0 Introduction In recent years, the study of Y-Ba-Cu-O superconductor have made much progress. The superconducting applications are showing bright future. Generally, critical current is very lower (especially bulk sam...0 Introduction In recent years, the study of Y-Ba-Cu-O superconductor have made much progress. The superconducting applications are showing bright future. Generally, critical current is very lower (especially bulk sample ). The Largest J_c is only 10~3 A/cm^2. Ordinarilly, the typical critical current of Nb-Ti alloy is 10~6 A/cm^2 about 4.2 K. Hence, the level of current density have become a problem interested in by scientists. In this paper, microstrueture of Y_1 Ba_2 Cu_2 O_(7-8) superconductor is examined. The grade intersection-tunnel modal is put forward here. Some mecha-展开更多
用 EPMA 的背散射电子像和相的元素分析发现,在 Ag-EuBa_2Cu_(3-x)O_7高 T_c 陶瓷中存在富 Ag 贫Cu 和无 Eu 二种非超导相,在 Ag-YBa_2Cu_(3-x)O_7中存在富 Ag 贫 Cu,富 Y 贫 Cu 和无 Y 富 Cu 三种非超导相,减少非超导相和气孔的数量是...用 EPMA 的背散射电子像和相的元素分析发现,在 Ag-EuBa_2Cu_(3-x)O_7高 T_c 陶瓷中存在富 Ag 贫Cu 和无 Eu 二种非超导相,在 Ag-YBa_2Cu_(3-x)O_7中存在富 Ag 贫 Cu,富 Y 贫 Cu 和无 Y 富 Cu 三种非超导相,减少非超导相和气孔的数量是提高超导氧化物陶瓷临界电流密度的重要途径。对高 T_(?)陶瓷显微结构的观察度现,T_c 对显微结构因素不敏感,T_c 相同的超导陶瓷显微结构可有明显差异;断裂方式与烧结温度有关。展开更多
文摘0 Introduction In recent years, the study of Y-Ba-Cu-O superconductor have made much progress. The superconducting applications are showing bright future. Generally, critical current is very lower (especially bulk sample ). The Largest J_c is only 10~3 A/cm^2. Ordinarilly, the typical critical current of Nb-Ti alloy is 10~6 A/cm^2 about 4.2 K. Hence, the level of current density have become a problem interested in by scientists. In this paper, microstrueture of Y_1 Ba_2 Cu_2 O_(7-8) superconductor is examined. The grade intersection-tunnel modal is put forward here. Some mecha-
文摘用 EPMA 的背散射电子像和相的元素分析发现,在 Ag-EuBa_2Cu_(3-x)O_7高 T_c 陶瓷中存在富 Ag 贫Cu 和无 Eu 二种非超导相,在 Ag-YBa_2Cu_(3-x)O_7中存在富 Ag 贫 Cu,富 Y 贫 Cu 和无 Y 富 Cu 三种非超导相,减少非超导相和气孔的数量是提高超导氧化物陶瓷临界电流密度的重要途径。对高 T_(?)陶瓷显微结构的观察度现,T_c 对显微结构因素不敏感,T_c 相同的超导陶瓷显微结构可有明显差异;断裂方式与烧结温度有关。