The aim of present study is to analyze the influence of volume percentage(vol.%) of nano-sized particles(TiB_2: average size is 35 nm) on microstructure, mechanical and tribological behavior of 6061-T6 Al alloy surfac...The aim of present study is to analyze the influence of volume percentage(vol.%) of nano-sized particles(TiB_2: average size is 35 nm) on microstructure, mechanical and tribological behavior of 6061-T6 Al alloy surface nano composite prepared via Friction stir process(FSP). The microstructure of the fabricated surface nanocomposites is examined using optical microscopy(OM) and scanning electron microscope(SEM) for distribution of TiB_2 nano reinforcement particles, thickness of nano composite layer formed on the Aluminum alloy substrate and fracture features. The depth of surface nano composite layer is measured as 3683.82 m m along the cross section of stir zone of nano composite perpendicular to FSP. It was observed that increase in volume percentage of TiB_2 particles, the microhardness is increased up to132 Hv and it is greater than as-received Al alloy's microhardness(104 Hv). It is also observed that at 4volume percentage higher tensile properties exhibited as compared with the 2 and 8 vol. %. It is found that high wear resistance exhibited at 4 volume percentage as-compared with the 2 and 8 vol. %. The observed wear and mechanical properties are interrelated with microstructure, fractography and worn morphology.展开更多
文摘The aim of present study is to analyze the influence of volume percentage(vol.%) of nano-sized particles(TiB_2: average size is 35 nm) on microstructure, mechanical and tribological behavior of 6061-T6 Al alloy surface nano composite prepared via Friction stir process(FSP). The microstructure of the fabricated surface nanocomposites is examined using optical microscopy(OM) and scanning electron microscope(SEM) for distribution of TiB_2 nano reinforcement particles, thickness of nano composite layer formed on the Aluminum alloy substrate and fracture features. The depth of surface nano composite layer is measured as 3683.82 m m along the cross section of stir zone of nano composite perpendicular to FSP. It was observed that increase in volume percentage of TiB_2 particles, the microhardness is increased up to132 Hv and it is greater than as-received Al alloy's microhardness(104 Hv). It is also observed that at 4volume percentage higher tensile properties exhibited as compared with the 2 and 8 vol. %. It is found that high wear resistance exhibited at 4 volume percentage as-compared with the 2 and 8 vol. %. The observed wear and mechanical properties are interrelated with microstructure, fractography and worn morphology.