Controllable synthesis of insertion-type anode materials with beneficial micro-and nanostructures is a promising approach for the synthesis of sodium-ion storage devices with high-reactivity and excellent electrochemi...Controllable synthesis of insertion-type anode materials with beneficial micro-and nanostructures is a promising approach for the synthesis of sodium-ion storage devices with high-reactivity and excellent electrochemical performance.In this study,we developed a sacrificial-templating route to synthesize TiO_(2)@N-doped carbon nanotubes(TiO_(2)@NC-NTs)with excellent electrochemical performance.The asprepared mesoporous TiO_(2)@NC-NTs with tiny nanocrystals of anatase TiO_(2) wrapped in N-doped carbon layers showed a well-defined tube structure with a large specific surface area of 198 m^(2) g^(-1) and a large pore size of~5 nm.The TiO_(2)@NC-NTs delivered high reversible capacities of 158 m A h g^(-1) at 2 C(1 C=335 m A g^(-1))for 2200 cycles and 146 m A h g^(-1) at 5 C for 4000 cycles,as well as an ultrahigh rate capability of up to 40 C with a capacity of 98 m A h g^(-1).Even at a high current density of 10 C,a capacity of 138 m A h g^(-1) could be delivered over 10,000 cycles.Thus,the synthesis of mesoporous TiO_(2)@NC-NTs was demonstrated to be an efficient approach for developing electrode materials with high sodium storage and long cycle life.展开更多
基金the financial support provided by internal reseach funding of Khalifa University of Science and Technology,United Arab Emirates(Grant No.CIRA-2018-16)。
文摘Controllable synthesis of insertion-type anode materials with beneficial micro-and nanostructures is a promising approach for the synthesis of sodium-ion storage devices with high-reactivity and excellent electrochemical performance.In this study,we developed a sacrificial-templating route to synthesize TiO_(2)@N-doped carbon nanotubes(TiO_(2)@NC-NTs)with excellent electrochemical performance.The asprepared mesoporous TiO_(2)@NC-NTs with tiny nanocrystals of anatase TiO_(2) wrapped in N-doped carbon layers showed a well-defined tube structure with a large specific surface area of 198 m^(2) g^(-1) and a large pore size of~5 nm.The TiO_(2)@NC-NTs delivered high reversible capacities of 158 m A h g^(-1) at 2 C(1 C=335 m A g^(-1))for 2200 cycles and 146 m A h g^(-1) at 5 C for 4000 cycles,as well as an ultrahigh rate capability of up to 40 C with a capacity of 98 m A h g^(-1).Even at a high current density of 10 C,a capacity of 138 m A h g^(-1) could be delivered over 10,000 cycles.Thus,the synthesis of mesoporous TiO_(2)@NC-NTs was demonstrated to be an efficient approach for developing electrode materials with high sodium storage and long cycle life.