The electrolyte integrated with lithium metal anodes is subjected to the issues of interfacial compatibility and stability,which strongly influence the performances of high-energy lithium metal batteries.Here,we repor...The electrolyte integrated with lithium metal anodes is subjected to the issues of interfacial compatibility and stability,which strongly influence the performances of high-energy lithium metal batteries.Here,we report a new electrolyte recipe viz.a moderately concentrated electrolyte comprising of 2.4 M lithium bis(fluorosulfonyl)imide(LiFSI)in a cosolvent mixture of fluorinated ethylene carbonate(FEC)and dimethyl carbonate(DMC)with relatively high ion conductivity.Owing to the preferential decomposition of LiFSI and FEC,an inorganic-rich interphase with abundant Li_(2)O and LiF nanocrystals is formed on lithium metal with improved robustness and ion transfer kinetics,enabling lithium plating/stripping with an extremely low overpotential of~8 mV and the average CE of 97%.When tested in Li||LiFePO_(4) cell,this electrolyte provides long-term cycling with a capacity retention of 98.3%after 1000 cycles at 1 C and an excellent rate performance of 20 C,as well as an areal capacity of 1.35 mA h cm^(-2)at the cathode areal loading of 9 mg cm^(-2).Moreover,the Li||LiFePO_(4) cell exhibits excellent wide-temperature performances(-40~60℃),including long-term cycling stability over 2600 cycles without visible capacity fading at 0℃,as well as extremely high average CEs of 99.6%and 99.8% over 400 cycles under-20℃ and 45℃.展开更多
基金the Innovation-Driven Project of Central South University(2019CX033)the National Natural Science Foundation of China(51904344 and 52172264)the Natural Science Foundation of Hunan Province of China(2021JJ10060 and 2022GK2033)。
文摘The electrolyte integrated with lithium metal anodes is subjected to the issues of interfacial compatibility and stability,which strongly influence the performances of high-energy lithium metal batteries.Here,we report a new electrolyte recipe viz.a moderately concentrated electrolyte comprising of 2.4 M lithium bis(fluorosulfonyl)imide(LiFSI)in a cosolvent mixture of fluorinated ethylene carbonate(FEC)and dimethyl carbonate(DMC)with relatively high ion conductivity.Owing to the preferential decomposition of LiFSI and FEC,an inorganic-rich interphase with abundant Li_(2)O and LiF nanocrystals is formed on lithium metal with improved robustness and ion transfer kinetics,enabling lithium plating/stripping with an extremely low overpotential of~8 mV and the average CE of 97%.When tested in Li||LiFePO_(4) cell,this electrolyte provides long-term cycling with a capacity retention of 98.3%after 1000 cycles at 1 C and an excellent rate performance of 20 C,as well as an areal capacity of 1.35 mA h cm^(-2)at the cathode areal loading of 9 mg cm^(-2).Moreover,the Li||LiFePO_(4) cell exhibits excellent wide-temperature performances(-40~60℃),including long-term cycling stability over 2600 cycles without visible capacity fading at 0℃,as well as extremely high average CEs of 99.6%and 99.8% over 400 cycles under-20℃ and 45℃.