalyst obtained by coprecipitation-reduction is much higher than that on the reduced catalyst obtained by the conventional method, which could be crucial for its high activity and selectivity for catalytic hydrogenation of CO 2 to methanol.展开更多
Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition...Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition, reaction temperature and activation conditions on the catalytic activity have been investigated Crystal phases of catalysts were analyzed by XRD The results showed that Cu/ZnO/Al2O3 catalysts displayed high activity and selectivity for hydrogen and stability The optimized molar ratio is Cu/Zn=10, a maximum methanol conversion of 994?mol%, hydrogen selectivity of 999?mol% and CO molar fraction of 0007% were obtained in the steam reforming reaction with the catalyst containing 45?mol% copper XRD results showed that the diffraction peaks of CuO in the catalyst were clearly lower and broaden It indicated that high dispersion of small copper crystallites on the catalyst surface was formed under the calcination conditions It is suggested that the good performance of Cu/ZnO/Al2O3 catalysts partly resulted from well dispersed展开更多
We demonstrate for the first time that a short time of microwave irradiation on the oxide precursor of a Cu/ZnO/Al2O3 catalyst can provide unique opportunity for tailoring the microstructure and activity of the cataly...We demonstrate for the first time that a short time of microwave irradiation on the oxide precursor of a Cu/ZnO/Al2O3 catalyst can provide unique opportunity for tailoring the microstructure and activity of the catalyst for methanol steam reforming. It is shown by in situ XRD that a considerable increase in the microstrain of Cu nanocrystals could be achieved in the catalysts processed by microwave irradiation for 310 min, which correlates well with the enhanced CH3OH conversion as observed on the corresponding samples. The present work also confirms that although the high specific surface area of Cu is a prerequisite for catalytic activity, it does not account for the observed changes in activity and selectivity alone without taking bulk microstructural changes into account.展开更多
基金Project(51965040)supported by the National Natural Science Foundation of ChinaProject(20181BAB206026)supported by the National Science Foundation of Jiangxi Province,China。
文摘The effects of hot extrusion and addition of Al_(2)O_(3p) on both microstructure and tribological behavior of 7075 composites were investigated via optical microscopy(OM),scanning electron microscopy(SEM),energy dispersive spectrometry(EDS),and transmission electron microscopy(TEM).The experimental consequences reveal that the optimal addition of Al_(2)O_(3p) was 2 wt%.After hot extrusion,the Mg(Zn,Cu,Al)2 phases partially dissolve into the matrix and generate many uniformly distributed aging precipitation particles,the Al_(7)Cu_(2)Fe phases are squeezed and broken,and the Al_(2)O_(3p) become uniform distribution.The microhardness of as-extruded 2 wt%Al_(2)O_(3p)/7075 composites reaches HV 170.34,increased by 41.5%than as-cast composites.The wear rate of as-extruded 2 wt%Al_(2)O_(3p)/7075 composites is further lower than that of as-cast composites under the same condition.SEM-EDS analyses reveal that the reinforced wear resistance of composites can put down to the protective effect of the Al_(2)O_(3p) reinforced transition layer.After hot extrusion,the transition layer becomes stable,which determines the reinforced wear resistance of the as-extruded composites.
基金Project(HIT.NSRIF.2010112)supported by the Fundamental Research Fund for the Central Universities,ChinaProjects(50902030,51021002)supported by the National Natural Science Foundation of China
文摘BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechanical properties and plasma erosion resistance were also investigated. With the increase of h-BNp content, relative density and Vickers＇ hardness of the composite ceramics decrease, while the flexural strength, elastic modulus and fracture toughness increase and then decrease. The plasma erosion resistance linearly deteriorated with the increase of BNp content which is mainly determined by the density, crystal structure and atomic number of the elements.
文摘A novel coprecipitation-reduction process has been proposed for preparing highly selective Cu/ZnO/Al 2O 3 catalysts for methanol synthesis from CO 2 hydrogenation. Compared to the catalysts prepared by the conventional method, the new catalysts prepared via the new method exhibit much higher BET surface area and pore size, much smaller crystallite size and higher catalytic activity and selectivity in CO 2 hydrogenation to methanol. It is also found that the molar ratio of Cu + to Cu 0 on the surface of the catalyst obtained by coprecipitation-reduction is much higher than that on the reduced catalyst obtained by the conventional method, which could be crucial for its high activity and selectivity for catalytic hydrogenation of CO 2 to methanol.
文摘Hydrogen production by catalytic steam reforming of methanol over a series of coprecipitated Cu/ZnO/Al2O3 catalysts under atmospheric pressure in a microreactor has been studied Effects of catalyst composition, reaction temperature and activation conditions on the catalytic activity have been investigated Crystal phases of catalysts were analyzed by XRD The results showed that Cu/ZnO/Al2O3 catalysts displayed high activity and selectivity for hydrogen and stability The optimized molar ratio is Cu/Zn=10, a maximum methanol conversion of 994?mol%, hydrogen selectivity of 999?mol% and CO molar fraction of 0007% were obtained in the steam reforming reaction with the catalyst containing 45?mol% copper XRD results showed that the diffraction peaks of CuO in the catalyst were clearly lower and broaden It indicated that high dispersion of small copper crystallites on the catalyst surface was formed under the calcination conditions It is suggested that the good performance of Cu/ZnO/Al2O3 catalysts partly resulted from well dispersed
文摘We demonstrate for the first time that a short time of microwave irradiation on the oxide precursor of a Cu/ZnO/Al2O3 catalyst can provide unique opportunity for tailoring the microstructure and activity of the catalyst for methanol steam reforming. It is shown by in situ XRD that a considerable increase in the microstrain of Cu nanocrystals could be achieved in the catalysts processed by microwave irradiation for 310 min, which correlates well with the enhanced CH3OH conversion as observed on the corresponding samples. The present work also confirms that although the high specific surface area of Cu is a prerequisite for catalytic activity, it does not account for the observed changes in activity and selectivity alone without taking bulk microstructural changes into account.