Based on the diffusion channel,the influence of Si content on the microstructure evolution of iron-based hot-dip Al-χSi coating was analyzed(χ=0,1.5 wt%,3.0 wt% and 7.0 wt%).The results show that the introduction of...Based on the diffusion channel,the influence of Si content on the microstructure evolution of iron-based hot-dip Al-χSi coating was analyzed(χ=0,1.5 wt%,3.0 wt% and 7.0 wt%).The results show that the introduction of Si makes the reaction interface change from the lingual-tooth interface of hot-dip Al to the flat interface of hot-dip Al-Si.It also reduces the thickness of the alloy layer in the coating,especially the Fe_(2)Al_(5) layer.When the Si content is 1.5 wt%or 3.0 wt%,the diffusion channel crosses the conjugate line of the two-phase region(FeAl_(3)+liquid phase)into the FeAl_(3) single-phase region,and then moves to the region with higher Si content.Next,the diffusion channel cuts off the conjugate line of FeAl_(3)phase,τ_(1)/τ_(9) phase,and Fe_(2)Al_(5)phase,which promotes the form ofτ_(1)/τ_(9) phase.The formedτ_(1)/τ_(9) phase inhibits the diffusion between Fe and Al atoms.When the Si content is 7.0 wt%,the diffusion channel passes through the two-phase region(liquid phase+τ_(5))and enters theτ_(5) single-phase region.The form ofτ_(5) single-phase region has a strong inhibitory effect on the interatomic diffusion of Fe and Al,thereby reducing the thickness of the coating,especially the Fe_(2)Al_(5)layer.展开更多
基金Projects(51971039,51671037)supported by the National Natural Science Foundation of ChinaProject(19KJA530001)supported by the Natural Science Research Project of Higher Education of Jiangsu,ChinaProject(KYCX21_2868)supported by the Postgraduate Research&Practice Innovation Program of Jiangsu Province,China。
文摘Based on the diffusion channel,the influence of Si content on the microstructure evolution of iron-based hot-dip Al-χSi coating was analyzed(χ=0,1.5 wt%,3.0 wt% and 7.0 wt%).The results show that the introduction of Si makes the reaction interface change from the lingual-tooth interface of hot-dip Al to the flat interface of hot-dip Al-Si.It also reduces the thickness of the alloy layer in the coating,especially the Fe_(2)Al_(5) layer.When the Si content is 1.5 wt%or 3.0 wt%,the diffusion channel crosses the conjugate line of the two-phase region(FeAl_(3)+liquid phase)into the FeAl_(3) single-phase region,and then moves to the region with higher Si content.Next,the diffusion channel cuts off the conjugate line of FeAl_(3)phase,τ_(1)/τ_(9) phase,and Fe_(2)Al_(5)phase,which promotes the form ofτ_(1)/τ_(9) phase.The formedτ_(1)/τ_(9) phase inhibits the diffusion between Fe and Al atoms.When the Si content is 7.0 wt%,the diffusion channel passes through the two-phase region(liquid phase+τ_(5))and enters theτ_(5) single-phase region.The form ofτ_(5) single-phase region has a strong inhibitory effect on the interatomic diffusion of Fe and Al,thereby reducing the thickness of the coating,especially the Fe_(2)Al_(5)layer.