Compared with noble metal catalyst, Co3O4-based electrocatalysts have attracted considerable interesting as low-cost alternatives for oxygen evolution reaction (OER). However, the poor electrocatalytic activity still ...Compared with noble metal catalyst, Co3O4-based electrocatalysts have attracted considerable interesting as low-cost alternatives for oxygen evolution reaction (OER). However, the poor electrocatalytic activity still remains a huge challenge. Herein, we demonstrate a feasible approach through oxidation of CoFe layered double hydroxide (CoFe-LDH) to synthesize Fe-doped Co3O4@C nanopmrticles with size of about 30-50 nm. As OER catalyst, the as-synthesized Fe-doped Co3O4@C nanoparticles exhibited superior OER performance with a small overpotential of 260 mV at the current density of 20 mA cm^-2, a small Tafel slope of 70 mV dec^-1 and long-term durability (there was no obviously OER current density degradation for 100 h) in alkaline solution. The present work opens a new avenue to the exploration of cost-effective and excellent electrocatalysts based on transition metal oxide materials to substitute precious metal materials for water splitting.展开更多
基金supported by the 973 Program(no.2014CB932104)the National Natural Science Foundation of China(nos:2177060378,U1707603 and 21521005)the Program for Changjiang Scholars,Innovative Research Teams in Universities(no.IRT1205)
文摘Compared with noble metal catalyst, Co3O4-based electrocatalysts have attracted considerable interesting as low-cost alternatives for oxygen evolution reaction (OER). However, the poor electrocatalytic activity still remains a huge challenge. Herein, we demonstrate a feasible approach through oxidation of CoFe layered double hydroxide (CoFe-LDH) to synthesize Fe-doped Co3O4@C nanopmrticles with size of about 30-50 nm. As OER catalyst, the as-synthesized Fe-doped Co3O4@C nanoparticles exhibited superior OER performance with a small overpotential of 260 mV at the current density of 20 mA cm^-2, a small Tafel slope of 70 mV dec^-1 and long-term durability (there was no obviously OER current density degradation for 100 h) in alkaline solution. The present work opens a new avenue to the exploration of cost-effective and excellent electrocatalysts based on transition metal oxide materials to substitute precious metal materials for water splitting.